Ag_(3)PO_(4)exhibits a high photocatalytic activity if exposed to visible light,however,it displays bottlenecks such as poor cycle-stability and mediocre ability to degrade methyl orange(MO)because of limited adsorpti...Ag_(3)PO_(4)exhibits a high photocatalytic activity if exposed to visible light,however,it displays bottlenecks such as poor cycle-stability and mediocre ability to degrade methyl orange(MO)because of limited adsorption of MO molecules onto its surface.In this study,nano TiO_(2)prepared by a one-step method was combined with Ag_(3)PO_(4)to form a TiO_(2)@Ag_(3)PO_(4)heterojunction in order to improve this material both in terms of photocatalysis and photostability.After adding a KH-570 silane coupling agent,the photocatalytic performance of TiO_(2)@Ag_(3)PO_(4)could be improved even further,with the degradation rate of MO maintained at more than 90%after three cycles of visible in light.展开更多
A new upconversion luminescence agent, 40CdF2·60BaF2·0.8ErO3, was synthesized and its fluorescent spectra were determined. This upconversion luminescence agent can emit five upconversion fluorescent peaks sh...A new upconversion luminescence agent, 40CdF2·60BaF2·0.8ErO3, was synthesized and its fluorescent spectra were determined. This upconversion luminescence agent can emit five upconversion fluorescent peaks shown in the fluorescent spectra whose wavelengths are all below 387 nm under the excitation of 488 nm visible light. This upconversion luminescence agent was mixed into nano rutile TiO2 powder by ultrasonic and boiling dispersion and the novel doped nano TiO2 photocatalyst utilizing visible light was firstly prepared. The doped TiO2 powder was charactered by XRD and TEM and its photocatalytic activity was tested through the photocatalytic degradation of methyl orange as a model compound under the visible light irradiation emitted by six three basic color lamps. In order to compare the photocatalytic activities, the same experiment was carried out for undoped TiO2 powder. The degradation ratio of methyl orange in the presence of doped nano TiO2 powder reached 32.5% under visible light irradiation at 20 h which was obviously higher than the corresponding 1.64% in the presence of undoped nano TiO2 powder, which indicate the upconversion luminescence agent prepared as dopant can effectively turn visible lights to ultraviolet lights that are absorbed by nano TiO2 particles to produce the electron-cavity pairs. All the results show that the nano rutile TiO2 powder doped with upconversion luminescence agent is a promising photocatalyst using sunlight for treating the industry dye wastewater in great force.展开更多
基金This work was supported by the Natural Science Foundation of the Jiangsu Higher Education Institutions of China(No.18KJD430009)the Qing Lan Project of Jiangsu Province.
文摘Ag_(3)PO_(4)exhibits a high photocatalytic activity if exposed to visible light,however,it displays bottlenecks such as poor cycle-stability and mediocre ability to degrade methyl orange(MO)because of limited adsorption of MO molecules onto its surface.In this study,nano TiO_(2)prepared by a one-step method was combined with Ag_(3)PO_(4)to form a TiO_(2)@Ag_(3)PO_(4)heterojunction in order to improve this material both in terms of photocatalysis and photostability.After adding a KH-570 silane coupling agent,the photocatalytic performance of TiO_(2)@Ag_(3)PO_(4)could be improved even further,with the degradation rate of MO maintained at more than 90%after three cycles of visible in light.
基金The National Natural Science Foundation of China (No.20371023)
文摘A new upconversion luminescence agent, 40CdF2·60BaF2·0.8ErO3, was synthesized and its fluorescent spectra were determined. This upconversion luminescence agent can emit five upconversion fluorescent peaks shown in the fluorescent spectra whose wavelengths are all below 387 nm under the excitation of 488 nm visible light. This upconversion luminescence agent was mixed into nano rutile TiO2 powder by ultrasonic and boiling dispersion and the novel doped nano TiO2 photocatalyst utilizing visible light was firstly prepared. The doped TiO2 powder was charactered by XRD and TEM and its photocatalytic activity was tested through the photocatalytic degradation of methyl orange as a model compound under the visible light irradiation emitted by six three basic color lamps. In order to compare the photocatalytic activities, the same experiment was carried out for undoped TiO2 powder. The degradation ratio of methyl orange in the presence of doped nano TiO2 powder reached 32.5% under visible light irradiation at 20 h which was obviously higher than the corresponding 1.64% in the presence of undoped nano TiO2 powder, which indicate the upconversion luminescence agent prepared as dopant can effectively turn visible lights to ultraviolet lights that are absorbed by nano TiO2 particles to produce the electron-cavity pairs. All the results show that the nano rutile TiO2 powder doped with upconversion luminescence agent is a promising photocatalyst using sunlight for treating the industry dye wastewater in great force.