By adding mixture of ZrOand carbon, a Zrenhanced composite coating was produced onto an AISI1045 substrate by laser cladding. The microstructure and phase formation, microhardness and wear resistance of the composite ...By adding mixture of ZrOand carbon, a Zrenhanced composite coating was produced onto an AISI1045 substrate by laser cladding. The microstructure and phase formation, microhardness and wear resistance of the composite coating were studied. The experimental results indicate that the composite coating with metallurgical bonding to substrate consists of y-Ni, massive ceramic particles of ZrC,NiZr, NiZr,(Fe,Ni)Cand FeC. The in situ-synthesized ZrC particles are uniformly dispersed in composite coating, which refines the microstructure of composite coating. With different Zr02 and carbon additions, the properties are improved differently. Finally, the fine in situ ZrC particles improve the microhardness of composite coating to HV650, which is nearly 2.7 times that of Ni25 coating. Also, the composite coating has an advantage in wear resistance; it offers better wear resistance when more mixture of ZrOand carbon was added in nickel alloys.展开更多
基金National Natural Science Foundation of China(51701165)China Postdoctoral Science Foundation(2017M623334XB)+1 种基金Natural Science Foundation of Shaanxi Province(2018JM5005)Shaanxi Postdoctoral Science Foundation(2018BSHQYXMZZ36)
基金financially supported by the National Natural Science Foundation of China (No.51275303)
文摘By adding mixture of ZrOand carbon, a Zrenhanced composite coating was produced onto an AISI1045 substrate by laser cladding. The microstructure and phase formation, microhardness and wear resistance of the composite coating were studied. The experimental results indicate that the composite coating with metallurgical bonding to substrate consists of y-Ni, massive ceramic particles of ZrC,NiZr, NiZr,(Fe,Ni)Cand FeC. The in situ-synthesized ZrC particles are uniformly dispersed in composite coating, which refines the microstructure of composite coating. With different Zr02 and carbon additions, the properties are improved differently. Finally, the fine in situ ZrC particles improve the microhardness of composite coating to HV650, which is nearly 2.7 times that of Ni25 coating. Also, the composite coating has an advantage in wear resistance; it offers better wear resistance when more mixture of ZrOand carbon was added in nickel alloys.