Nano-Y2O3 and nano-CeO2 of different weight ratio mixed with deionizing water were doped into MoO2 powder by liquid-solid doping method. The diameter 1.80 and 0.18 mm alloy wires of Mo-0.3Y, Mo-0.3Ce, and Mo-0.15Y-0.1...Nano-Y2O3 and nano-CeO2 of different weight ratio mixed with deionizing water were doped into MoO2 powder by liquid-solid doping method. The diameter 1.80 and 0.18 mm alloy wires of Mo-0.3Y, Mo-0.3Ce, and Mo-0.15Y-0.15Ce were prepared through reduction, iso- static pressing, sintering, and drawing. Tensile properties, second phase microstructure and fracture surface appear- ance of wires were analyzed. The better refining effect for Mo alloy powder can be gotten after two kinds of nano- particle oxide doped into MoO2 than only one doped. Nano-Y2O3 and nano-CeO2 have different influences on sintering process. For nano-CeO2, the constraining effect of grain growth focuses on the initial sintering stage, nano- Y2O3 plays refining grains roles in the later densification stage. Nano-Y2O3 is undistorted and keeps intact in the process of drawing; and nano-CeO2 is elongated and bro- ken into parts in the drawing direction. The strengthening effect of nano-Y2O3 and nano-CeO2 keeps the finer grains and superior tensile properties for Mo-0.15Y-0.15Ce wire.展开更多
Here we report the effects of nano-Y203 addition, sintering atmosphere and time during on the fabrication of PM duplex and ferritic stainless steels composites by dual-drive planetary milling of elemental Fe, Cr and N...Here we report the effects of nano-Y203 addition, sintering atmosphere and time during on the fabrication of PM duplex and ferritic stainless steels composites by dual-drive planetary milling of elemental Fe, Cr and Ni powders followed by conventional pressureless sintering. Yttria-free and yttria-dispersed duplex and ferritic stainless steels are fabricated by conventional sintering at 1000, 1200 and 1400 ℃ temperatures under argon atmosphere. In another set of experiment, yttria-free and yttria-dispersed duplex and ferritic stainless steels are consolidated at 1000 ℃ for l h under nitrogen atmosphere to study the effect of sintering atmosphere. It has been found that densities of duplex and yttria- dispersed duplex stainless steel increase from 71% to 91% and 78% to 94%, respectively, with the increase in sintering temperature. Similarly, hardness value increases from 257 to 567 HV25 in case of duplex, and from 332 to 576 HV25 in yttria-dispersed duplex stainless steel. X-ray diffraction analysis shows the domination of more intense austenite phase than ferrite at higher sintering temperature and also in nitrogen atmosphere. It is also evident that addition of yttria enhances phase transformation from a-Fe to 7-Fe. Duplex and yttria-dispersed duplex stainless steels exhibit the maximum com- pressive yield strength of 360 and 312 MPa, respectively.展开更多
Nano-Y_2O_3:Eu^(3+) powder was prepared by the homogeneous precipitation. With controlling the conditions of the reaction, nano powders with different grain size were obtained. It is found that the blue-shift phenomen...Nano-Y_2O_3:Eu^(3+) powder was prepared by the homogeneous precipitation. With controlling the conditions of the reaction, nano powders with different grain size were obtained. It is found that the blue-shift phenomena exist in the nano-Y2O3:Eu3+ emission spectra excited by X-ray. The wave lengths of the peak (5D0→7F2) are related with the grain size of the powder展开更多
基金financially supported by the National Tungsten and Molybdenum Value-added Utilization Tech-nology Industry Development(No.2012BAE06B02)Shanxi Province Science and Technology Innovation Plan(No.2012KTCQ01-08)
文摘Nano-Y2O3 and nano-CeO2 of different weight ratio mixed with deionizing water were doped into MoO2 powder by liquid-solid doping method. The diameter 1.80 and 0.18 mm alloy wires of Mo-0.3Y, Mo-0.3Ce, and Mo-0.15Y-0.15Ce were prepared through reduction, iso- static pressing, sintering, and drawing. Tensile properties, second phase microstructure and fracture surface appear- ance of wires were analyzed. The better refining effect for Mo alloy powder can be gotten after two kinds of nano- particle oxide doped into MoO2 than only one doped. Nano-Y2O3 and nano-CeO2 have different influences on sintering process. For nano-CeO2, the constraining effect of grain growth focuses on the initial sintering stage, nano- Y2O3 plays refining grains roles in the later densification stage. Nano-Y2O3 is undistorted and keeps intact in the process of drawing; and nano-CeO2 is elongated and bro- ken into parts in the drawing direction. The strengthening effect of nano-Y2O3 and nano-CeO2 keeps the finer grains and superior tensile properties for Mo-0.15Y-0.15Ce wire.
基金Financial support for this work from the Council of Scientific & Industrial Research(CSIR),India(Grant No. 22/561/11/EMR Ⅱ Dated 11.04.2011)
文摘Here we report the effects of nano-Y203 addition, sintering atmosphere and time during on the fabrication of PM duplex and ferritic stainless steels composites by dual-drive planetary milling of elemental Fe, Cr and Ni powders followed by conventional pressureless sintering. Yttria-free and yttria-dispersed duplex and ferritic stainless steels are fabricated by conventional sintering at 1000, 1200 and 1400 ℃ temperatures under argon atmosphere. In another set of experiment, yttria-free and yttria-dispersed duplex and ferritic stainless steels are consolidated at 1000 ℃ for l h under nitrogen atmosphere to study the effect of sintering atmosphere. It has been found that densities of duplex and yttria- dispersed duplex stainless steel increase from 71% to 91% and 78% to 94%, respectively, with the increase in sintering temperature. Similarly, hardness value increases from 257 to 567 HV25 in case of duplex, and from 332 to 576 HV25 in yttria-dispersed duplex stainless steel. X-ray diffraction analysis shows the domination of more intense austenite phase than ferrite at higher sintering temperature and also in nitrogen atmosphere. It is also evident that addition of yttria enhances phase transformation from a-Fe to 7-Fe. Duplex and yttria-dispersed duplex stainless steels exhibit the maximum com- pressive yield strength of 360 and 312 MPa, respectively.
文摘Nano-Y_2O_3:Eu^(3+) powder was prepared by the homogeneous precipitation. With controlling the conditions of the reaction, nano powders with different grain size were obtained. It is found that the blue-shift phenomena exist in the nano-Y2O3:Eu3+ emission spectra excited by X-ray. The wave lengths of the peak (5D0→7F2) are related with the grain size of the powder