W-type barium ferrites doped with Gd^3＋,Ba1-xGdx（Zn0.3Co0.7）2Fe16O27（x = 0,0.05,0.10,0.15,0.20）,were prepared by a sol-gel method.The effects of Gd^3＋ substitution on their microstructure,electromagnetic propert...W-type barium ferrites doped with Gd^3＋,Ba1-xGdx（Zn0.3Co0.7）2Fe16O27（x = 0,0.05,0.10,0.15,0.20）,were prepared by a sol-gel method.The effects of Gd^3＋ substitution on their microstructure,electromagnetic properties and microwave absorptive behavior were analyzed.The XRD patterns showed the single phase of W-type barium ferrite when x ≤ 0.15.Microwave electromagnetic properties of samples were studied at the frequency range from 2 GHz to 18 GHz using a network analyzer（Agilent 8722ET）.The complex permittivity ε（ε＇,ε＇＇） increased gradually when x ≤ 0.10,but it decreased as x = 0.15.The real permeability（μ＇） decreased with the increase of Gd^3＋ content,while the imaginary permeability（μ＇＇） increased when x ≤ 0.10.All these reasons were discussed using the electromagnetic theory.Furthermore,the ferrite-epoxy compound coating materials with 80 wt.% of Ba0.9Gd0.1（Zn0.3Co0.7）2Fe16O27 were prepared to measure the microwave absorbing properties.The maximum of reflection loss（RL） reached about-27 dB and RL was below-10 dB in the frequency range of 8-18 GHz when the thickness was 1.92 mm.展开更多
In order to study the effect of mixing dye in ferroelectric liquid crystal （FLC） materials, the phase transition temperature and electro-optical properties of azo dye doped FLC samples have been investigated. All th...In order to study the effect of mixing dye in ferroelectric liquid crystal （FLC） materials, the phase transition temperature and electro-optical properties of azo dye doped FLC samples have been investigated. All the properties have been found to be changed drastically. The results have revealed that not only the SmC^＊- SmA^＊ transition temperature decreased markedly by the addition of azo-dye, but also dye-doped FLC had lower threshold voltage and saturation voltage than the pure FLC.展开更多
基金supported by the Pre-research Foundation of CPLA General Equipment Department (NO.9140A××××6401)
文摘W-type barium ferrites doped with Gd^3＋,Ba1-xGdx（Zn0.3Co0.7）2Fe16O27（x = 0,0.05,0.10,0.15,0.20）,were prepared by a sol-gel method.The effects of Gd^3＋ substitution on their microstructure,electromagnetic properties and microwave absorptive behavior were analyzed.The XRD patterns showed the single phase of W-type barium ferrite when x ≤ 0.15.Microwave electromagnetic properties of samples were studied at the frequency range from 2 GHz to 18 GHz using a network analyzer（Agilent 8722ET）.The complex permittivity ε（ε＇,ε＇＇） increased gradually when x ≤ 0.10,but it decreased as x = 0.15.The real permeability（μ＇） decreased with the increase of Gd^3＋ content,while the imaginary permeability（μ＇＇） increased when x ≤ 0.10.All these reasons were discussed using the electromagnetic theory.Furthermore,the ferrite-epoxy compound coating materials with 80 wt.% of Ba0.9Gd0.1（Zn0.3Co0.7）2Fe16O27 were prepared to measure the microwave absorbing properties.The maximum of reflection loss（RL） reached about-27 dB and RL was below-10 dB in the frequency range of 8-18 GHz when the thickness was 1.92 mm.
基金supported by the National"973"Project of China under Grant No.2003CB314704.
文摘In order to study the effect of mixing dye in ferroelectric liquid crystal （FLC） materials, the phase transition temperature and electro-optical properties of azo dye doped FLC samples have been investigated. All the properties have been found to be changed drastically. The results have revealed that not only the SmC^＊- SmA^＊ transition temperature decreased markedly by the addition of azo-dye, but also dye-doped FLC had lower threshold voltage and saturation voltage than the pure FLC.