Technological parameters of asymmetric cast-rolling under multi-energy field were investigated on horizontal twin roll caster（d400 mm×500 mm）, and their effects on structures and properties of 1050 strips were ...Technological parameters of asymmetric cast-rolling under multi-energy field were investigated on horizontal twin roll caster（d400 mm×500 mm）, and their effects on structures and properties of 1050 strips were analyzed by comparing with traditional cast-rolling. Results show that when length of cast-rolling area is 70 mm, melt temperature of head box is 670 °C, cast rolling speed is 1.3 m/min, exciting current is 10 A, center frequency is（13±1） Hz, ultrasonic power is 200 W and ultrasonic frequency is（20±0.2） kHz, the 1050 strip with the best microstructure can be prepared successfully; its center segregated layer disappears; the average grain size is reduced by about 40%; the crystal grains are distributed evenly; micro segregation decreases obviously; the precipitated phases are distributed along the grain boundaries evenly; and the tensile strength, yield strength, elongation and micro-hardness of cast-rolled strip are improved by 22.6%, 23.66%, 38.75% and 9.90%, respectively.展开更多
基金Project(2014CB046702)supported by National Basic Research Program of China
文摘Technological parameters of asymmetric cast-rolling under multi-energy field were investigated on horizontal twin roll caster（d400 mm×500 mm）, and their effects on structures and properties of 1050 strips were analyzed by comparing with traditional cast-rolling. Results show that when length of cast-rolling area is 70 mm, melt temperature of head box is 670 °C, cast rolling speed is 1.3 m/min, exciting current is 10 A, center frequency is（13±1） Hz, ultrasonic power is 200 W and ultrasonic frequency is（20±0.2） kHz, the 1050 strip with the best microstructure can be prepared successfully; its center segregated layer disappears; the average grain size is reduced by about 40%; the crystal grains are distributed evenly; micro segregation decreases obviously; the precipitated phases are distributed along the grain boundaries evenly; and the tensile strength, yield strength, elongation and micro-hardness of cast-rolled strip are improved by 22.6%, 23.66%, 38.75% and 9.90%, respectively.