The α alloy Ti-2Al-2.5Zr and near α alloy Ti-4Al-2V were hydrogenated to various levels. The morphology, orientation relation （OR）, and habit plane of the hydrides were studied by means of transmission electron mi...The α alloy Ti-2Al-2.5Zr and near α alloy Ti-4Al-2V were hydrogenated to various levels. The morphology, orientation relation （OR）, and habit plane of the hydrides were studied by means of transmission electron microscopy （TEM）. It was found that in the two alloys most of the precipitates are δ-hydrides which have fcc structure with the lattice parameter a = 0.44 nm. Two basic orientation relationships and habit planes of the precipitates are determined. Twin structure was observed in both alloys.展开更多
Microstructures in X80 line pipe were classified by SEM analysis.The experimental results showed that the microstructures in X 80 line pipe steels were complicated consisting of polygonal ferrite,bainite and acicular ...Microstructures in X80 line pipe were classified by SEM analysis.The experimental results showed that the microstructures in X 80 line pipe steels were complicated consisting of polygonal ferrite,bainite and acicular ferrite.Orientation relation within acicular ferrite was investigated systematically by means of EBSD-OIM.The sub-structures were observed maximum in acicular ferrite which gives high strength and high toughness to line pipe steels.The K-S orientation relation was generally observed between acicular ferrite and austenite during phase transformation.The low energy CSL boundary characterized by Σ3 orientation relation according to Brandon criterion appeared with higher probability,which was benefit to improve the mechanical properties of line pipe steels.The orientations or texture of initial austenite grains could be deduced based on the Σ3 orientation relationship of acicular ferrite variants.展开更多
文摘The α alloy Ti-2Al-2.5Zr and near α alloy Ti-4Al-2V were hydrogenated to various levels. The morphology, orientation relation （OR）, and habit plane of the hydrides were studied by means of transmission electron microscopy （TEM）. It was found that in the two alloys most of the precipitates are δ-hydrides which have fcc structure with the lattice parameter a = 0.44 nm. Two basic orientation relationships and habit planes of the precipitates are determined. Twin structure was observed in both alloys.
文摘Microstructures in X80 line pipe were classified by SEM analysis.The experimental results showed that the microstructures in X 80 line pipe steels were complicated consisting of polygonal ferrite,bainite and acicular ferrite.Orientation relation within acicular ferrite was investigated systematically by means of EBSD-OIM.The sub-structures were observed maximum in acicular ferrite which gives high strength and high toughness to line pipe steels.The K-S orientation relation was generally observed between acicular ferrite and austenite during phase transformation.The low energy CSL boundary characterized by Σ3 orientation relation according to Brandon criterion appeared with higher probability,which was benefit to improve the mechanical properties of line pipe steels.The orientations or texture of initial austenite grains could be deduced based on the Σ3 orientation relationship of acicular ferrite variants.