A three-stage molding process involving microcellular injection molding with core retraction and an ＂out-of-mold＂ expansion was developed to manufacture thermoplastic polyurethane into lightweight foams of varying l...A three-stage molding process involving microcellular injection molding with core retraction and an ＂out-of-mold＂ expansion was developed to manufacture thermoplastic polyurethane into lightweight foams of varying local densities, microstructures, and mechanical properties in the same microcellular injection molded part. Two stages of cavity expansion through sequential core retractions and a third expansion in a separate mold at an elevated temperature were carried out. The densities varied from 0.25 to 0.42 g/cm3 （77% to 62% weight reduction）. The mechanical properties varied as well Cyclic com- pressive strengths and hysteresis loss ratios, together with the microstructures, were characterized and reported.展开更多
文摘A three-stage molding process involving microcellular injection molding with core retraction and an ＂out-of-mold＂ expansion was developed to manufacture thermoplastic polyurethane into lightweight foams of varying local densities, microstructures, and mechanical properties in the same microcellular injection molded part. Two stages of cavity expansion through sequential core retractions and a third expansion in a separate mold at an elevated temperature were carried out. The densities varied from 0.25 to 0.42 g/cm3 （77% to 62% weight reduction）. The mechanical properties varied as well Cyclic com- pressive strengths and hysteresis loss ratios, together with the microstructures, were characterized and reported.