The effect of cerium on ignition temperature of AZ91D magnesium alloy was studie d. By the addition of cerium of 1%, the ignition temperature is raised by 180 ℃ , s o the magnesium alloy added with cerium can be melt...The effect of cerium on ignition temperature of AZ91D magnesium alloy was studie d. By the addition of cerium of 1%, the ignition temperature is raised by 180 ℃ , s o the magnesium alloy added with cerium can be melted in air. The burning temper ature increases with the increasing of cerium. The structure and chemical compos itions of the surface oxide film were investigated by XRD and Auger electron spe ctrometry(AES). The results of XRD indicate that the oxide film of the surface o f ignition-inhibition magnesium alloy can change from loose structure of simple magnesia to compact composite structure consisting of magnesia, cerium oxide, M g17 A112 and aluminum oxide, which has excellent ignition-inhibition effect. AE S depth profile analysis shows that the oxide film can be divided into three lay ers. The outside layer is mainly made up of magnesia, the middle layer, which co nsists of cerium oxide, magnesia, and aluminum oxide, is compound and compact. T hermodynamic analysis indicates that the structure of the surface oxide film is accordant to the change of free energy and high vapor pressure of magnesium.展开更多
文摘The effect of cerium on ignition temperature of AZ91D magnesium alloy was studie d. By the addition of cerium of 1%, the ignition temperature is raised by 180 ℃ , s o the magnesium alloy added with cerium can be melted in air. The burning temper ature increases with the increasing of cerium. The structure and chemical compos itions of the surface oxide film were investigated by XRD and Auger electron spe ctrometry(AES). The results of XRD indicate that the oxide film of the surface o f ignition-inhibition magnesium alloy can change from loose structure of simple magnesia to compact composite structure consisting of magnesia, cerium oxide, M g17 A112 and aluminum oxide, which has excellent ignition-inhibition effect. AE S depth profile analysis shows that the oxide film can be divided into three lay ers. The outside layer is mainly made up of magnesia, the middle layer, which co nsists of cerium oxide, magnesia, and aluminum oxide, is compound and compact. T hermodynamic analysis indicates that the structure of the surface oxide film is accordant to the change of free energy and high vapor pressure of magnesium.