A super-fine compound powder, Ag/SnO_2+La_2O_3+ Bi_2O_3, has been obtainedusing the chemical coprecipitation method. And a new contact material, Ag/SnO_2+La_2O_3+Bi_2O_3, wasproduced by the powder metallurgy method. I...A super-fine compound powder, Ag/SnO_2+La_2O_3+ Bi_2O_3, has been obtainedusing the chemical coprecipitation method. And a new contact material, Ag/SnO_2+La_2O_3+Bi_2O_3, wasproduced by the powder metallurgy method. Its properties are as follows: the density is 9.75-9.93g/cm^3, the resistivity is 2.31-2.55 μΩ ·cm, the hardness is 880-985 MPa. Its mi-crostructureshows that the fine oxides have a uniform distribution in the silver matrix. The results ofmake-break capacity and temperature rise testing show that the new material has better ability ofanti-arc erosion and lower temperature rise than that of commonly used Ag/CdO.展开更多
A new silver rare earth oxide contact material, Ag/La2O3(12), was produced by powder metallurgy method. Its performances are as follows: the density is 9.71 similar to 9.96 g.cm(-3); the hardness (HB) is 760 similar t...A new silver rare earth oxide contact material, Ag/La2O3(12), was produced by powder metallurgy method. Its performances are as follows: the density is 9.71 similar to 9.96 g.cm(-3); the hardness (HB) is 760 similar to 970 MPa and the resistivity is 2.25 similar to 2.38 mu Omega . cm. The microstructure of Ag/La2O3(12) mas analyzed by SEM and EDS. Rare earth oxide La2O3 shows two shapes, which are uniformly distributed in the form of sphere and abnormality in Ag matrix. La2O3 shows fine spherical shape in the melted area of Ag after laser acting which is used to simulate electric are. The results are contributed to the less splash erosion of Ag. Compared with the main physical and mechanical properties of Ag/SnO2(12) and Ag/CdO(12), the properties of three contact materials are similar, and hence Ag/La2O3(12) may become a potential contact material to be used as the substitute of Ag/CdO(12).展开更多
基金This project is financially supported by the Science Foundation of Hebei Province (No.502048)
文摘A super-fine compound powder, Ag/SnO_2+La_2O_3+ Bi_2O_3, has been obtainedusing the chemical coprecipitation method. And a new contact material, Ag/SnO_2+La_2O_3+Bi_2O_3, wasproduced by the powder metallurgy method. Its properties are as follows: the density is 9.75-9.93g/cm^3, the resistivity is 2.31-2.55 μΩ ·cm, the hardness is 880-985 MPa. Its mi-crostructureshows that the fine oxides have a uniform distribution in the silver matrix. The results ofmake-break capacity and temperature rise testing show that the new material has better ability ofanti-arc erosion and lower temperature rise than that of commonly used Ag/CdO.
文摘A new silver rare earth oxide contact material, Ag/La2O3(12), was produced by powder metallurgy method. Its performances are as follows: the density is 9.71 similar to 9.96 g.cm(-3); the hardness (HB) is 760 similar to 970 MPa and the resistivity is 2.25 similar to 2.38 mu Omega . cm. The microstructure of Ag/La2O3(12) mas analyzed by SEM and EDS. Rare earth oxide La2O3 shows two shapes, which are uniformly distributed in the form of sphere and abnormality in Ag matrix. La2O3 shows fine spherical shape in the melted area of Ag after laser acting which is used to simulate electric are. The results are contributed to the less splash erosion of Ag. Compared with the main physical and mechanical properties of Ag/SnO2(12) and Ag/CdO(12), the properties of three contact materials are similar, and hence Ag/La2O3(12) may become a potential contact material to be used as the substitute of Ag/CdO(12).