A series of compounds, La 2/3- x Li 3 x MoO 4, were first prepared. Their structures are tetragonal scheelites with the cationic defects. The cell parameters a, c and values of c/a decrease with...A series of compounds, La 2/3- x Li 3 x MoO 4, were first prepared. Their structures are tetragonal scheelites with the cationic defects. The cell parameters a, c and values of c/a decrease with the increasing of the substitution amount (3 x ) of lithium ion. Cationic vacancies are getting more as Li + concentration is lower. The diffusion of lithium ion is predominant. The concentration of charge carriers increases with increasing the substitution amount (3 x ) of lithium ion, meanwhile, the concentration of cationic vacancies decreases. The conductivity approaches the best when the substitution amount (3 x ) of lithium ion is about 0.3. The conductivity of La 0.567 Li 0.3 MoO 4 is 6.5×10 -6 S·cm -1 at room temperature.展开更多
文摘A series of compounds, La 2/3- x Li 3 x MoO 4, were first prepared. Their structures are tetragonal scheelites with the cationic defects. The cell parameters a, c and values of c/a decrease with the increasing of the substitution amount (3 x ) of lithium ion. Cationic vacancies are getting more as Li + concentration is lower. The diffusion of lithium ion is predominant. The concentration of charge carriers increases with increasing the substitution amount (3 x ) of lithium ion, meanwhile, the concentration of cationic vacancies decreases. The conductivity approaches the best when the substitution amount (3 x ) of lithium ion is about 0.3. The conductivity of La 0.567 Li 0.3 MoO 4 is 6.5×10 -6 S·cm -1 at room temperature.