In the present study,V3O5 microcrystals that synthesized via vacuum calcination are employed as anodes for lithium-ion batteries(LIBs)for the first time.Despite the widely observed sluggish reaction kinetics and poor ...In the present study,V3O5 microcrystals that synthesized via vacuum calcination are employed as anodes for lithium-ion batteries(LIBs)for the first time.Despite the widely observed sluggish reaction kinetics and poor cycling stability in most microsized transition metal oxides,the V3O5 microcrystals exhibit excellent rate capability(specific capacities of 144 and 125 mAh g^−1 are achieved at extremely high current densities of 20 and 50 A g^−1,respectively)and long-term cycling performance(specific capacity of 117 mAh g^−1 is sustained over 2000 cycles at 50 A g^−1).It is ascribed to the three-dimensional open-framework structure of the V3O5 microcrystals as a major factor in dictating the fast reaction kinetics(lithium diffusion coefficient:~10−9 cm^2 s^−1).In addition,significant insight into the reaction mechanism of the V3O5 microcrystals in concomitant its phase evolution are obtained from ex-situ XRD study,revealing that the V3O5 microcrystals undergo intercalation reaction with insignificant structural change in response to lithiation/delithiation.展开更多
基金The authors gratefully acknowledge the National Key R&D Research Program of China(No.2018YFB0905400)National Natural Science Foundation of China(Grant Nos.51622210,51872277,21606003,51802044 and 51420105002)+1 种基金the DNL cooperation Fund,CAS(DNL180310)Opening Project of CAS Key Laboratory of Materials for Energy Conversion。
文摘In the present study,V3O5 microcrystals that synthesized via vacuum calcination are employed as anodes for lithium-ion batteries(LIBs)for the first time.Despite the widely observed sluggish reaction kinetics and poor cycling stability in most microsized transition metal oxides,the V3O5 microcrystals exhibit excellent rate capability(specific capacities of 144 and 125 mAh g^−1 are achieved at extremely high current densities of 20 and 50 A g^−1,respectively)and long-term cycling performance(specific capacity of 117 mAh g^−1 is sustained over 2000 cycles at 50 A g^−1).It is ascribed to the three-dimensional open-framework structure of the V3O5 microcrystals as a major factor in dictating the fast reaction kinetics(lithium diffusion coefficient:~10−9 cm^2 s^−1).In addition,significant insight into the reaction mechanism of the V3O5 microcrystals in concomitant its phase evolution are obtained from ex-situ XRD study,revealing that the V3O5 microcrystals undergo intercalation reaction with insignificant structural change in response to lithiation/delithiation.