The coarsening behavior of γ particles in a nickel-base superalloy FGH95 was investigated by means of experimental observations and growth kinetics calculations. The results show that when aging at 1000,1080 and 1140...The coarsening behavior of γ particles in a nickel-base superalloy FGH95 was investigated by means of experimental observations and growth kinetics calculations. The results show that when aging at 1000,1080 and 1140°C for different times,the relation of average particle size to time obeys the cube law ( a /2)3= kt,where k is 15.49 × 103,77.5 × 103 and 230.04 × 103 nm3/min,respectively. The particle size distributions are better fit to the LSW theoretical distributions when aging at 1000°C within 1440 min....展开更多
The coarsening and ageing hardening behaviors of γ′ particles in superalloy GH742 have been investigated by field emission scanning electron microscopy （FESEM）, coarsening kinetics calculation and microhardness te...The coarsening and ageing hardening behaviors of γ′ particles in superalloy GH742 have been investigated by field emission scanning electron microscopy （FESEM）, coarsening kinetics calculation and microhardness testing when ageing at 1 050, 950 and 900 ℃ for different time. The cube of γ′ particle size and ageing time follows a linear law as predicted by LSW theory. The particle size distributions give better fit to the LSW theoretical distribution. The activation energy for γ′ coarsening is accurately determined to have 245. 06±14.42 kJ/mol when considering the effect of temperature on the solution concentrations in matrix. Based on the activation energy, the coarsening kinetics of γ′ particle is predicted as r^-t^3=7.35×10^15 Ce/T exp -（245060±14420）/RT t.The microhardness studies indicate that microhardness decreases rapidly with increasing the ageing temperature and it has a maximum value corresponding to a critical particle size beyond which the microhardness increase stalls with increasing the ageing time.展开更多
基金the National Natural Science Foundation of China (No. 50471097)the Programme of Introducing Talents of Discipline to Chinese Universities (No. B07003).
文摘The coarsening behavior of γ particles in a nickel-base superalloy FGH95 was investigated by means of experimental observations and growth kinetics calculations. The results show that when aging at 1000,1080 and 1140°C for different times,the relation of average particle size to time obeys the cube law ( a /2)3= kt,where k is 15.49 × 103,77.5 × 103 and 230.04 × 103 nm3/min,respectively. The particle size distributions are better fit to the LSW theoretical distributions when aging at 1000°C within 1440 min....
基金Sponsored by National Natural Science Foundation of China(50471097)
文摘The coarsening and ageing hardening behaviors of γ′ particles in superalloy GH742 have been investigated by field emission scanning electron microscopy （FESEM）, coarsening kinetics calculation and microhardness testing when ageing at 1 050, 950 and 900 ℃ for different time. The cube of γ′ particle size and ageing time follows a linear law as predicted by LSW theory. The particle size distributions give better fit to the LSW theoretical distribution. The activation energy for γ′ coarsening is accurately determined to have 245. 06±14.42 kJ/mol when considering the effect of temperature on the solution concentrations in matrix. Based on the activation energy, the coarsening kinetics of γ′ particle is predicted as r^-t^3=7.35×10^15 Ce/T exp -（245060±14420）/RT t.The microhardness studies indicate that microhardness decreases rapidly with increasing the ageing temperature and it has a maximum value corresponding to a critical particle size beyond which the microhardness increase stalls with increasing the ageing time.