Introduction Microwave irradiation has been very widely used in heating, cooking and brewing. Several papers which describe the use of domestic microwave ovens to perform rapid organic synthesis in solution have been ...Introduction Microwave irradiation has been very widely used in heating, cooking and brewing. Several papers which describe the use of domestic microwave ovens to perform rapid organic synthesis in solution have been published. The high heating efficiency gives rise to remarkable rate of reaction and dramatic reduction of reaction time. Nevertheless, its application seems to be limited to these procedures because of展开更多
To obtain a novel support with practical value for metallocene catalyst(\%η\%\|C\-5H\-5)TiCl\-3(CpTiCl\-3), poly(styrene\|co\|4\|vinylpyridine)/SiO\-2 nanoscale hybrid material(SrP/SiO\-2) was firstly produced as sup...To obtain a novel support with practical value for metallocene catalyst(\%η\%\|C\-5H\-5)TiCl\-3(CpTiCl\-3), poly(styrene\|co\|4\|vinylpyridine)/SiO\-2 nanoscale hybrid material(SrP/SiO\-2) was firstly produced as support. After pretreatment by methylaluminoxane(MAO), the hybrid materials reacted with CpTiCl\-3. The results from SAXS, SEM and TEM indicated the morphology and structure of organic/inorganic hybrid materials, and the size of inorganic particle in hybrid was nanoscale. The results from IR and XPS showed that there were two possible cationic active species in the hybrid\|supported catalyst, the polymerization results of styrene proved this possibility.展开更多
文摘Introduction Microwave irradiation has been very widely used in heating, cooking and brewing. Several papers which describe the use of domestic microwave ovens to perform rapid organic synthesis in solution have been published. The high heating efficiency gives rise to remarkable rate of reaction and dramatic reduction of reaction time. Nevertheless, its application seems to be limited to these procedures because of
文摘To obtain a novel support with practical value for metallocene catalyst(\%η\%\|C\-5H\-5)TiCl\-3(CpTiCl\-3), poly(styrene\|co\|4\|vinylpyridine)/SiO\-2 nanoscale hybrid material(SrP/SiO\-2) was firstly produced as support. After pretreatment by methylaluminoxane(MAO), the hybrid materials reacted with CpTiCl\-3. The results from SAXS, SEM and TEM indicated the morphology and structure of organic/inorganic hybrid materials, and the size of inorganic particle in hybrid was nanoscale. The results from IR and XPS showed that there were two possible cationic active species in the hybrid\|supported catalyst, the polymerization results of styrene proved this possibility.