In this research, cerium （III） nitrate hexahydrate （Ce（NO3）3·6H2O） and ammonium molybdate tetrahydrate （（NH4）6Mo7O24·4H2O） with Ce3＋-to-Mo6＋ molar ratio of 2：3 were dissolved in 40 ml different ...In this research, cerium （III） nitrate hexahydrate （Ce（NO3）3·6H2O） and ammonium molybdate tetrahydrate （（NH4）6Mo7O24·4H2O） with Ce3＋-to-Mo6＋ molar ratio of 2：3 were dissolved in 40 ml different solvents of deionized （DI） water, polyethylene glycol （PEG） and ethylene glycol （EG） to form different solutions which were followed by adjusting pH from the traditional values to 7.0 and 10.0 with 1 mol.L-1 sodium hydroxide （NaOH）. Subsequently, the solutions were processed by 270-W microwave-hydrother- mal/solvothermal method. Phase, morphology, vibrational modes and photonic properties were fully characterized by X-ray powder diffraction （XRD）, scanning electron microscopy （SEM）, transmission electron microscopy （TEM）, Fourier transform infrared spectroscopy （FTIR）, Raman spectrophotometry, ultraviolet-visible （UV-Vis） absorption and photoluminescence （PL） spectroscopy. The as-synthe-sized products were pure cerium molybdenum oxide （Ce2（MoO4）3） of nanoparticles clustered together as nano- plates in DI water and PEG solvents, and of spindle-like nanoparticles in EG solvent, including the presence of Ce-O-H mode and MoO4 units. The results show that direct energy gaps of the first two have the same value of 2.30 eV, and that of the last is 2.80 eV, including their blue emission at the same wavelength of 488 nm.展开更多
文摘采用超声水热/溶剂热过程使Zn(CH3COO)2,Eu2O3和H2NCSNH2在不同混合溶剂下反应,通过改变表面活性剂的浓度、原料配比、反应温度等变量成功制备了不同形貌的Zn S∶Eu2+样品。采用XRD、SEM对样品结构和形貌情况进行测试表征。结果表明:控制不同的反应条件可以合成包括颗粒、絮状、微球及一维条状等Zn S∶Eu2+形貌,其中乙二胺对形成微球形貌具有明显影响。使用荧光光谱仪分析在乙二胺/水/无水乙醇反应系统中制备的样品,结果表明掺杂3.5mol%Eu2+的样品呈蓝光,且在乙二胺为10 m L时发光最强。
基金financially supported by Thailand's Office of the Higher Education Commission through the National Research University Project for Chiang Mai University
文摘In this research, cerium （III） nitrate hexahydrate （Ce（NO3）3·6H2O） and ammonium molybdate tetrahydrate （（NH4）6Mo7O24·4H2O） with Ce3＋-to-Mo6＋ molar ratio of 2：3 were dissolved in 40 ml different solvents of deionized （DI） water, polyethylene glycol （PEG） and ethylene glycol （EG） to form different solutions which were followed by adjusting pH from the traditional values to 7.0 and 10.0 with 1 mol.L-1 sodium hydroxide （NaOH）. Subsequently, the solutions were processed by 270-W microwave-hydrother- mal/solvothermal method. Phase, morphology, vibrational modes and photonic properties were fully characterized by X-ray powder diffraction （XRD）, scanning electron microscopy （SEM）, transmission electron microscopy （TEM）, Fourier transform infrared spectroscopy （FTIR）, Raman spectrophotometry, ultraviolet-visible （UV-Vis） absorption and photoluminescence （PL） spectroscopy. The as-synthe-sized products were pure cerium molybdenum oxide （Ce2（MoO4）3） of nanoparticles clustered together as nano- plates in DI water and PEG solvents, and of spindle-like nanoparticles in EG solvent, including the presence of Ce-O-H mode and MoO4 units. The results show that direct energy gaps of the first two have the same value of 2.30 eV, and that of the last is 2.80 eV, including their blue emission at the same wavelength of 488 nm.