In this study, a new near-beta titanium alloy, Ti- 4Al-1 Sn-2Zr-5Mo-8V-2.5Cr, was prepared by induction skull melting (ISM) and multidirectional forging. The effect of aging heat treat me rn on microstructure and ten ...In this study, a new near-beta titanium alloy, Ti- 4Al-1 Sn-2Zr-5Mo-8V-2.5Cr, was prepared by induction skull melting (ISM) and multidirectional forging. The effect of aging heat treat me rn on microstructure and ten sile properties of the alloy after solution treatment in the twophase (α+β) region was investigated. The microstructure results show that the globular primary ot phase (cxp) and the needle-like secondary y. phase (ots) are precipitated in the P matrix. The size of ots increases with the increase in aging temperature, while the con tent of ots goes up to a peak value and then decreases. The tensile testing results show that the strength increases first and then decreases with the in crease in temperature. The variation of ductility presents the opposite way compared with the trend of strength level. When aged at 500℃, the alloy exhibits an excellebalance of tensile strength (1529 MPa) and elongation (9.22%). And the relative mechanism of sirengthening and toughening was analyzed and discussed.展开更多
In this work, the microstructure and the corresponding tensile properties of the rolled Ti-7Mo-3Nb-3Cr-3Al(Ti-7333) alloy before and after the thermal treatments were investigated. The results show that a strong α-fi...In this work, the microstructure and the corresponding tensile properties of the rolled Ti-7Mo-3Nb-3Cr-3Al(Ti-7333) alloy before and after the thermal treatments were investigated. The results show that a strong α-fiber texture is developed in the rolled Ti-7333 alloy. The deformed matrix and the texture significantly induce the variant selection of β phase. The high strength of the rolled Ti-7333 alloy is attributed to the <110> texture parallel to the tensile direction and the dispersed α phase within the matrix. After the solution treatment followed by the aging treatment, the texture decreases and the microstructure consists of the equiaxed β grains, the spheroidal α_p phase and various needle-like α variants. Eventually, the alloy could achieve an optimal combination with the strength of about 1450 MPa,the ductility of about 10.5% and a considerable shear strength of about 775 MPa. This balance can be ascribed to the performance of the spheroidal α_p phase and various needle-like α_s variants. The results indicate that the Ti-7333 alloy could be a promising candidate material for the high-strength fastener.展开更多
基金financially supported by the National Natural Science Foundation of China (Nos. 51504163, 51604191 and 51601099)
文摘In this study, a new near-beta titanium alloy, Ti- 4Al-1 Sn-2Zr-5Mo-8V-2.5Cr, was prepared by induction skull melting (ISM) and multidirectional forging. The effect of aging heat treat me rn on microstructure and ten sile properties of the alloy after solution treatment in the twophase (α+β) region was investigated. The microstructure results show that the globular primary ot phase (cxp) and the needle-like secondary y. phase (ots) are precipitated in the P matrix. The size of ots increases with the increase in aging temperature, while the con tent of ots goes up to a peak value and then decreases. The tensile testing results show that the strength increases first and then decreases with the in crease in temperature. The variation of ductility presents the opposite way compared with the trend of strength level. When aged at 500℃, the alloy exhibits an excellebalance of tensile strength (1529 MPa) and elongation (9.22%). And the relative mechanism of sirengthening and toughening was analyzed and discussed.
基金supported by the National Natural Science Foundation of China(Nos.51675435,51875470,52074228)the Research Fund of the State Key Laboratory of Solidification Processing(NPU),China(No.2021-TZ-01,2021-TS-07)。
基金The Project of Introducing Talents of Discipline to Universities(B08040)The International Cooperation Fund of the State Key Laboratory of Solidification Processing in NWPU
基金financially supported by the National Natural Science Foundation of China(Grant No.51711530151)the Major State Research Development Program of China(Nos.2016YFB0701303 and 2016YFB0701305)
文摘In this work, the microstructure and the corresponding tensile properties of the rolled Ti-7Mo-3Nb-3Cr-3Al(Ti-7333) alloy before and after the thermal treatments were investigated. The results show that a strong α-fiber texture is developed in the rolled Ti-7333 alloy. The deformed matrix and the texture significantly induce the variant selection of β phase. The high strength of the rolled Ti-7333 alloy is attributed to the <110> texture parallel to the tensile direction and the dispersed α phase within the matrix. After the solution treatment followed by the aging treatment, the texture decreases and the microstructure consists of the equiaxed β grains, the spheroidal α_p phase and various needle-like α variants. Eventually, the alloy could achieve an optimal combination with the strength of about 1450 MPa,the ductility of about 10.5% and a considerable shear strength of about 775 MPa. This balance can be ascribed to the performance of the spheroidal α_p phase and various needle-like α_s variants. The results indicate that the Ti-7333 alloy could be a promising candidate material for the high-strength fastener.
基金The Project of Introducing Talents of Discipline to Universities("111"Project,B08040)The International Cooperation Fund of the State Key Laboratory of Solidification Processing in NWPU