Selective hydrogenolysis of biomass‐derived furfuryl alcohol(FFA)to 1,5‐and 1,2‐pentanediol(PeD)was conducted over Cu‐LaCoO3 catalysts with different Cu loadings;the catalysts were derived from perovskite structur...Selective hydrogenolysis of biomass‐derived furfuryl alcohol(FFA)to 1,5‐and 1,2‐pentanediol(PeD)was conducted over Cu‐LaCoO3 catalysts with different Cu loadings;the catalysts were derived from perovskite structures prepared by a one‐step citrate complexing method.The catalytic performances of the Cu‐LaCoO3 catalysts were found to depend on the Cu loading and pretreatment conditions.The catalyst with 10 wt%Cu loading exhibited the best catalytic performance after prereduction in 5%H2‐95%N2,achieving a high FFA conversion of 100%and selectivity of 55.5%for 1,5‐pentanediol(40.3%)and 1,2‐pentanediol(15.2%)at 413 K and 6 MPa H2.This catalyst could be reused four times without a loss of FFA conversion but it resulted in a slight decrease in pentanediol selectivity.Correlation between the structural changes in the catalysts at different states and the simultaneous variation in the catalytic performance revealed that cooperative catalysis between Cu0 and CoO promoted the hydrogenolysis of FFA to PeDs,especially to 1,5‐PeD,while Co0 promoted the hydrogenation of FFA to tetrahydrofurfuryl alcohol(THFA).Therefore,it is suggested that a synergetic effect between balanced Cu0 and CoO sites plays a critical role in achieving a high yield of PeDs with a high 1,5‐/1,2‐pentanediol selectivity ratio during FFA hydrogenolysis.展开更多
The present work explores the reaction pathways of γ-valerolactone(GVL) over a supported ruthenium catalyst. The conversion of GVL in aqueous phase over a 5% Ru/C catalyst was investigated in a batch reactor operatin...The present work explores the reaction pathways of γ-valerolactone(GVL) over a supported ruthenium catalyst. The conversion of GVL in aqueous phase over a 5% Ru/C catalyst was investigated in a batch reactor operating at 463 K under 500–1000 psi of H2. The main reaction products obtained under these conditions were 2-butanol(2-BuOH), 1,4-pentanediol(1,4-PDO), 2-methyltetrahydrofuran(2-MTHF) and 2-pentanol(2-PeOH). A complete reaction network was developed, identifying the primary and/or secondary products. In this reaction network, production of 2-BuOH via decarbonylation of a ring-opened surface intermediate CH3CH(O*)–(CH2)2–CO*is clearly the dominant pathway. From the evolution of products as a function of reaction time and theoretical(DFT) calculations, a mechanism for the formation of intermediates and products is proposed. The high sensitivity of 2-BuOH production to the presence of CO, compared to a much lower effect on the production of the other products indicates that the sites responsible for decarbonylation are particularly prone to CO adsorption and poisoning. Also, since the decarbonylation rate is not affected by the H2 pressure it is concluded that the direct decarbonylation path of the CH3CH(O*)–(CH2)2–CO*intermediate does not required a previous dehydrogenation step, as is the case in decarbonylation of short alcohols.展开更多
Cu nanoparticles supported on a variety of oxide supports, including SiO2, TiO2, ZrO2, Al2O3, MgO and ZnO, were investigated for the hydrogenolysis of biomass‐derived furfuryl alcohol to1,2‐pentanediol and 1,5‐pent...Cu nanoparticles supported on a variety of oxide supports, including SiO2, TiO2, ZrO2, Al2O3, MgO and ZnO, were investigated for the hydrogenolysis of biomass‐derived furfuryl alcohol to1,2‐pentanediol and 1,5‐pentanediol. A Cu‐Al2O3 catalyst with 10 wt% Cu loading prepared by a co‐precipitation method exhibited the best performance in terms of producing pentanediols compared with the other materials. This catalyst generated an 85.8% conversion and a 70.3% combined selectivity for the target pentanediols at 413 K and 8 MPa H2 over an 8‐h reaction. The catalyst could also be recycled over repeated reaction trials without any significant decrease in productivity. Characterizations with X‐ray diffraction, NH3/CO2‐temperature programmed desorption, N2 adsorption,transmission electron microscopy and N2 O chemisorption demonstrated that intimate and effective interactions between Cu particles and the acidic Al2O3 support in this material greatly enhanced its activity and selectivity. The promotion of the hydrogenolysis reaction was found to be especially sensitive to the Cu particle size, and the catalyst with Cu particles 1.9 to 2.4 nm in size showed the highest turnover frequency during the synthesis of pentanediols.展开更多
In this work, MoOx promoted Ir/SiO2 catalysts were prepared and used for the selective hydrogenolysis of tetrahydrofurfuryl alcohol （THFA） to 1,5-pentanediol in a continuous flow reactor. The effects of different no...In this work, MoOx promoted Ir/SiO2 catalysts were prepared and used for the selective hydrogenolysis of tetrahydrofurfuryl alcohol （THFA） to 1,5-pentanediol in a continuous flow reactor. The effects of different noble metals （Ir, Pt, Pd, Ru, Rh）, supports and Ir contents were screened. Among the investigated catalysts, 4 wt%Ir-MoOx/SiO2 with a Mo/Ir atomic ratio of 0.13 exhibited the best catalytic performance. The synergy between Ix particles and the partially reduced isolated MoOx species attached on them is essential for the excellent catalytic performance of Ix-MoOx/SiO2. The catalyst exhibited a better hydrogenolysis efficiency of THFA with the selectivity of 1,5-pentanediol of 65%-74% at a conversion of THFA of 70%-75% when the initial THFA concentration is ranging from 20 wt% and 40 wt%. And higher system pressure was also in favor of the conversion of THFA. During a stability test, the conversion of THFA and 1,5-pentanediol yield over Ix-MoOz/SiO2 decreased with reaction time, which can be explained by the leaching of Mo species during the reaction.展开更多
文摘Selective hydrogenolysis of biomass‐derived furfuryl alcohol(FFA)to 1,5‐and 1,2‐pentanediol(PeD)was conducted over Cu‐LaCoO3 catalysts with different Cu loadings;the catalysts were derived from perovskite structures prepared by a one‐step citrate complexing method.The catalytic performances of the Cu‐LaCoO3 catalysts were found to depend on the Cu loading and pretreatment conditions.The catalyst with 10 wt%Cu loading exhibited the best catalytic performance after prereduction in 5%H2‐95%N2,achieving a high FFA conversion of 100%and selectivity of 55.5%for 1,5‐pentanediol(40.3%)and 1,2‐pentanediol(15.2%)at 413 K and 6 MPa H2.This catalyst could be reused four times without a loss of FFA conversion but it resulted in a slight decrease in pentanediol selectivity.Correlation between the structural changes in the catalysts at different states and the simultaneous variation in the catalytic performance revealed that cooperative catalysis between Cu0 and CoO promoted the hydrogenolysis of FFA to PeDs,especially to 1,5‐PeD,while Co0 promoted the hydrogenation of FFA to tetrahydrofurfuryl alcohol(THFA).Therefore,it is suggested that a synergetic effect between balanced Cu0 and CoO sites plays a critical role in achieving a high yield of PeDs with a high 1,5‐/1,2‐pentanediol selectivity ratio during FFA hydrogenolysis.
基金the Department of Energy for funding the experimental part of this work under grant DE-SC0004600the theoretical part under grant DE-EE0006287 of the Bioenergy Technology Office CHASE program
文摘The present work explores the reaction pathways of γ-valerolactone(GVL) over a supported ruthenium catalyst. The conversion of GVL in aqueous phase over a 5% Ru/C catalyst was investigated in a batch reactor operating at 463 K under 500–1000 psi of H2. The main reaction products obtained under these conditions were 2-butanol(2-BuOH), 1,4-pentanediol(1,4-PDO), 2-methyltetrahydrofuran(2-MTHF) and 2-pentanol(2-PeOH). A complete reaction network was developed, identifying the primary and/or secondary products. In this reaction network, production of 2-BuOH via decarbonylation of a ring-opened surface intermediate CH3CH(O*)–(CH2)2–CO*is clearly the dominant pathway. From the evolution of products as a function of reaction time and theoretical(DFT) calculations, a mechanism for the formation of intermediates and products is proposed. The high sensitivity of 2-BuOH production to the presence of CO, compared to a much lower effect on the production of the other products indicates that the sites responsible for decarbonylation are particularly prone to CO adsorption and poisoning. Also, since the decarbonylation rate is not affected by the H2 pressure it is concluded that the direct decarbonylation path of the CH3CH(O*)–(CH2)2–CO*intermediate does not required a previous dehydrogenation step, as is the case in decarbonylation of short alcohols.
基金supported by the National Natural Science Foundation of China(2113301121203221+1 种基金21473224)the Natural Science Foundation of Gansu Province(1308RJZA281)~~
文摘Cu nanoparticles supported on a variety of oxide supports, including SiO2, TiO2, ZrO2, Al2O3, MgO and ZnO, were investigated for the hydrogenolysis of biomass‐derived furfuryl alcohol to1,2‐pentanediol and 1,5‐pentanediol. A Cu‐Al2O3 catalyst with 10 wt% Cu loading prepared by a co‐precipitation method exhibited the best performance in terms of producing pentanediols compared with the other materials. This catalyst generated an 85.8% conversion and a 70.3% combined selectivity for the target pentanediols at 413 K and 8 MPa H2 over an 8‐h reaction. The catalyst could also be recycled over repeated reaction trials without any significant decrease in productivity. Characterizations with X‐ray diffraction, NH3/CO2‐temperature programmed desorption, N2 adsorption,transmission electron microscopy and N2 O chemisorption demonstrated that intimate and effective interactions between Cu particles and the acidic Al2O3 support in this material greatly enhanced its activity and selectivity. The promotion of the hydrogenolysis reaction was found to be especially sensitive to the Cu particle size, and the catalyst with Cu particles 1.9 to 2.4 nm in size showed the highest turnover frequency during the synthesis of pentanediols.
基金supported by the National Natural Science Foundation of China(No.21106143,No.21277140)100-Talent Project of Dalian Institute of Chemical Physics(DICP)+1 种基金the Independent Innovation Foundation of State Key Laboratory of Catalysis(No.R201113)the Zhejiang Provincial Natural Science Foundation of China(LR12E02001)
文摘In this work, MoOx promoted Ir/SiO2 catalysts were prepared and used for the selective hydrogenolysis of tetrahydrofurfuryl alcohol （THFA） to 1,5-pentanediol in a continuous flow reactor. The effects of different noble metals （Ir, Pt, Pd, Ru, Rh）, supports and Ir contents were screened. Among the investigated catalysts, 4 wt%Ir-MoOx/SiO2 with a Mo/Ir atomic ratio of 0.13 exhibited the best catalytic performance. The synergy between Ix particles and the partially reduced isolated MoOx species attached on them is essential for the excellent catalytic performance of Ix-MoOx/SiO2. The catalyst exhibited a better hydrogenolysis efficiency of THFA with the selectivity of 1,5-pentanediol of 65%-74% at a conversion of THFA of 70%-75% when the initial THFA concentration is ranging from 20 wt% and 40 wt%. And higher system pressure was also in favor of the conversion of THFA. During a stability test, the conversion of THFA and 1,5-pentanediol yield over Ix-MoOz/SiO2 decreased with reaction time, which can be explained by the leaching of Mo species during the reaction.