Functionalized graphene oxide （FGO） was prepared by treating graphene oxide with y-aminopropyl triethoxysilane （KH-550） before the mixture was dispersed into a, ω-dihydroxy polydimethylsiloxane to get room temper...Functionalized graphene oxide （FGO） was prepared by treating graphene oxide with y-aminopropyl triethoxysilane （KH-550） before the mixture was dispersed into a, ω-dihydroxy polydimethylsiloxane to get room temperature vulcanized （RTV） silicone rubber composites by solution casting. The cured composites were then reduced with hydrazine hydrate to obtain functionalized graphene （FG）/RTV silicone rubber composites. The structures of FGO and the resultant composites were characterized by atomic force microscopy, FT-IR spectra and X-ray diffraction. KH-550 was found to be grafted onto graphene sheets, leading to an increased interlayer spacing. Significant improvements in thermal and mechanical properties were obtained. Both the FGO/RTV silicone rubber composite contain 1.0 wt% of FGO, and its reduced product showed an increase of one-step weight loss temperature with 61 ℃ and 133 ℃ higher than that of pure silicone rubber. Tensile strength and elongation at break of FG/RTV silicone rubber composite （with 0.5 wt% FGO content） increased by 175% and 67%, respectively, compared with those of pure silicone rubber.展开更多
In this work,molecular structures,dynamic mechanical properties and glass transition temperatures of microbe coagulated natural rubber（NR） samples were analyzed by using pyrolysis gas chromatography-mass spectrometr...In this work,molecular structures,dynamic mechanical properties and glass transition temperatures of microbe coagulated natural rubber（NR） samples were analyzed by using pyrolysis gas chromatography-mass spectrometry（py-GC/MS）,rubber process analyzer（RPA） and dynamic mechanical thermal analysis（DMA）.And the cross-linked network structures and mechanical properties of the corresponding NR vulcanizates were further determined by using nuclear magnetic resonance（NMR） crosslink density spectrometer（XLDS-15） and universal testing machines.The results show that NR raw rubber produced by rapidly coagulated with microorganism exhibits a simple molecular structure composition and good dynamic mechanical properties,and the corresponding NR vulcanizates possess the aggregation structure of high cross-linked density,a high glass transition temperature of-61.5 ℃ and high mechanical properties（tensile strength reaches 25.2 MPa）,as compared with that coagulated with acetic acid.展开更多
New natural rubber(NR)/nitrile butadiene rubber(NBR)/hindered phenol(AO-80)composites with high-damping properties were prepared in this study.The morpholo-gical,structural,and mechanical properties were characterized...New natural rubber(NR)/nitrile butadiene rubber(NBR)/hindered phenol(AO-80)composites with high-damping properties were prepared in this study.The morpholo-gical,structural,and mechanical properties were characterized by atomic force micro-scopy(AFM),polarized Fourier transform infrared spectrometer(FTIR),dynamic mechanical thermal analyzer(DMTA),and a tensile tester.Each composite consisted of two phases:the NR phase and the NBR/AO-80 phase.There was partial compat-ibility between the NR phase and the NBR/AO-80 phase,and the NR/NBR/AO-80(50/50/20)composite exhibited a co-continuous morphology.Strain-induced crystal-lization occurred in the NR phase at strains higher than 200%,and strain-induced orientation appeared in the NBR/AO-80 phase with the increase of strain from 100%to 500%.The composites had a special stress–strain behavior and mechanical properties because of the simultaneous strain-induced orientation and strain-induced crystalliza-tion.In the working temperature range of a seismic isolation bearing,the composites(especially the NR/NBR/AO-80(50/50/20)composite)presented a high loss factor,high area of loss peak(TA),and high hysteresis energy.Therefore,the NR/NBR/AO-80 rubber composites are expected to have important application as a high-perfor-mance damping material for rubber bearing.展开更多
This research focused on using the waste rubber powder as a kind of regenerate resources to improve the mechanical properties of cement mortar.The two kinds of hybrid modified rubber powder TRP and ATRP were prepared ...This research focused on using the waste rubber powder as a kind of regenerate resources to improve the mechanical properties of cement mortar.The two kinds of hybrid modified rubber powder TRP and ATRP were prepared by sol-gel method and then used in cement mortar.The structures and properties of them were studied.It is shown that the nano Si-O-Si network is generated in TRP and ATRP networks and the hydrophilic group is grafted on the surface of ATRP.The mechanical properties of rubber-treated mortar（RTM） were tested and the microstructures of them were also studied.Compared to the mortars with unmodified rubber powders（RP）,NaOH treated rubber powder（SRP） and coupling agent treated rubber powder（CRP）,the RTM with ATRP has the highest compressive strength and flexural strength.The stress-strain curves shown that the peak of stress of RTM with ATRP is increased and indicated the higher compression deformation and toughness.It is found that the interfacial adhesion between the ATRP and cement mortar is increased distinctly by SEM,which results in enhanced ductility and mechanical properties of RTM with ATRP.展开更多
基金Funded by the National Natural Science Foundation of China (No.51072059)
文摘Functionalized graphene oxide （FGO） was prepared by treating graphene oxide with y-aminopropyl triethoxysilane （KH-550） before the mixture was dispersed into a, ω-dihydroxy polydimethylsiloxane to get room temperature vulcanized （RTV） silicone rubber composites by solution casting. The cured composites were then reduced with hydrazine hydrate to obtain functionalized graphene （FG）/RTV silicone rubber composites. The structures of FGO and the resultant composites were characterized by atomic force microscopy, FT-IR spectra and X-ray diffraction. KH-550 was found to be grafted onto graphene sheets, leading to an increased interlayer spacing. Significant improvements in thermal and mechanical properties were obtained. Both the FGO/RTV silicone rubber composite contain 1.0 wt% of FGO, and its reduced product showed an increase of one-step weight loss temperature with 61 ℃ and 133 ℃ higher than that of pure silicone rubber. Tensile strength and elongation at break of FG/RTV silicone rubber composite （with 0.5 wt% FGO content） increased by 175% and 67%, respectively, compared with those of pure silicone rubber.
基金Special Fund for Agro-scientific Research in the Public Interest Project (nyhyzx07-033-6)Natural Science Foundation of Hainan Province (807047)
文摘In this work,molecular structures,dynamic mechanical properties and glass transition temperatures of microbe coagulated natural rubber（NR） samples were analyzed by using pyrolysis gas chromatography-mass spectrometry（py-GC/MS）,rubber process analyzer（RPA） and dynamic mechanical thermal analysis（DMA）.And the cross-linked network structures and mechanical properties of the corresponding NR vulcanizates were further determined by using nuclear magnetic resonance（NMR） crosslink density spectrometer（XLDS-15） and universal testing machines.The results show that NR raw rubber produced by rapidly coagulated with microorganism exhibits a simple molecular structure composition and good dynamic mechanical properties,and the corresponding NR vulcanizates possess the aggregation structure of high cross-linked density,a high glass transition temperature of-61.5 ℃ and high mechanical properties（tensile strength reaches 25.2 MPa）,as compared with that coagulated with acetic acid.
基金This work was supported by the National Natural Science Foundation of China[grant number 51320105012],[grant number 51221002],[grant number 51103006],[grant number 51373010].
文摘New natural rubber(NR)/nitrile butadiene rubber(NBR)/hindered phenol(AO-80)composites with high-damping properties were prepared in this study.The morpholo-gical,structural,and mechanical properties were characterized by atomic force micro-scopy(AFM),polarized Fourier transform infrared spectrometer(FTIR),dynamic mechanical thermal analyzer(DMTA),and a tensile tester.Each composite consisted of two phases:the NR phase and the NBR/AO-80 phase.There was partial compat-ibility between the NR phase and the NBR/AO-80 phase,and the NR/NBR/AO-80(50/50/20)composite exhibited a co-continuous morphology.Strain-induced crystal-lization occurred in the NR phase at strains higher than 200%,and strain-induced orientation appeared in the NBR/AO-80 phase with the increase of strain from 100%to 500%.The composites had a special stress–strain behavior and mechanical properties because of the simultaneous strain-induced orientation and strain-induced crystalliza-tion.In the working temperature range of a seismic isolation bearing,the composites(especially the NR/NBR/AO-80(50/50/20)composite)presented a high loss factor,high area of loss peak(TA),and high hysteresis energy.Therefore,the NR/NBR/AO-80 rubber composites are expected to have important application as a high-perfor-mance damping material for rubber bearing.
文摘This research focused on using the waste rubber powder as a kind of regenerate resources to improve the mechanical properties of cement mortar.The two kinds of hybrid modified rubber powder TRP and ATRP were prepared by sol-gel method and then used in cement mortar.The structures and properties of them were studied.It is shown that the nano Si-O-Si network is generated in TRP and ATRP networks and the hydrophilic group is grafted on the surface of ATRP.The mechanical properties of rubber-treated mortar（RTM） were tested and the microstructures of them were also studied.Compared to the mortars with unmodified rubber powders（RP）,NaOH treated rubber powder（SRP） and coupling agent treated rubber powder（CRP）,the RTM with ATRP has the highest compressive strength and flexural strength.The stress-strain curves shown that the peak of stress of RTM with ATRP is increased and indicated the higher compression deformation and toughness.It is found that the interfacial adhesion between the ATRP and cement mortar is increased distinctly by SEM,which results in enhanced ductility and mechanical properties of RTM with ATRP.