Scanning electronic microscopy (SEM) was employed to investigate fractographs of sandstone in mine roof strata under thermal-mechanical coupled effect. Based on the evolution of sandstone surface morphology in the fai...Scanning electronic microscopy (SEM) was employed to investigate fractographs of sandstone in mine roof strata under thermal-mechanical coupled effect. Based on the evolution of sandstone surface morphology in the failure process and frac- tography, the fracture mechanism was studied and classified under meso and mi- cro scales, respectively. The differences between fractographs under different tem- peratures were examined in detail. Under high temperature, fatigue fracture and plastic deformation occurred in the fracture surface. Therefore, the temperature was manifested by these phenomena to influence strongly on micro failure mechanism of sandstone. In addition, the failure mechanism would transit from brittle failure mechanism at low temperature to coupled brittle-ductile failure mechanism at high temperature. The variation of sandstone strength under differ- ent temperature can be attributed to the occurrence of plastic deformation, fatigue fracture, and microcracking. The fatigue striations in the fracture surfaces under high temperature may be interpreted as micro fold. And the coupled effect of tem- perature and tensile stress may be another formation mechanism of micro fold in geology.展开更多
基金Supported by the Open Research Project of State Key Laboratory of Coal Resources and Safe Mining (China University of Mining and Technology) (Grant No. 2007-08)the National Natural Science Foundation of China (Grant Nos. 50674092, 50221402, 50579042, 50620130440, 50639100, 50490272)+1 种基金the National Basic Research Program of China (Grant No. 2002CB412707)the Program for New Century Excellent Talents in University (Grant No. NCET-04-0491)
文摘Scanning electronic microscopy (SEM) was employed to investigate fractographs of sandstone in mine roof strata under thermal-mechanical coupled effect. Based on the evolution of sandstone surface morphology in the failure process and frac- tography, the fracture mechanism was studied and classified under meso and mi- cro scales, respectively. The differences between fractographs under different tem- peratures were examined in detail. Under high temperature, fatigue fracture and plastic deformation occurred in the fracture surface. Therefore, the temperature was manifested by these phenomena to influence strongly on micro failure mechanism of sandstone. In addition, the failure mechanism would transit from brittle failure mechanism at low temperature to coupled brittle-ductile failure mechanism at high temperature. The variation of sandstone strength under differ- ent temperature can be attributed to the occurrence of plastic deformation, fatigue fracture, and microcracking. The fatigue striations in the fracture surfaces under high temperature may be interpreted as micro fold. And the coupled effect of tem- perature and tensile stress may be another formation mechanism of micro fold in geology.