The semi-solid billet of 6061 aluminum alloy was prepared by the near-liquidus semi-continuous casting（LSC） with rosette or near-spheroide grains.The pre-deformation processing was applied before partial remelting t...The semi-solid billet of 6061 aluminum alloy was prepared by the near-liquidus semi-continuous casting（LSC） with rosette or near-spheroide grains.The pre-deformation processing was applied before partial remelting to further improve the microstructure and properties of the semi-solid alloy.The effects of different processing parameters,such as holding temperature and holding time,on the semisolid microstructures during partial remelting have been investigated.It was found that the optimal partial remelting parameters should be 630℃ and 10-15 min for 6061 alloy cold rolled with 60% reduction in height of pre-deformation.The coarsening rates were anasysed by Lifshitz-Slyozov-Wagner（LSW） theory.The pre-deformed 6061 alloy exhibits lower coarsening rate constants than that of the as-cast one,and also lower than other alloys processed by different method found in previous literature.It is because the coarsening rate is associated with the initial microstructure and composition of the alloy.The secondary phases in the alloy inhibit the migration of the liquid film grain boundaries.The microstructure obtained by using the combination of near-liquidus semicontinuous casting and pre-deformation treatment is better than that without pre-deformation processing,which demonstrates that the used method is promising for fabricating high quality semi-solid alloys.展开更多
The 6061 semi-solid aluminium alloy feedstocks prepared by near-liquidus casting were compressed in semi-solid state by means of Gleeble-3500 thermal-mechanical simulator.The relationship between the true stress and t...The 6061 semi-solid aluminium alloy feedstocks prepared by near-liquidus casting were compressed in semi-solid state by means of Gleeble-3500 thermal-mechanical simulator.The relationship between the true stress and the true strain at different temperatures and strain rates was studied with the deformation degree of 70%.The microstructures during the deformation process were characterized.The deformation mechanism and thixo-forming properties of the semi-solid alloys were analyzed.The results show that the homogeneous and non-dendrite microstructures of semi-solid 6061Al alloy manufactured by near-liquidus casting technology could be transformed into semi-solid state with the microstructure suitable for thixo-forming which are composed of near-spherical grains and liquid phase with eutectic composition through reheating process.The deformation temperature and strain rate affect the peak stress significantly rather than steady flow stress.The resistance to deformation in semi-solid state decreases with the increase of the deformation temperature and decrease of the strain rate.At steady thixotropic deformation stage, the thixotropic property is uniform, and the main deformation mechanism is the rotating or sliding between the solid particles and the plastic deformation of the solid particles.展开更多
基金financially supported by the National Natural Science Foundation of China (Grant No.50674032)
文摘The semi-solid billet of 6061 aluminum alloy was prepared by the near-liquidus semi-continuous casting（LSC） with rosette or near-spheroide grains.The pre-deformation processing was applied before partial remelting to further improve the microstructure and properties of the semi-solid alloy.The effects of different processing parameters,such as holding temperature and holding time,on the semisolid microstructures during partial remelting have been investigated.It was found that the optimal partial remelting parameters should be 630℃ and 10-15 min for 6061 alloy cold rolled with 60% reduction in height of pre-deformation.The coarsening rates were anasysed by Lifshitz-Slyozov-Wagner（LSW） theory.The pre-deformed 6061 alloy exhibits lower coarsening rate constants than that of the as-cast one,and also lower than other alloys processed by different method found in previous literature.It is because the coarsening rate is associated with the initial microstructure and composition of the alloy.The secondary phases in the alloy inhibit the migration of the liquid film grain boundaries.The microstructure obtained by using the combination of near-liquidus semicontinuous casting and pre-deformation treatment is better than that without pre-deformation processing,which demonstrates that the used method is promising for fabricating high quality semi-solid alloys.
基金Project(50874049) supported by the National Natural Science Foundation of ChinaProject(2008DFB50020) supported by International Science and Technology Cooperation of Ministry of Science and Technology of China
文摘The 6061 semi-solid aluminium alloy feedstocks prepared by near-liquidus casting were compressed in semi-solid state by means of Gleeble-3500 thermal-mechanical simulator.The relationship between the true stress and the true strain at different temperatures and strain rates was studied with the deformation degree of 70%.The microstructures during the deformation process were characterized.The deformation mechanism and thixo-forming properties of the semi-solid alloys were analyzed.The results show that the homogeneous and non-dendrite microstructures of semi-solid 6061Al alloy manufactured by near-liquidus casting technology could be transformed into semi-solid state with the microstructure suitable for thixo-forming which are composed of near-spherical grains and liquid phase with eutectic composition through reheating process.The deformation temperature and strain rate affect the peak stress significantly rather than steady flow stress.The resistance to deformation in semi-solid state decreases with the increase of the deformation temperature and decrease of the strain rate.At steady thixotropic deformation stage, the thixotropic property is uniform, and the main deformation mechanism is the rotating or sliding between the solid particles and the plastic deformation of the solid particles.