Fe-2Cu-2Ni-1Mo-0.8C （wt pct） elemental mixed powders were rapidly sintered within 6 min by spark plasma sintering, and the effects of sintering parameters on the densification degree and performance of the assintere...Fe-2Cu-2Ni-1Mo-0.8C （wt pct） elemental mixed powders were rapidly sintered within 6 min by spark plasma sintering, and the effects of sintering parameters on the densification degree and performance of the assintered materials were investigated. Results showed that when a proper combination of pulse electric current and constant electric current was employed for sintering, the density and bend strength of the as-sintered material reached the maxima, being 7.61×10^3 kg/m^3 and 1540 MPa, respectively. Its corresponding fracture morphology was characterized as the mix of ductile, intergranular and cleavage fractures.展开更多
文摘Fe-2Cu-2Ni-1Mo-0.8C （wt pct） elemental mixed powders were rapidly sintered within 6 min by spark plasma sintering, and the effects of sintering parameters on the densification degree and performance of the assintered materials were investigated. Results showed that when a proper combination of pulse electric current and constant electric current was employed for sintering, the density and bend strength of the as-sintered material reached the maxima, being 7.61×10^3 kg/m^3 and 1540 MPa, respectively. Its corresponding fracture morphology was characterized as the mix of ductile, intergranular and cleavage fractures.