The effect of Ti-Al on microstructures and mechanical properties of SiCp/Al MMC joints produced by plasma arc in-situ weld-alloying was investigated, in which argon-nitrogen mixture was used as plasma gases and Ti-Al ...The effect of Ti-Al on microstructures and mechanical properties of SiCp/Al MMC joints produced by plasma arc in-situ weld-alloying was investigated, in which argon-nitrogen mixture was used as plasma gases and Ti-Al alloy as filling composite. The results show that the formation of needle-like harmful phase Al4C3 is effectively prevented in the weld by in-situ weld-alloying/plasma arc welding with Ti-Al alloy sheet filler whose titanium content is more than 20%. The fluidity of molten pool is improved, and stable molten pool is gained for the addition of the Ti-Al alloy. The mechanical properties of welded joint are effectively enhanced by the compact-grain structure and the new reinforced composites such as Al3Ti, TiN, AlN and TiC welded joint. The test results of mechanical property show that the maximum tensile strength of welded joint gained by adding Ti-60Al alloy is up to 235 MPa. The factors influencing the tensile strength were also investigated.展开更多
The influence of Ti-Si-Mg-AI wire on microstructure and mechanical properties of SiCp/A1 metal matrix composite joints produced by plasma arc in-situ weld-alloying was investigated. Argon-nitrogen mixture was used as ...The influence of Ti-Si-Mg-AI wire on microstructure and mechanical properties of SiCp/A1 metal matrix composite joints produced by plasma arc in-situ weld-alloying was investigated. Argon-nitrogen mixture was used as plasma gas and Ti-Si-Mg-A1 flux-cored wires as filled composites. Weldments were submitted to tensile test. Meanwhile, the macro morphology and microstructure of the joints were examined. The result shows that the formation ofneedie-like harmful phase A14C3 is effectively inhibited and the wettability of molten pool is improved by adding Ti-Si-Mg-A1 flux-cored wires. With 15Ti-5Si-5Mg-A1 flux-cored wire as filled composite, the maximum tensile strength of the welded joint is 267 MPa, which is up to 83% that of the matrix composites under annealed condition.展开更多
Additive layer manufacturing （ALM） of aerospace grade titanium components shows great promise in supplying a cost-effective alternative to the conventional production routes. Complex microstructures comprised of col...Additive layer manufacturing （ALM） of aerospace grade titanium components shows great promise in supplying a cost-effective alternative to the conventional production routes. Complex microstructures comprised of columnar remnants of directionally solidifiedβ-grains, with interior inhabited by colonies of finerα-plate structures, were found in samples produced by layered plasma welding of Ti-6Al-4V alloy. The application of in-situ tensile tests combined with rapid offline electron backscatter diffraction （EBSD） analysis provides a powerful tool for understanding and drawing qualitative correlations between microstructural features and deformation characteristics. Non-uniform deformation occurs due to a strong variation in strain response between colonies and across columnar grain boundaries. Prismatic and basal slip systems are active, with the prismatic systems contributing to the most severe deformation through coarse and widely spaced slip lines. Certain colonies behave as microstructural units, with easy slip transmission across the entire colony. Other regions exhibit significant deformation mismatch, with local build-up of strain gradients and stress concentration. The segmentation occurs due to the growth morphology and variant constraints imposed by the columnar solidification structures through orientation relationships, interface alignment and preferred growth directions. Tensile tests perpendicular to columnar structures reveal deformation localization at columnar grain boundaries. In this work connections are made between the theoretical macro- and microstructural growth mechanisms and the observed microstructure of the Ti-6Al-4V alloy, which in turn is linked to observations during in-situ tensile tests.展开更多
基金Project(50475126) supported by the National Natural Science Foundation of ChinaProject(JSAWT-07-04) supported by Key Lab of Jiangsu Province for Advanced Joining Technology, China
文摘The effect of Ti-Al on microstructures and mechanical properties of SiCp/Al MMC joints produced by plasma arc in-situ weld-alloying was investigated, in which argon-nitrogen mixture was used as plasma gases and Ti-Al alloy as filling composite. The results show that the formation of needle-like harmful phase Al4C3 is effectively prevented in the weld by in-situ weld-alloying/plasma arc welding with Ti-Al alloy sheet filler whose titanium content is more than 20%. The fluidity of molten pool is improved, and stable molten pool is gained for the addition of the Ti-Al alloy. The mechanical properties of welded joint are effectively enhanced by the compact-grain structure and the new reinforced composites such as Al3Ti, TiN, AlN and TiC welded joint. The test results of mechanical property show that the maximum tensile strength of welded joint gained by adding Ti-60Al alloy is up to 235 MPa. The factors influencing the tensile strength were also investigated.
基金Project (09003) supported by the Open-Fund Research of State Key Laboratory of Advanced Welding and Joining,Harbin Institute of Technology,ChinaProject (JD0805) supported by the Science and Technology Innovation Team,Jiangsu University,China
文摘The influence of Ti-Si-Mg-AI wire on microstructure and mechanical properties of SiCp/A1 metal matrix composite joints produced by plasma arc in-situ weld-alloying was investigated. Argon-nitrogen mixture was used as plasma gas and Ti-Si-Mg-A1 flux-cored wires as filled composites. Weldments were submitted to tensile test. Meanwhile, the macro morphology and microstructure of the joints were examined. The result shows that the formation ofneedie-like harmful phase A14C3 is effectively inhibited and the wettability of molten pool is improved by adding Ti-Si-Mg-A1 flux-cored wires. With 15Ti-5Si-5Mg-A1 flux-cored wire as filled composite, the maximum tensile strength of the welded joint is 267 MPa, which is up to 83% that of the matrix composites under annealed condition.
文摘Additive layer manufacturing （ALM） of aerospace grade titanium components shows great promise in supplying a cost-effective alternative to the conventional production routes. Complex microstructures comprised of columnar remnants of directionally solidifiedβ-grains, with interior inhabited by colonies of finerα-plate structures, were found in samples produced by layered plasma welding of Ti-6Al-4V alloy. The application of in-situ tensile tests combined with rapid offline electron backscatter diffraction （EBSD） analysis provides a powerful tool for understanding and drawing qualitative correlations between microstructural features and deformation characteristics. Non-uniform deformation occurs due to a strong variation in strain response between colonies and across columnar grain boundaries. Prismatic and basal slip systems are active, with the prismatic systems contributing to the most severe deformation through coarse and widely spaced slip lines. Certain colonies behave as microstructural units, with easy slip transmission across the entire colony. Other regions exhibit significant deformation mismatch, with local build-up of strain gradients and stress concentration. The segmentation occurs due to the growth morphology and variant constraints imposed by the columnar solidification structures through orientation relationships, interface alignment and preferred growth directions. Tensile tests perpendicular to columnar structures reveal deformation localization at columnar grain boundaries. In this work connections are made between the theoretical macro- and microstructural growth mechanisms and the observed microstructure of the Ti-6Al-4V alloy, which in turn is linked to observations during in-situ tensile tests.