The effect of lanthanum content in the range of 04）.01 1 wt.%, on the inclusion size distribution, microstructure, texture and magnetic properties of three non-oriented electrical steels was studied. After final anne...The effect of lanthanum content in the range of 04）.01 1 wt.%, on the inclusion size distribution, microstructure, texture and magnetic properties of three non-oriented electrical steels was studied. After final annealing, lanthanum effectively inhibited the precipitation of MnS precipitates in steel, the formations of La2O2S and LaS inclusions not only acted as nuclei of AlN precipitates, but also combined with A1203 and formed composite inclusions with larger size. Grain size firstly increased and then decreased with lanthanum content increasing. Steel containing 0.0066 wt.% lanthanum obtained the largest grain size, the strongest { 110} 〈 110〉 texture and the weakest { 112}〈110〉 texture among all the tested steels. Magnetic flux density firstly increased and then decreased, core loss firstly dramatically decreased and then slightly decreased with lanthanum content increasing. Among the three tested steels, steel with 0.0066 wt.% lanthanum demonstrated the best comprehensive magnetic properties mainly through the development of favorable texture and appropriate final grain size.展开更多
Combining with the study of analogue experiments and test analysis, the kinetics of precipitation and growth of AlN and MnS in non-oriented electrical steel produced by the CSP process is calculated. The results show ...Combining with the study of analogue experiments and test analysis, the kinetics of precipitation and growth of AlN and MnS in non-oriented electrical steel produced by the CSP process is calculated. The results show that the precipitate phase particles of AlN and MnS in typical non-oriented electrical steel grades produced by the CSP process have grown to some extent in the soaking stage, but the precipitation contents are less than 20% of the total contents of nitride and sulfide. The precipitate phase particles of AlN and MnS have precipitated almost after the hot rolling process. The precipitation contents are more than 80% of the total contents of nitride and sulfide, but it is very late for the precipitate phase particles to grow at the end of the hot rolling process.展开更多
文摘The effect of lanthanum content in the range of 04）.01 1 wt.%, on the inclusion size distribution, microstructure, texture and magnetic properties of three non-oriented electrical steels was studied. After final annealing, lanthanum effectively inhibited the precipitation of MnS precipitates in steel, the formations of La2O2S and LaS inclusions not only acted as nuclei of AlN precipitates, but also combined with A1203 and formed composite inclusions with larger size. Grain size firstly increased and then decreased with lanthanum content increasing. Steel containing 0.0066 wt.% lanthanum obtained the largest grain size, the strongest { 110} 〈 110〉 texture and the weakest { 112}〈110〉 texture among all the tested steels. Magnetic flux density firstly increased and then decreased, core loss firstly dramatically decreased and then slightly decreased with lanthanum content increasing. Among the three tested steels, steel with 0.0066 wt.% lanthanum demonstrated the best comprehensive magnetic properties mainly through the development of favorable texture and appropriate final grain size.
基金Mega-Projects of Science Research for the 10th Five-Year Plan (2004BA318B)
文摘Combining with the study of analogue experiments and test analysis, the kinetics of precipitation and growth of AlN and MnS in non-oriented electrical steel produced by the CSP process is calculated. The results show that the precipitate phase particles of AlN and MnS in typical non-oriented electrical steel grades produced by the CSP process have grown to some extent in the soaking stage, but the precipitation contents are less than 20% of the total contents of nitride and sulfide. The precipitate phase particles of AlN and MnS have precipitated almost after the hot rolling process. The precipitation contents are more than 80% of the total contents of nitride and sulfide, but it is very late for the precipitate phase particles to grow at the end of the hot rolling process.