In this work,ultrasonic surface rolling process(USRP)was utilized to produce a gradient structured layer on 7 B50-T7751 aluminum alloy,and the mechanical properties and corrosion fatigue behavior of treated samples we...In this work,ultrasonic surface rolling process(USRP)was utilized to produce a gradient structured layer on 7 B50-T7751 aluminum alloy,and the mechanical properties and corrosion fatigue behavior of treated samples were studied.These results reveal that underwent USRP,a 425~m thick gradient structure and a 700~m deep compressive residual stress field are created,aluminum grain size become fine(~67 nm),and the corrosion rate of treated surface reduces by 60.08%owing to the combined effect of compressive residual stress and surface nanocrystallization.The corrosion fatigue strength is enhanced to 117%of that of 7 B50 Al alloys by means of USRP due to the introduced compressive residual stress,which is considered as the major favorable factor in suppressing the initiation and early propagation of corrosion fatigue cracks.Besides,the gradient structure is an important factor in providing a significant synergistic contribution to the improvement of corrosion fatigue performance.展开更多
基金supported financially by the National Natural Science Foundation of China(No.51771155)the Equipment Pre-research Field Foundation(No.61409220202).
文摘In this work,ultrasonic surface rolling process(USRP)was utilized to produce a gradient structured layer on 7 B50-T7751 aluminum alloy,and the mechanical properties and corrosion fatigue behavior of treated samples were studied.These results reveal that underwent USRP,a 425~m thick gradient structure and a 700~m deep compressive residual stress field are created,aluminum grain size become fine(~67 nm),and the corrosion rate of treated surface reduces by 60.08%owing to the combined effect of compressive residual stress and surface nanocrystallization.The corrosion fatigue strength is enhanced to 117%of that of 7 B50 Al alloys by means of USRP due to the introduced compressive residual stress,which is considered as the major favorable factor in suppressing the initiation and early propagation of corrosion fatigue cracks.Besides,the gradient structure is an important factor in providing a significant synergistic contribution to the improvement of corrosion fatigue performance.