The flotation of hemimorphite using the S(Ⅱ)–Pb(Ⅱ)–xanthate process,which includes sulfidization with sodium sulfide,activation by lead cations,and subsequent flotation with xanthate,was investigated.The flotation...The flotation of hemimorphite using the S(Ⅱ)–Pb(Ⅱ)–xanthate process,which includes sulfidization with sodium sulfide,activation by lead cations,and subsequent flotation with xanthate,was investigated.The flotation results indicated that hemimorphite floats when the S(Ⅱ)–Pb(Ⅱ)–xanthate process is used; a maximum recovery of approximately 90% was obtained.Zeta-potential,contact-angle,scanning electron microscopy–energy-dispersive spectrometry(SEM–EDS),and diffuse-reflectance infrared Fourier transform spectroscopy(DRIFTS) measurements were used to characterize the activation products on the hemimorphite surface and their subsequent interaction with sodium butyl xanthate(SBX).The results showed that a Zn S coating formed on the hemimorphite surface after the sample was conditioned in an Na2 S solution.However,the formation of a Zn S coating on the hemimorphite surface did not improve hemimorphite flotation.With the subsequent addition of lead cations,Pb S species formed on the mineral surface.The formation of the Pb S species on the surface of hemimorphite significantly increased the adsorption capacity of SBX,forming lead xanthate(referred to as chemical adsorption) and leading to a substantial improvement in hemimorphite flotation.Our results indicate that the addition of lead cations is a critical step in the successful flotation of hemimorphite using the sulfidization–lead ion activation–xanthate process.展开更多
基金financially supported by the State Key Development Program for Basic Research of China (No.2014CB643402)the Collaborative Innovation Center for Clean and Efficient Utilization of Strategic Metal Mineral Resources of Central South University
文摘The flotation of hemimorphite using the S(Ⅱ)–Pb(Ⅱ)–xanthate process,which includes sulfidization with sodium sulfide,activation by lead cations,and subsequent flotation with xanthate,was investigated.The flotation results indicated that hemimorphite floats when the S(Ⅱ)–Pb(Ⅱ)–xanthate process is used; a maximum recovery of approximately 90% was obtained.Zeta-potential,contact-angle,scanning electron microscopy–energy-dispersive spectrometry(SEM–EDS),and diffuse-reflectance infrared Fourier transform spectroscopy(DRIFTS) measurements were used to characterize the activation products on the hemimorphite surface and their subsequent interaction with sodium butyl xanthate(SBX).The results showed that a Zn S coating formed on the hemimorphite surface after the sample was conditioned in an Na2 S solution.However,the formation of a Zn S coating on the hemimorphite surface did not improve hemimorphite flotation.With the subsequent addition of lead cations,Pb S species formed on the mineral surface.The formation of the Pb S species on the surface of hemimorphite significantly increased the adsorption capacity of SBX,forming lead xanthate(referred to as chemical adsorption) and leading to a substantial improvement in hemimorphite flotation.Our results indicate that the addition of lead cations is a critical step in the successful flotation of hemimorphite using the sulfidization–lead ion activation–xanthate process.
