In order to study the high temperature flow behaviour of the V modified 2.25Cr-1Mo steel plate to guide the industrial rolling practice, the hot compression tests were carried out at the temperatures from 900 ℃ to 11...In order to study the high temperature flow behaviour of the V modified 2.25Cr-1Mo steel plate to guide the industrial rolling practice, the hot compression tests were carried out at the temperatures from 900 ℃ to 1150 ℃ and the strain rates from 0.01s^-1 to 1 s^-1 on Thermecmastor-Z equipment. Based on the experimental data of the hot compression tests, a kind of Arrhenius-type constitutive equation was developed.The equation can accurately show the relationship between the flow stress and the deformation temperature, the strain and the strain rate. The measured true stress-true strain curves exhibit two kinds of flow stress curves. Moreover, the forming mechanisms of these two types curves were explained by softening, wok hardening theory as well as metallographic and hardness experimental results. The accuracy of the developed Arrheniustype constitutive equation was identified by three kinds of statistic parameters and also by comparison of the measured and predicted data. The reasonable value of the three types of statistic parameters and the good agreement between the experimental and predicted data can confirm the validity of the developed Arrheniustype constitutive equation for V modified 2.25 Cr-1 Mo heat resistant steel plate.展开更多
基金Funded by the New Product Research Program(No.X18ECQ0A00)of Baoshan Iron&Steel Co.Ltd.
文摘In order to study the high temperature flow behaviour of the V modified 2.25Cr-1Mo steel plate to guide the industrial rolling practice, the hot compression tests were carried out at the temperatures from 900 ℃ to 1150 ℃ and the strain rates from 0.01s^-1 to 1 s^-1 on Thermecmastor-Z equipment. Based on the experimental data of the hot compression tests, a kind of Arrhenius-type constitutive equation was developed.The equation can accurately show the relationship between the flow stress and the deformation temperature, the strain and the strain rate. The measured true stress-true strain curves exhibit two kinds of flow stress curves. Moreover, the forming mechanisms of these two types curves were explained by softening, wok hardening theory as well as metallographic and hardness experimental results. The accuracy of the developed Arrheniustype constitutive equation was identified by three kinds of statistic parameters and also by comparison of the measured and predicted data. The reasonable value of the three types of statistic parameters and the good agreement between the experimental and predicted data can confirm the validity of the developed Arrheniustype constitutive equation for V modified 2.25 Cr-1 Mo heat resistant steel plate.