A facile technique is herein reported to fabricate three-dimensional （3D） polymeric porous scaffolds with interior surfaces of a topographic microstructure favorable for cell adhesion. As demonstration, a well-known...A facile technique is herein reported to fabricate three-dimensional （3D） polymeric porous scaffolds with interior surfaces of a topographic microstructure favorable for cell adhesion. As demonstration, a well-known biodegradable polymer poly（lactide-co-glycolide） （PLGA） was employed as matrix. Under the porogen-leaching strategy, the large and soft porogens of paraffin were modified by colliding with small and hard salt particles, which generated micropits on the surfaces of paraffin spheres. The eventual PLGA scaffolds after leaching the modified porogens had thus interior surfaces of microscale roughness imprinted by those micropits. The microrough scaffolds were confirmed to benefit adhesion of bone marrow stromal cells （BMSCs） of rats and meanwhile not to hamper the proliferation and osteogenic differentiation of the cells. The insight and technique might be helpful for biomaterial designing in tissue engineering and regenerative medicine.展开更多
In this paper, preparation of nano-biphasic calcium phosphate （nBCP）, mechanical behavior and load-bearing of poly （lactide-co-glycolide） （PLGA） and PLGA/nBCP are presented. The nBCP with composition of 63/37 （...In this paper, preparation of nano-biphasic calcium phosphate （nBCP）, mechanical behavior and load-bearing of poly （lactide-co-glycolide） （PLGA） and PLGA/nBCP are presented. The nBCP with composition of 63/37 （w/w） HA/-TCP （hydroxyapatite/fl-tricalcium phosphate） was produced by heating of bovine bone at 700℃. Composite scaffolds were made by using PLGA matrix and 10-50 wt% nBCP powders as reinforcement material. All scaffolds were prepared by thermally induced solid-liquid phase separation （TIPS） at -60~C under 4 Pa （0.04 mbar） vacuum. The results of elastic modulus testing were adjusted with Ishai-Cohen and Narkis models for rigid polymeric matrix and compared to each other. PLGA/nBCP scaffolds with 30 wt% nBCP showed the highest value of yield strength among the scaffolds. In addition, it was found that by increasing the nBCP in scaffolds to 50 wt%, the modulus of elasticity was highly enhanced. However, the optimum value of yield strength was obtained at 30 wt% nBCP, and the agglomeration of reinforcing particles at higher percentages caused a reduction in yield strength. It is clear that the elastic modulus of matrix has the significant role in elastic modulus of scaffolds, as also the size of the filler particles in the matrix.展开更多
Poly(lactide-co-glycolide acid)(PLGA) is an extraordinary well-described polymer and has excellent pharmaceutical properties like high biocompatibility and good biodegradability. Hence, it is one of the most used mate...Poly(lactide-co-glycolide acid)(PLGA) is an extraordinary well-described polymer and has excellent pharmaceutical properties like high biocompatibility and good biodegradability. Hence, it is one of the most used materials for drug delivery and biomedical systems, also being present in several US Food and Drug Administration-approved carrier systems and therapeutic devices. For both applications, the quantification of the polymer is inalienable. During the development of a production process, parameters like yield or loading efficacy are essential to be determined. Although PLGA is a well-defined biomaterial,it still lacks a sensitive and convenient quantification approach for PLGA-based systems. Thus, we present a novel method for the fast and precise quantification of PLGA by RP-HPLC. The polymer is hydrolyzed into its monomers, glycolic acid and lactic acid. Afterwards, the monomers are derivatized with the absorption-enhancing molecule 2,4′-dibromoacetophenone. Furthermore, the wavelength of the derivatized monomers is shifted to higher wavelengths, where the used solvents show a lower absorption,increasing the sensitivity and detectability. The developed method has a detection limit of 0.1 mg/mL,enabling the quantification of low amounts of PLGA. By quantifying both monomers separately, information about the PLGA monomer ratio can be also directly obtained, being relevant for degradation behavior. Compared to existing approaches, like gravimetric or nuclear magnetic resonance measurements, which are tedious or expensive, the developed method is fast, ideal for routine screening, and it is selective since no stabilizer or excipient is interfering. Due to the high sensitivity and rapidity of the method, it is suitable for both laboratory and industrial uses.展开更多
When a protein is encapsulated into poly( DL -lactide-co-glycolide)(PLGA) microspheres by means of the double-emulsion method,the harsh microspheres formation process including ultrasonification,exposure to an organic...When a protein is encapsulated into poly( DL -lactide-co-glycolide)(PLGA) microspheres by means of the double-emulsion method,the harsh microspheres formation process including ultrasonification,exposure to an organic solvent and a polymer may cause the denaturation of the protein. In this study,we investigated the enzymatic activity change and the effect of the excipients on the stability of recombinant human Cu,Zn-superoxide dismutase(rhCu,Zn-SOD) during the emulsification. The specific activity recovery was found to be concentration dependent and the excipients involved such as PEG 600 and Tween 20,and trehalose were shown to increase the stability of rhCu,Zn-SOD. The protein structural integrity within the microspheres was analyzed by FTIR. The structure of rhCu,Zn-SOD within PLGA microspheres containing trehalose was found to be similar to that of the native solid state,whereas the protein encapsulated during the preparation in the absence of any excipient changed due to the possible hydrophobic interaction with the polymer. The results suggest that a rational stability strategy for protein to be encapsulated into microspheres should aim at different processes.展开更多
目的建立一种与体内释药数据相关的体外加速释药评价方法，用于胸腺五肽微球的处方优化和质量控制。方法残留法测定微球在大鼠体内的释放情况，绘制体内累积释药曲线；对体外加速释放的重要条件进行筛选，包括释放介质种类、乙醇浓度、...目的建立一种与体内释药数据相关的体外加速释药评价方法，用于胸腺五肽微球的处方优化和质量控制。方法残留法测定微球在大鼠体内的释放情况，绘制体内累积释药曲线；对体外加速释放的重要条件进行筛选，包括释放介质种类、乙醇浓度、表面活性剂浓度、加热温度，进行体内外释放相关性拟合，最大程度模拟体内释放，并采用最终优化的条件验证另两种处方。结果最终优化的体外释放条件为：20%（V/V）乙醇中含0.06%（W/V）Tween 80作为释放介质，程序升温（0～1 h 40°C，1～6 h 45°C，6～30 h 50°C）的方法用于介质加热，（8、13和28）×1033种相对分子质量PLGA制备的微球体外加速曲线与体内释药曲线相关系数r2依次为0.9783、0.9886和0.9780。结论释放介质中加入乙醇并采取程序升温的办法，能最大程度模拟体内释药，可用于胸腺五肽微球的处方优化和质量控制。展开更多
基金financially supported by Chinese Ministry of Science and Technology(973 programs Nos.2009CB930000 and 2011CB606203)NSF of China(Nos.21034002,91127028 and 51273046)
文摘A facile technique is herein reported to fabricate three-dimensional （3D） polymeric porous scaffolds with interior surfaces of a topographic microstructure favorable for cell adhesion. As demonstration, a well-known biodegradable polymer poly（lactide-co-glycolide） （PLGA） was employed as matrix. Under the porogen-leaching strategy, the large and soft porogens of paraffin were modified by colliding with small and hard salt particles, which generated micropits on the surfaces of paraffin spheres. The eventual PLGA scaffolds after leaching the modified porogens had thus interior surfaces of microscale roughness imprinted by those micropits. The microrough scaffolds were confirmed to benefit adhesion of bone marrow stromal cells （BMSCs） of rats and meanwhile not to hamper the proliferation and osteogenic differentiation of the cells. The insight and technique might be helpful for biomaterial designing in tissue engineering and regenerative medicine.
基金supported by Isfahan University of Technology and Ministry of Sciences, Research & Technology in Iran and Materials Science & Engineering School of Nanyang Technological University in Singapore
文摘In this paper, preparation of nano-biphasic calcium phosphate （nBCP）, mechanical behavior and load-bearing of poly （lactide-co-glycolide） （PLGA） and PLGA/nBCP are presented. The nBCP with composition of 63/37 （w/w） HA/-TCP （hydroxyapatite/fl-tricalcium phosphate） was produced by heating of bovine bone at 700℃. Composite scaffolds were made by using PLGA matrix and 10-50 wt% nBCP powders as reinforcement material. All scaffolds were prepared by thermally induced solid-liquid phase separation （TIPS） at -60~C under 4 Pa （0.04 mbar） vacuum. The results of elastic modulus testing were adjusted with Ishai-Cohen and Narkis models for rigid polymeric matrix and compared to each other. PLGA/nBCP scaffolds with 30 wt% nBCP showed the highest value of yield strength among the scaffolds. In addition, it was found that by increasing the nBCP in scaffolds to 50 wt%, the modulus of elasticity was highly enhanced. However, the optimum value of yield strength was obtained at 30 wt% nBCP, and the agglomeration of reinforcing particles at higher percentages caused a reduction in yield strength. It is clear that the elastic modulus of matrix has the significant role in elastic modulus of scaffolds, as also the size of the filler particles in the matrix.
文摘Poly(lactide-co-glycolide acid)(PLGA) is an extraordinary well-described polymer and has excellent pharmaceutical properties like high biocompatibility and good biodegradability. Hence, it is one of the most used materials for drug delivery and biomedical systems, also being present in several US Food and Drug Administration-approved carrier systems and therapeutic devices. For both applications, the quantification of the polymer is inalienable. During the development of a production process, parameters like yield or loading efficacy are essential to be determined. Although PLGA is a well-defined biomaterial,it still lacks a sensitive and convenient quantification approach for PLGA-based systems. Thus, we present a novel method for the fast and precise quantification of PLGA by RP-HPLC. The polymer is hydrolyzed into its monomers, glycolic acid and lactic acid. Afterwards, the monomers are derivatized with the absorption-enhancing molecule 2,4′-dibromoacetophenone. Furthermore, the wavelength of the derivatized monomers is shifted to higher wavelengths, where the used solvents show a lower absorption,increasing the sensitivity and detectability. The developed method has a detection limit of 0.1 mg/mL,enabling the quantification of low amounts of PLGA. By quantifying both monomers separately, information about the PLGA monomer ratio can be also directly obtained, being relevant for degradation behavior. Compared to existing approaches, like gravimetric or nuclear magnetic resonance measurements, which are tedious or expensive, the developed method is fast, ideal for routine screening, and it is selective since no stabilizer or excipient is interfering. Due to the high sensitivity and rapidity of the method, it is suitable for both laboratory and industrial uses.
文摘When a protein is encapsulated into poly( DL -lactide-co-glycolide)(PLGA) microspheres by means of the double-emulsion method,the harsh microspheres formation process including ultrasonification,exposure to an organic solvent and a polymer may cause the denaturation of the protein. In this study,we investigated the enzymatic activity change and the effect of the excipients on the stability of recombinant human Cu,Zn-superoxide dismutase(rhCu,Zn-SOD) during the emulsification. The specific activity recovery was found to be concentration dependent and the excipients involved such as PEG 600 and Tween 20,and trehalose were shown to increase the stability of rhCu,Zn-SOD. The protein structural integrity within the microspheres was analyzed by FTIR. The structure of rhCu,Zn-SOD within PLGA microspheres containing trehalose was found to be similar to that of the native solid state,whereas the protein encapsulated during the preparation in the absence of any excipient changed due to the possible hydrophobic interaction with the polymer. The results suggest that a rational stability strategy for protein to be encapsulated into microspheres should aim at different processes.
文摘目的建立一种与体内释药数据相关的体外加速释药评价方法，用于胸腺五肽微球的处方优化和质量控制。方法残留法测定微球在大鼠体内的释放情况，绘制体内累积释药曲线；对体外加速释放的重要条件进行筛选，包括释放介质种类、乙醇浓度、表面活性剂浓度、加热温度，进行体内外释放相关性拟合，最大程度模拟体内释放，并采用最终优化的条件验证另两种处方。结果最终优化的体外释放条件为：20%（V/V）乙醇中含0.06%（W/V）Tween 80作为释放介质，程序升温（0～1 h 40°C，1～6 h 45°C，6～30 h 50°C）的方法用于介质加热，（8、13和28）×1033种相对分子质量PLGA制备的微球体外加速曲线与体内释药曲线相关系数r2依次为0.9783、0.9886和0.9780。结论释放介质中加入乙醇并采取程序升温的办法，能最大程度模拟体内释药，可用于胸腺五肽微球的处方优化和质量控制。