考察了白炭黑种类、羟基硅油用量、含氢硅油用量以及不同乙烯基含量生胶并用对热硫化(HTV)硅橡胶撕裂强度的影响。结果显示,气相法白炭黑的补强效果强于沉淀法白炭黑,且比表面积越大,硅橡胶的撕裂强度越高;随着羟基硅油加入量的增加,硅...考察了白炭黑种类、羟基硅油用量、含氢硅油用量以及不同乙烯基含量生胶并用对热硫化(HTV)硅橡胶撕裂强度的影响。结果显示,气相法白炭黑的补强效果强于沉淀法白炭黑,且比表面积越大,硅橡胶的撕裂强度越高;随着羟基硅油加入量的增加,硅橡胶的撕裂强度先增后趋于稳定;含氢硅油的用量对HTV硅橡胶的撕裂强度基本没有影响;高乙烯基含量生胶和低乙烯基含量生胶并用能显著提高HTV硅橡胶的撕裂强度。较佳配方是:166 g 110-0生胶,4 g 112生胶、80 g QS-102气相法白炭黑、8.5 g羟基硅油、1.0 g含氢硅油、0.5 g乙烯基硅油,此时,HTV硅橡胶的撕裂强度达到21 KN/m。展开更多
The main chemical composition of pyrolysis carbon black of waste tires is C,O,Cu,Zn and so on.The content of ash and fine powder in pyrolysis carbon black is high,and the 300%elongation stress is high.The difference b...The main chemical composition of pyrolysis carbon black of waste tires is C,O,Cu,Zn and so on.The content of ash and fine powder in pyrolysis carbon black is high,and the 300%elongation stress is high.The difference between pyrolysis carbon black and furnace black N326,which is commonly used in rubber,is obvious compared with chemical property.The pyrolysis carbon black was used to replace furnace black N326 in the transition layer of all steel load Radial tire rubber through experimental study.It was found that the compression heat generation and dynamic loss(Tanδ)of the blend rubber before and after aging were obviously reduced,the elongation at break and resilience increased,while the tensile stress and tear strength decreased by 100%and 300%,but the hardness and tensile strength changed little before and after aging.According to the latest raw material price calculation,15 used tire pyrolysis carbon black instead of furnace carbon black N326 used in all steel Radial tire transition layer rubber application,excluding labor costs,electricity and equipment depreciation,a ton of blended rubber saves about$22.86 in production costs.展开更多
文摘考察了白炭黑种类、羟基硅油用量、含氢硅油用量以及不同乙烯基含量生胶并用对热硫化(HTV)硅橡胶撕裂强度的影响。结果显示,气相法白炭黑的补强效果强于沉淀法白炭黑,且比表面积越大,硅橡胶的撕裂强度越高;随着羟基硅油加入量的增加,硅橡胶的撕裂强度先增后趋于稳定;含氢硅油的用量对HTV硅橡胶的撕裂强度基本没有影响;高乙烯基含量生胶和低乙烯基含量生胶并用能显著提高HTV硅橡胶的撕裂强度。较佳配方是:166 g 110-0生胶,4 g 112生胶、80 g QS-102气相法白炭黑、8.5 g羟基硅油、1.0 g含氢硅油、0.5 g乙烯基硅油,此时,HTV硅橡胶的撕裂强度达到21 KN/m。
文摘The main chemical composition of pyrolysis carbon black of waste tires is C,O,Cu,Zn and so on.The content of ash and fine powder in pyrolysis carbon black is high,and the 300%elongation stress is high.The difference between pyrolysis carbon black and furnace black N326,which is commonly used in rubber,is obvious compared with chemical property.The pyrolysis carbon black was used to replace furnace black N326 in the transition layer of all steel load Radial tire rubber through experimental study.It was found that the compression heat generation and dynamic loss(Tanδ)of the blend rubber before and after aging were obviously reduced,the elongation at break and resilience increased,while the tensile stress and tear strength decreased by 100%and 300%,but the hardness and tensile strength changed little before and after aging.According to the latest raw material price calculation,15 used tire pyrolysis carbon black instead of furnace carbon black N326 used in all steel Radial tire transition layer rubber application,excluding labor costs,electricity and equipment depreciation,a ton of blended rubber saves about$22.86 in production costs.