The relationship between compressive strength obtained by universal testing machine and rebound value obtained by the hammer of high performance concrete was systematically investigated at the macro level. And a model...The relationship between compressive strength obtained by universal testing machine and rebound value obtained by the hammer of high performance concrete was systematically investigated at the macro level. And a model of high performance concrete strength curve was established from them. At the micro level, the microstructure, hydration products and pore structure of concrete surface were analyzed by scanning electron microscopy（SEM）, comprehensive thermal analysis（TG-DSC） and mercury intrusion porosimetry（MIP）, respectively. The effect of carbonation on surface strength was also investigated. The results showed that the concrete surface hardness layer grew rapidly at early stage and then stabilized at last with ongoing curing age; the rebound value and compressive strength of concrete with slag were higher than those of concrete with the same content of fly ash. In addition, the strength curve obtained by the least square method can satisfy the local standard requirements with an average relative error of 8.9% and a relative standard deviation of 11.3%. When the carbonation depth was 6 mm, the compressive strength calculated by national uniform strength curve was 25 PMa higher than that by high performance concrete.展开更多
Basic magnesium sulfate cement coral aggregate concrete(MCAC)is a new type of concrete consisting of basic magnesium sulfate cement,coarse coral aggregate,coral reef sand and seawater.The rebound hammer(RH),the ultras...Basic magnesium sulfate cement coral aggregate concrete(MCAC)is a new type of concrete consisting of basic magnesium sulfate cement,coarse coral aggregate,coral reef sand and seawater.The rebound hammer(RH),the ultrasonic pulse velocity(UPV)and the compressive strength(fcu)tests of 14 sets of cube specimens of the MCAC after 28 d of aging were conducted.The impact of the content and length of sisal fiber on the relationship between the fcu-RH and the fcu-UPV was determined.A mathematical model was established to predict the strength of the MCAC using the UPV,RH,and comprehensive UPV/RH methods and to obtain the curves of test strength.The applicability of the test strength curves of ordinary portland concrete(OPC),light-weight aggregate concrete(LAC),and coral aggregate concrete(CAC)to MCAC was assessed.The results showed that the test strength curves of OPC,LAC and CAC were inappropriate to determine the strength of MCAC using non-destructive method.The relative standard error of the curves of test strength of the RH method and the comprehensive method met the specifications,whereas that of the UPV method did not.展开更多
基金Funded by the National Natural Science Foundation of China(No.2015CB655102)National Science&Technology Pillar Program(No.2014BAB15B01-02)
文摘The relationship between compressive strength obtained by universal testing machine and rebound value obtained by the hammer of high performance concrete was systematically investigated at the macro level. And a model of high performance concrete strength curve was established from them. At the micro level, the microstructure, hydration products and pore structure of concrete surface were analyzed by scanning electron microscopy（SEM）, comprehensive thermal analysis（TG-DSC） and mercury intrusion porosimetry（MIP）, respectively. The effect of carbonation on surface strength was also investigated. The results showed that the concrete surface hardness layer grew rapidly at early stage and then stabilized at last with ongoing curing age; the rebound value and compressive strength of concrete with slag were higher than those of concrete with the same content of fly ash. In addition, the strength curve obtained by the least square method can satisfy the local standard requirements with an average relative error of 8.9% and a relative standard deviation of 11.3%. When the carbonation depth was 6 mm, the compressive strength calculated by national uniform strength curve was 25 PMa higher than that by high performance concrete.
基金Funded by National Natural Science Foundation of China(Nos.51878350,11832013,52078250)the Postgraduate Research&Practice Innovation Program of Jiangsu Province(No.KYCX21_0236)。
文摘Basic magnesium sulfate cement coral aggregate concrete(MCAC)is a new type of concrete consisting of basic magnesium sulfate cement,coarse coral aggregate,coral reef sand and seawater.The rebound hammer(RH),the ultrasonic pulse velocity(UPV)and the compressive strength(fcu)tests of 14 sets of cube specimens of the MCAC after 28 d of aging were conducted.The impact of the content and length of sisal fiber on the relationship between the fcu-RH and the fcu-UPV was determined.A mathematical model was established to predict the strength of the MCAC using the UPV,RH,and comprehensive UPV/RH methods and to obtain the curves of test strength.The applicability of the test strength curves of ordinary portland concrete(OPC),light-weight aggregate concrete(LAC),and coral aggregate concrete(CAC)to MCAC was assessed.The results showed that the test strength curves of OPC,LAC and CAC were inappropriate to determine the strength of MCAC using non-destructive method.The relative standard error of the curves of test strength of the RH method and the comprehensive method met the specifications,whereas that of the UPV method did not.