The creep rupture properties of a single crystal superalloy were tested at 975℃/255 MPa as a function of the deviation degrees from [001].The misorientation of the specimens away from [001] distributed approximately ...The creep rupture properties of a single crystal superalloy were tested at 975℃/255 MPa as a function of the deviation degrees from [001].The misorientation of the specimens away from [001] distributed approximately along a line between [001]-[011] and [001]-[111] boundaries in the triangle of the stereographic projection.Creep rupture lifetimes of the specimens were not sensitive to the misorientation until the deviation degree exceeded ～30 deg.Two steps of lattice rotation were found in all specimens during creep,first towards the [001]-[111] boundary,and then to [001] or [111] along the boundary.Single slip and strong asymmetric deformation were observed during the first stage of lattice rotation in specimens with large misorientation.The rotation mechanism was associated with the activated slip systems according to the calculated Schmid factors.The impact of lattice rotation on the rupture properties was also discussed.展开更多
在高温状态下,镍基单晶超合金的变形、损伤及断裂分析中,孔洞的长大都起着主要的作用。本研究进行了系列的蠕变、疲劳及热机械疲劳(TMF)试验。对试件的断面进行的 SEM 观察表明,所有的断面都是有许多小断面构成,在断面的中心,至少有一...在高温状态下,镍基单晶超合金的变形、损伤及断裂分析中,孔洞的长大都起着主要的作用。本研究进行了系列的蠕变、疲劳及热机械疲劳(TMF)试验。对试件的断面进行的 SEM 观察表明,所有的断面都是有许多小断面构成,在断面的中心,至少有一个孔洞。孔洞的尺寸与加载的条件相关。使用晶体塑性有限元程序对单胞模型进行分析,模拟孔洞的长大规律。给出了蠕变和弹塑性两种条件下的模拟结果及不同的晶体取向对孔穴长大的影响结果。对孔洞长大的有限元分析有助于对实验结果的理解。展开更多
The oxidation behavior of a novel Ni-based single-crystal 4774DD1 superalloy for industrial gas turbine applications was investigated by the isothermal oxidation at 980℃ and discontinuous oxidation weight gain method...The oxidation behavior of a novel Ni-based single-crystal 4774DD1 superalloy for industrial gas turbine applications was investigated by the isothermal oxidation at 980℃ and discontinuous oxidation weight gain methods.The phase constitution and morphology of surface oxides and the characteristics of the crosssection oxide film were analyzed by XRD,SEM and EDS.Results show that the oxidation kinetics of the 4774DD1 superalloy follows the cubic law,indicating its weak oxidation resistance at this temperature.As the oxidation time increases,the composition of the oxide film evolves as following:One layer consisting of a bottom Al_(2)O_(3)sublayer and an upper(Al_(2)O_(3)+NiO)mixture sublayer after oxidized for 25 h.Then,two layers composed of an outermost small NiO discontinuous grain layer and an internal layer for 75 h.This internal layer is consisted of the bottom Al_(2)O_(3)sublayer,an intermediate narrow CrTaO_(4)sublayer,and an upper(Al_(2)O_(3)+NiO)mixture sublayer.Also two layers comprising an outermost relative continuous NiO layer with large grain size and an internal layer as the oxidation time increases to 125 h.This internal layer is composed of the upper(Al_(2)O_(3)+NiO)mixture sublayer,an intermediate continuous(CrTaO_(4)+NiWO_(4))mixture sublayer,and a bottom Al_(2)O_(3)sublayer.Finally,three layers consisting of an outermost(NiAl2O_(4)+NiCr2O_(4))mixture layer,an intermediate(CrTaO_(4)+NiWO_(4))mixture layer,and a bottom Al_(2)O_(3)layer for 200 h.展开更多
基金sponsored by the National Basic Research Program of China (Grant No.2010CB631201)the National Natural Science Foundation of China (Grant No.50931004)
文摘The creep rupture properties of a single crystal superalloy were tested at 975℃/255 MPa as a function of the deviation degrees from [001].The misorientation of the specimens away from [001] distributed approximately along a line between [001]-[011] and [001]-[111] boundaries in the triangle of the stereographic projection.Creep rupture lifetimes of the specimens were not sensitive to the misorientation until the deviation degree exceeded ～30 deg.Two steps of lattice rotation were found in all specimens during creep,first towards the [001]-[111] boundary,and then to [001] or [111] along the boundary.Single slip and strong asymmetric deformation were observed during the first stage of lattice rotation in specimens with large misorientation.The rotation mechanism was associated with the activated slip systems according to the calculated Schmid factors.The impact of lattice rotation on the rupture properties was also discussed.
基金Natural Science Foundation of China (50005016, 50375124), Natural Science Foundation of Shaanxi Province and China aviation foundation (00B53010, 03B53003) as well as the Yangtze River foundation.
文摘在高温状态下,镍基单晶超合金的变形、损伤及断裂分析中,孔洞的长大都起着主要的作用。本研究进行了系列的蠕变、疲劳及热机械疲劳(TMF)试验。对试件的断面进行的 SEM 观察表明,所有的断面都是有许多小断面构成,在断面的中心,至少有一个孔洞。孔洞的尺寸与加载的条件相关。使用晶体塑性有限元程序对单胞模型进行分析,模拟孔洞的长大规律。给出了蠕变和弹塑性两种条件下的模拟结果及不同的晶体取向对孔穴长大的影响结果。对孔洞长大的有限元分析有助于对实验结果的理解。
基金supported by the fund of State Key Laboratory of Long-life High Temperature Materials(Grant No.DTCC28EE200787)the Natural Science Basic Research Plan in Shaanxi Province of China(Grant No.2022JQ-553)+3 种基金the China Postdoctoral Science Foundation(Grant No.2021M692555)the Excellent Youth Foundation of Shaanxi Province of China(Grant No.2021JC-08)the Beilin district of Xi’an Science and Technology Project(Grant No.GX2123)the support from the Youth Innovation Team of Shaanxi Universities。
文摘The oxidation behavior of a novel Ni-based single-crystal 4774DD1 superalloy for industrial gas turbine applications was investigated by the isothermal oxidation at 980℃ and discontinuous oxidation weight gain methods.The phase constitution and morphology of surface oxides and the characteristics of the crosssection oxide film were analyzed by XRD,SEM and EDS.Results show that the oxidation kinetics of the 4774DD1 superalloy follows the cubic law,indicating its weak oxidation resistance at this temperature.As the oxidation time increases,the composition of the oxide film evolves as following:One layer consisting of a bottom Al_(2)O_(3)sublayer and an upper(Al_(2)O_(3)+NiO)mixture sublayer after oxidized for 25 h.Then,two layers composed of an outermost small NiO discontinuous grain layer and an internal layer for 75 h.This internal layer is consisted of the bottom Al_(2)O_(3)sublayer,an intermediate narrow CrTaO_(4)sublayer,and an upper(Al_(2)O_(3)+NiO)mixture sublayer.Also two layers comprising an outermost relative continuous NiO layer with large grain size and an internal layer as the oxidation time increases to 125 h.This internal layer is composed of the upper(Al_(2)O_(3)+NiO)mixture sublayer,an intermediate continuous(CrTaO_(4)+NiWO_(4))mixture sublayer,and a bottom Al_(2)O_(3)sublayer.Finally,three layers consisting of an outermost(NiAl2O_(4)+NiCr2O_(4))mixture layer,an intermediate(CrTaO_(4)+NiWO_(4))mixture layer,and a bottom Al_(2)O_(3)layer for 200 h.