In this work, the microstructure and the corresponding tensile properties of the rolled Ti-7Mo-3Nb-3Cr-3Al(Ti-7333) alloy before and after the thermal treatments were investigated. The results show that a strong α-fi...In this work, the microstructure and the corresponding tensile properties of the rolled Ti-7Mo-3Nb-3Cr-3Al(Ti-7333) alloy before and after the thermal treatments were investigated. The results show that a strong α-fiber texture is developed in the rolled Ti-7333 alloy. The deformed matrix and the texture significantly induce the variant selection of β phase. The high strength of the rolled Ti-7333 alloy is attributed to the <110> texture parallel to the tensile direction and the dispersed α phase within the matrix. After the solution treatment followed by the aging treatment, the texture decreases and the microstructure consists of the equiaxed β grains, the spheroidal α_p phase and various needle-like α variants. Eventually, the alloy could achieve an optimal combination with the strength of about 1450 MPa,the ductility of about 10.5% and a considerable shear strength of about 775 MPa. This balance can be ascribed to the performance of the spheroidal α_p phase and various needle-like α_s variants. The results indicate that the Ti-7333 alloy could be a promising candidate material for the high-strength fastener.展开更多
基金The Project of Introducing Talents of Discipline to Universities(B08040)The International Cooperation Fund of the State Key Laboratory of Solidification Processing in NWPU
基金financially supported by the National Natural Science Foundation of China(Grant No.51711530151)the Major State Research Development Program of China(Nos.2016YFB0701303 and 2016YFB0701305)
文摘In this work, the microstructure and the corresponding tensile properties of the rolled Ti-7Mo-3Nb-3Cr-3Al(Ti-7333) alloy before and after the thermal treatments were investigated. The results show that a strong α-fiber texture is developed in the rolled Ti-7333 alloy. The deformed matrix and the texture significantly induce the variant selection of β phase. The high strength of the rolled Ti-7333 alloy is attributed to the <110> texture parallel to the tensile direction and the dispersed α phase within the matrix. After the solution treatment followed by the aging treatment, the texture decreases and the microstructure consists of the equiaxed β grains, the spheroidal α_p phase and various needle-like α variants. Eventually, the alloy could achieve an optimal combination with the strength of about 1450 MPa,the ductility of about 10.5% and a considerable shear strength of about 775 MPa. This balance can be ascribed to the performance of the spheroidal α_p phase and various needle-like α_s variants. The results indicate that the Ti-7333 alloy could be a promising candidate material for the high-strength fastener.
基金The Project of Introducing Talents of Discipline to Universities("111"Project,B08040)The International Cooperation Fund of the State Key Laboratory of Solidification Processing in NWPU