The mineralogical phase transformation of a low-grade nickel laterite ore during pre-roasting process and the extraction of silicon during alkaline leaching process were investigated.The results indicate that the reac...The mineralogical phase transformation of a low-grade nickel laterite ore during pre-roasting process and the extraction of silicon during alkaline leaching process were investigated.The results indicate that the reaction activity of nickel ores is effectively improved by pre-roasting at650°C for2h,because of the transformation of lizardite into magnesium olivine and protoenstatite.When finely ground ore samples(44-61μm)pre-roasted firstly react with sodium hydroxide solution(60g/L)with a solid/liquid ratio of1:5at140°C for120min,the extraction of silicon can reach89.89%,and the other valuable elements of magnesium,iron and nickel are accumulated in the solid residues.The leaching kinetics of nickel laterite ore can be described successfully by the diffusion through the product layer control model.The activation energy is calculated to be11.63kJ/mol and the kinetics equation can be expressed as1-3(1-x)2/3+2(1-x)=13.53×10-2exp[-11.63/(RT)]t.展开更多
Abstract The α ＋ β→β phase transformation kinetics of Ti-1300 alloy during continuous heating at different heating rates were investigated using dilatometric method. Results show that the curves of the α ＋ β...Abstract The α ＋ β→β phase transformation kinetics of Ti-1300 alloy during continuous heating at different heating rates were investigated using dilatometric method. Results show that the curves of the α ＋ β→β phase transformation exhibit a typical S-shaped pattern, which indicates that the α ＋ β→β phase transformation is a nucleation-growth-controlled process. The overall activation energy of the α ＋ β→β transformation of the alloy is 797 kJ·mol^-1. The nucleation and growth mechanism of the α ＋ β→β transformation was also investigated using the non-isothermal Avrami exponent. The Avrami exponent during α ＋ β→β transformation process significantly changes with transformed volume fraction increasing, which indicates that the α ＋ β→β transformation mechanism in the Ti-1300 alloy varies at different sections.展开更多
基金Project(2014CB643405) supported by the National Basic Research Program of ChinaProjects(51204036,51234009) supported by the National Natural Science Foundation of ChinaProject(BJ201604) supported by the Program for Top Young Talents of Higher Education Institutions of Hebei Province,China
文摘The mineralogical phase transformation of a low-grade nickel laterite ore during pre-roasting process and the extraction of silicon during alkaline leaching process were investigated.The results indicate that the reaction activity of nickel ores is effectively improved by pre-roasting at650°C for2h,because of the transformation of lizardite into magnesium olivine and protoenstatite.When finely ground ore samples(44-61μm)pre-roasted firstly react with sodium hydroxide solution(60g/L)with a solid/liquid ratio of1:5at140°C for120min,the extraction of silicon can reach89.89%,and the other valuable elements of magnesium,iron and nickel are accumulated in the solid residues.The leaching kinetics of nickel laterite ore can be described successfully by the diffusion through the product layer control model.The activation energy is calculated to be11.63kJ/mol and the kinetics equation can be expressed as1-3(1-x)2/3+2(1-x)=13.53×10-2exp[-11.63/(RT)]t.
基金National Key Research and Development Program of China(2016YFB0301400)State Key Program of National Natural Science Foundation of China(U1502274)+1 种基金Innovation Scientists and Technicians Troop Construction Projects of Henan Province(C20150014)Program for Innovation Research Team(in Science and Technology)in University of Henan Province(14IRTSTHN007)
基金financially supported by the National Natural Science Foundation of China(No.51401058)the Transformation Project of Major Scientific and Technological Achievements of Shanxi Province(No.2012KTCG04-14)the Science and Technology Innovation Team Project of Shanxi Province of China(No.2012KCT-23)
文摘Abstract The α ＋ β→β phase transformation kinetics of Ti-1300 alloy during continuous heating at different heating rates were investigated using dilatometric method. Results show that the curves of the α ＋ β→β phase transformation exhibit a typical S-shaped pattern, which indicates that the α ＋ β→β phase transformation is a nucleation-growth-controlled process. The overall activation energy of the α ＋ β→β transformation of the alloy is 797 kJ·mol^-1. The nucleation and growth mechanism of the α ＋ β→β transformation was also investigated using the non-isothermal Avrami exponent. The Avrami exponent during α ＋ β→β transformation process significantly changes with transformed volume fraction increasing, which indicates that the α ＋ β→β transformation mechanism in the Ti-1300 alloy varies at different sections.