This study focuses on developing pervious concrete mixtures that have higher compressive strengths than conventional pervious concrete. This study also focuses on producing high strength pervious concrete that is also...This study focuses on developing pervious concrete mixtures that have higher compressive strengths than conventional pervious concrete. This study also focuses on producing high strength pervious concrete that is also made with locally available materials. The study focused on four aspects of pervious concrete to produce high compressive strengths. These parameters were the effect of the coarse aggregate (type and size), the compaction of the test specimens, the effect of the w/c along with superplasticizers, and lastly the effect of silica fume. This study was completed parametrically in order to isolate each variable in order to see its individual affect. Once an optimum performance was obtained from one variable the best performing mixture was used for the next variable testing. This method allowed for the highest performing mixture to be obtained from each of the investigated variables. The results showed that high strength pervious concrete made with local aggregates, without polymers, and without fibers can be produced in the range of 15.44 MPa - 21.63 MPa. A porosity range 19.1% - 32.9% with a percolation rate range of 5.8 mm/s - 1.9 mm/s was also achieved, with a porosity of 19.4% and percolation rate of 2.6 mm/s for the highest performing mixture.展开更多
The main objective of this experimental study is to investigate the behavior of Recycled Reactive Powder Concrete (RRPC) developed from finely dispersed local waste raw materials. In this study, RRPC was developed by ...The main objective of this experimental study is to investigate the behavior of Recycled Reactive Powder Concrete (RRPC) developed from finely dispersed local waste raw materials. In this study, RRPC was developed by utilizing local wastes (finely dispersed waste glass powder, waste fly ash and waste ceramic powder) together with Portland cement, fine sand, admixture, steel fibers and water through full replacement of silica fume as well as quartz powder for sustainable construction practice. In this study, all raw materials for making RRPC were analyzed for X-Ray Fluorescence analysis. For sustainability of local construction works, this study employed standard curing method at ambient temperatures instead of steam curing at higher temperatures. Moreover, hand mixing was used throughout the study. To evaluate the structural performances of the developed RRPC mixes, compressive and flexural strengths of RRPC were investigated experimentally and compared with the control mix. The experimental results indicated that replacing the silica fume fully by finely dispersed local waste glass powder (GP) and fly ash (FA) is a promising approach for local structural construction applications. Accordingly, a mean compressive strength of 62.9 MPa and flexural strength of 8.8 MPa were developed using 50% GP-50% FA at 28thdays standard curing. In this study, 17.56% larger compressive strength and 30.6% flexural strength improvements were observed as compared to the control mix.展开更多
文摘This study focuses on developing pervious concrete mixtures that have higher compressive strengths than conventional pervious concrete. This study also focuses on producing high strength pervious concrete that is also made with locally available materials. The study focused on four aspects of pervious concrete to produce high compressive strengths. These parameters were the effect of the coarse aggregate (type and size), the compaction of the test specimens, the effect of the w/c along with superplasticizers, and lastly the effect of silica fume. This study was completed parametrically in order to isolate each variable in order to see its individual affect. Once an optimum performance was obtained from one variable the best performing mixture was used for the next variable testing. This method allowed for the highest performing mixture to be obtained from each of the investigated variables. The results showed that high strength pervious concrete made with local aggregates, without polymers, and without fibers can be produced in the range of 15.44 MPa - 21.63 MPa. A porosity range 19.1% - 32.9% with a percolation rate range of 5.8 mm/s - 1.9 mm/s was also achieved, with a porosity of 19.4% and percolation rate of 2.6 mm/s for the highest performing mixture.
文摘The main objective of this experimental study is to investigate the behavior of Recycled Reactive Powder Concrete (RRPC) developed from finely dispersed local waste raw materials. In this study, RRPC was developed by utilizing local wastes (finely dispersed waste glass powder, waste fly ash and waste ceramic powder) together with Portland cement, fine sand, admixture, steel fibers and water through full replacement of silica fume as well as quartz powder for sustainable construction practice. In this study, all raw materials for making RRPC were analyzed for X-Ray Fluorescence analysis. For sustainability of local construction works, this study employed standard curing method at ambient temperatures instead of steam curing at higher temperatures. Moreover, hand mixing was used throughout the study. To evaluate the structural performances of the developed RRPC mixes, compressive and flexural strengths of RRPC were investigated experimentally and compared with the control mix. The experimental results indicated that replacing the silica fume fully by finely dispersed local waste glass powder (GP) and fly ash (FA) is a promising approach for local structural construction applications. Accordingly, a mean compressive strength of 62.9 MPa and flexural strength of 8.8 MPa were developed using 50% GP-50% FA at 28thdays standard curing. In this study, 17.56% larger compressive strength and 30.6% flexural strength improvements were observed as compared to the control mix.