The goal is to develop a hybrid IPN network of polyvinyl acetate (PVAc) and ethylene-vinyl acetate (VAE). In this research work, the vinyl acetate (VAc)/ VAE hybrid emulsion and polyvinyl acetate emulsion (PVAc) were ...The goal is to develop a hybrid IPN network of polyvinyl acetate (PVAc) and ethylene-vinyl acetate (VAE). In this research work, the vinyl acetate (VAc)/ VAE hybrid emulsion and polyvinyl acetate emulsion (PVAc) were effectively synthesized. Emulsions with various characteristics have been developed by adjusting the weight ratios between the vinyl acetate monomer and the VAE component. The impacts on the mechanical, thermal, and physical properties of the films were investigated using tests for pencil hardness, tensile shear strength, pH, contact angle measurement, differential scanning calorimetry (DSC), and viscosity. When 5.0 weight percent VAE was added, the tensile shear strength in dry conditions decreased by 18.75% after a 24-hour bonding period, the heat resistance decreased by 26.29% (as per WATT 91) and the tensile shear strength decreased by approximately 36.52% in wet conditions (per EN 204). The pristine sample’s results were also confirmed by the contact angle test. The interpenetrating network (IPN) formation in hybrid PVAc emulsion as primary bonds does not directly attach to PVAc and VAE chains. The addition of VAE reduced the mechanical properties (at dry conditions) and heat resistance as per WATT 91. Contact angle analysis demonstrated that PVAc adhesives containing VAE had increased water resistance when compared to conventional PVA stabilised PVAc homopolymer-based adhesives. When compared to virgin PVAc Homo, the water resistance of the PVAc emulsion polymerization was enhanced by the addition of VAE.展开更多
Polyvinyl alcohol (PVA) stabilized Polyvinyl acetate (PVAc) dispersions-based wood adhesive has poor water and heat resistance. Recently, the addition of fillers in the wood adhesive is one of the most effective ways ...Polyvinyl alcohol (PVA) stabilized Polyvinyl acetate (PVAc) dispersions-based wood adhesive has poor water and heat resistance. Recently, the addition of fillers in the wood adhesive is one of the most effective ways to enhance the performance of PVAc wood adhesive. Inorganic fillers have unique characteristics to improve the performance of adhesive, such as small size, high surface energy and surface hardness. Hence, the present work investigates the applicability of calcium carbonate and clay incorporated 3% in situ emulsion polymerization PVAc wood adhesive. Effect on physical, thermal and mechanical properties was studied by viscosity, pH, contact angle measurement, differential scanning calorimetry (DSC) and pencil hardness test of films. Emulsions with 3% calcium carbonate and 3% clay were prepared and the shear strength of the applied adhesive on wood was measured. The viscosity of the adhesives was reduced in the case of the addition of calcium carbonate and increased in the case of clay. The mechanical properties like tensile strength of adhesives with calcium carbonate and clay were measured by a universal tensile machine (UTM). Thermal stability was studied by differential scanning calorimetry (DSC). The tensile shear strength demonstrates that clay can improve bonding strength as compared to calcium carbonate of PVAc adhesive in wet conditions. The hardness of PVAc films was also changed positively by the addition of calcium carbonate and clay. Thermal stability of PVAc was significantly improved as calcium carbonate and clay were added to PVAc. Here, we did a comparative study of the effect of the addition of calcium carbonate and clay filler materials in situ polymerization of PVAc on their different properties.展开更多
文摘The goal is to develop a hybrid IPN network of polyvinyl acetate (PVAc) and ethylene-vinyl acetate (VAE). In this research work, the vinyl acetate (VAc)/ VAE hybrid emulsion and polyvinyl acetate emulsion (PVAc) were effectively synthesized. Emulsions with various characteristics have been developed by adjusting the weight ratios between the vinyl acetate monomer and the VAE component. The impacts on the mechanical, thermal, and physical properties of the films were investigated using tests for pencil hardness, tensile shear strength, pH, contact angle measurement, differential scanning calorimetry (DSC), and viscosity. When 5.0 weight percent VAE was added, the tensile shear strength in dry conditions decreased by 18.75% after a 24-hour bonding period, the heat resistance decreased by 26.29% (as per WATT 91) and the tensile shear strength decreased by approximately 36.52% in wet conditions (per EN 204). The pristine sample’s results were also confirmed by the contact angle test. The interpenetrating network (IPN) formation in hybrid PVAc emulsion as primary bonds does not directly attach to PVAc and VAE chains. The addition of VAE reduced the mechanical properties (at dry conditions) and heat resistance as per WATT 91. Contact angle analysis demonstrated that PVAc adhesives containing VAE had increased water resistance when compared to conventional PVA stabilised PVAc homopolymer-based adhesives. When compared to virgin PVAc Homo, the water resistance of the PVAc emulsion polymerization was enhanced by the addition of VAE.
文摘Polyvinyl alcohol (PVA) stabilized Polyvinyl acetate (PVAc) dispersions-based wood adhesive has poor water and heat resistance. Recently, the addition of fillers in the wood adhesive is one of the most effective ways to enhance the performance of PVAc wood adhesive. Inorganic fillers have unique characteristics to improve the performance of adhesive, such as small size, high surface energy and surface hardness. Hence, the present work investigates the applicability of calcium carbonate and clay incorporated 3% in situ emulsion polymerization PVAc wood adhesive. Effect on physical, thermal and mechanical properties was studied by viscosity, pH, contact angle measurement, differential scanning calorimetry (DSC) and pencil hardness test of films. Emulsions with 3% calcium carbonate and 3% clay were prepared and the shear strength of the applied adhesive on wood was measured. The viscosity of the adhesives was reduced in the case of the addition of calcium carbonate and increased in the case of clay. The mechanical properties like tensile strength of adhesives with calcium carbonate and clay were measured by a universal tensile machine (UTM). Thermal stability was studied by differential scanning calorimetry (DSC). The tensile shear strength demonstrates that clay can improve bonding strength as compared to calcium carbonate of PVAc adhesive in wet conditions. The hardness of PVAc films was also changed positively by the addition of calcium carbonate and clay. Thermal stability of PVAc was significantly improved as calcium carbonate and clay were added to PVAc. Here, we did a comparative study of the effect of the addition of calcium carbonate and clay filler materials in situ polymerization of PVAc on their different properties.
