Both Cu60Ni38Co2 and Cu60Ni40 alloy were naturally cooled after rapid solidification from the liquid phase.The transformation law of the microstructure characteristics of the rapidly solidified alloy with the change o...Both Cu60Ni38Co2 and Cu60Ni40 alloy were naturally cooled after rapid solidification from the liquid phase.The transformation law of the microstructure characteristics of the rapidly solidified alloy with the change of undercooling(DT)was systematically studied.It was found that the two alloys experienced the same transformation process.The refinement structures under different undercoolings were characterized by electron backscatter diffraction(EBSD).The experimental results show that the characteristics of the refinement structure of the two alloys with low undercooling are the same,whereas,the characteristics of the refinement structure with high undercooling are opposite.The transmission electron microscope(TEM)results of Cu60Ni38Co2 alloy show that the dislocation network density of low undercooled microstructure is lower than that of high undercooled microstructure.By combining EBSD and TEM,it can be confirmed that the dendrite remelting fracture is the reason for the refinement of the low undercooled structure,while the high undercooled structure is refined due to recrystallization.展开更多
Both Cu60Ni38Co2 and Cu60Ni40 alloy were naturally cooled after rapid solidification from the liquid phase.The transformation law of the microstructure characteristics of the rapidly solidified alloy with the change o...Both Cu60Ni38Co2 and Cu60Ni40 alloy were naturally cooled after rapid solidification from the liquid phase.The transformation law of the microstructure characteristics of the rapidly solidified alloy with the change of undercooling(ΔT)was systematically studied.It is found that the two alloys experience the same transformation process.The refinement structures under different undercoolings were characterized by electron backscatter diffraction(EBSD).The results show that the characteristics of the refinement structure of the two alloys with low undercooling are the same,but the characteristics of the refinement structure with high undercooling are opposite.The transmission electron microscopy(TEM)results of Cu60Ni38Co2 alloy show that the dislocation network density of low undercooled microstructure is lower than that of high undercooled microstructure.By combining EBSD and TEM,it could be confirmed that the dendrite remelting fracture is the reason for the refinement of the low undercooled structure,while the high undercooled structure is refined due to recrystallization.On this basis,in the processing of copper base alloys,there will be serious work hardening phenomenon and machining hard problem of consciousness problems caused by excessive cutting force.A twodimensional orthogonal turning finite element model was established using ABAQUS software to analyze the changes in cutting speed and tool trajectory in copper based alloy ultrasonic elliptical vibration turning.The results show that in copper based alloy ultrasonic elliptical vibration turning,cutting process parameters have a significant impact on cutting force.Choosing reasonable process parameters can effectively reduce cutting force and improve machining quality.展开更多
In order to increase the modifying effect, the Cu-P master alloy was rapidly solidified with melt-spin method, and the nano-sized ribbon was gained at 105?106 ℃/s. Subsequently, ZL109 alloy was modified by nanocrysta...In order to increase the modifying effect, the Cu-P master alloy was rapidly solidified with melt-spin method, and the nano-sized ribbon was gained at 105?106 ℃/s. Subsequently, ZL109 alloy was modified by nanocrystal and massive Cu-P master alloy, respectively, with molten metal casting method. The results show that the microscopic structure of ZL109 alloy modified by nanocrystal Cu-P master alloy is better than that modified by massive Cu-P master alloy, the original crystal silicon and eutectic silicon are refined more effectively and the mechanical properties are increased evidently: the tensile-strength is increased by 25%, the elongation is increased by 32.26% and the hardness is increased by 17.2%. Therefore, the melt-spin treatment is a feasible method to improve the modifying effect of Cu-P master alloy.展开更多
基金Funded by the Basic Research Projects in Shanxi Province(No.202103021224183)。
文摘Both Cu60Ni38Co2 and Cu60Ni40 alloy were naturally cooled after rapid solidification from the liquid phase.The transformation law of the microstructure characteristics of the rapidly solidified alloy with the change of undercooling(DT)was systematically studied.It was found that the two alloys experienced the same transformation process.The refinement structures under different undercoolings were characterized by electron backscatter diffraction(EBSD).The experimental results show that the characteristics of the refinement structure of the two alloys with low undercooling are the same,whereas,the characteristics of the refinement structure with high undercooling are opposite.The transmission electron microscope(TEM)results of Cu60Ni38Co2 alloy show that the dislocation network density of low undercooled microstructure is lower than that of high undercooled microstructure.By combining EBSD and TEM,it can be confirmed that the dendrite remelting fracture is the reason for the refinement of the low undercooled structure,while the high undercooled structure is refined due to recrystallization.
基金Funded by the Basic Research Projects in Shanxi Province(202103021224183)。
文摘Both Cu60Ni38Co2 and Cu60Ni40 alloy were naturally cooled after rapid solidification from the liquid phase.The transformation law of the microstructure characteristics of the rapidly solidified alloy with the change of undercooling(ΔT)was systematically studied.It is found that the two alloys experience the same transformation process.The refinement structures under different undercoolings were characterized by electron backscatter diffraction(EBSD).The results show that the characteristics of the refinement structure of the two alloys with low undercooling are the same,but the characteristics of the refinement structure with high undercooling are opposite.The transmission electron microscopy(TEM)results of Cu60Ni38Co2 alloy show that the dislocation network density of low undercooled microstructure is lower than that of high undercooled microstructure.By combining EBSD and TEM,it could be confirmed that the dendrite remelting fracture is the reason for the refinement of the low undercooled structure,while the high undercooled structure is refined due to recrystallization.On this basis,in the processing of copper base alloys,there will be serious work hardening phenomenon and machining hard problem of consciousness problems caused by excessive cutting force.A twodimensional orthogonal turning finite element model was established using ABAQUS software to analyze the changes in cutting speed and tool trajectory in copper based alloy ultrasonic elliptical vibration turning.The results show that in copper based alloy ultrasonic elliptical vibration turning,cutting process parameters have a significant impact on cutting force.Choosing reasonable process parameters can effectively reduce cutting force and improve machining quality.
基金Project(E2006000025) supported by the Natural Science Foundation of Hebei Province, China
文摘In order to increase the modifying effect, the Cu-P master alloy was rapidly solidified with melt-spin method, and the nano-sized ribbon was gained at 105?106 ℃/s. Subsequently, ZL109 alloy was modified by nanocrystal and massive Cu-P master alloy, respectively, with molten metal casting method. The results show that the microscopic structure of ZL109 alloy modified by nanocrystal Cu-P master alloy is better than that modified by massive Cu-P master alloy, the original crystal silicon and eutectic silicon are refined more effectively and the mechanical properties are increased evidently: the tensile-strength is increased by 25%, the elongation is increased by 32.26% and the hardness is increased by 17.2%. Therefore, the melt-spin treatment is a feasible method to improve the modifying effect of Cu-P master alloy.