Reactive brazing of TiAl-based intermetallics and Ni-based alloy with Ti foil as interlayer was investigated. The interfacial microstructure and shear strength of the joints were studied. According to the experimental...Reactive brazing of TiAl-based intermetallics and Ni-based alloy with Ti foil as interlayer was investigated. The interfacial microstructure and shear strength of the joints were studied. According to the experimental observations, the molten interlayer reacts vigorously with base metals, forming several continuous reaction layers. The typical interfacial microstructure of the joint can be expressed as GH99/（Ni,Cr）ss（γ）/TiNi（β2）＋TiNi2Al（τ4）＋Ti2Ni（δ）/δ＋Ti3Al（α2）＋Al3NiTi2（τ3）/α2＋τ3/TiAl. The maximum shear strength is 258 MPa for the specimen brazed at 1000°C for 10 min. Higher brazing temperature or longer brazing time causes coarsening of the phases in the brazing seam and formation of brittle intermetallic layer, which greatly depresses the shear strength of the joints.展开更多
采用Ag Cu Ti活性钎料对Invar合金和Si3N4陶瓷进行钎焊连接,研究了接头界面组织及其形成机制,分析了钎焊工艺参数对接头界面结构和性能的影响。结果表明,钎焊过程中液态钎料中的活性元素Ti与Si3N4陶瓷发生反应,在陶瓷界面形成致密的Ti N...采用Ag Cu Ti活性钎料对Invar合金和Si3N4陶瓷进行钎焊连接,研究了接头界面组织及其形成机制,分析了钎焊工艺参数对接头界面结构和性能的影响。结果表明,钎焊过程中液态钎料中的活性元素Ti与Si3N4陶瓷发生反应,在陶瓷界面形成致密的Ti N和Ti5Si3反应层;同时,Invar合金向液态钎料中溶解,与活性元素Ti反应生成脆性的Fe2Ti和Ni3Ti化合物。钎焊温度和保温时间影响Si3N4陶瓷界面反应层的厚度以及接头中Fe2Ti和Ni3Ti脆性化合物的形成量和分布,这两方面共同决定着接头的抗剪强度。当钎焊温度为870℃,保温15 min时,接头的平均抗剪强度最大值达到92.8 MPa,此时接头的断裂形式呈现沿Si3N4陶瓷基体和界面反应层的复合断裂模式。展开更多
基金Projects (50975062, 51105107, 51021002) supported by the National Natural Science Foundation of ChinaProjects (QC2011C044) supported by the Natural Science Foundation of Heilongjiang Province,China+1 种基金Project (20112302130005) supported by the Specialized Research Fund for the Doctoral Program of Higher Education,ChinaProject (CUGA4130902510) supported by the China Postdoctoral Science Foundation Funded
文摘Reactive brazing of TiAl-based intermetallics and Ni-based alloy with Ti foil as interlayer was investigated. The interfacial microstructure and shear strength of the joints were studied. According to the experimental observations, the molten interlayer reacts vigorously with base metals, forming several continuous reaction layers. The typical interfacial microstructure of the joint can be expressed as GH99/（Ni,Cr）ss（γ）/TiNi（β2）＋TiNi2Al（τ4）＋Ti2Ni（δ）/δ＋Ti3Al（α2）＋Al3NiTi2（τ3）/α2＋τ3/TiAl. The maximum shear strength is 258 MPa for the specimen brazed at 1000°C for 10 min. Higher brazing temperature or longer brazing time causes coarsening of the phases in the brazing seam and formation of brittle intermetallic layer, which greatly depresses the shear strength of the joints.
基金National Strongof China(TC170A2KN-8)Industrialization Project of Scientific and Technological Achievements in Wuxi City(CYE22C1706)+1 种基金Wuxi Enterprise Academician Workstation(BM2018503)National Natural Science Foundation of China(51801149)。