To study the mechanism by which activated carbon is modified by HNO3 and Mn(NO3)2,the pore texture and surface chemical characteristics of carbon materials in coconut husk activated carbon(AC)were examined via scannin...To study the mechanism by which activated carbon is modified by HNO3 and Mn(NO3)2,the pore texture and surface chemical characteristics of carbon materials in coconut husk activated carbon(AC)were examined via scanning electron microscopy(SEM),Brunauer-Emmett-Teller(BET),X-ray diffraction(XRD),Fourier-transform infrared spectroscopy(FTIR),and X-ray photoelectron spectroscopy(XPS).After being modified by HNO3,the millipore character of AC became deformed,and the character of the adjacent pores remained consolidated.The surface manganites of Mn/AC-1 presented as block and reticular fiber structures,Mn/AC-2's surface manganites presented as petty mammock crystals,and Mn/AC-3's surface manganites were observed as gauze nanosheets that interlace to fill in the pore canal.Nitric acid modification was shown to enlarge surface pores but decrease the specific surface area of AC.Mn loading can be used to construct a new pore structure that,in turn,increased the total specific surface area as well as the specific surface area and the volume of the millipores.Mn/AC-2's pore structure was optimized at a calcination temperature of 500℃and a loading quantity of 5%.The ash content of AC was considerably reduced after modified by HNO3.The active materials for Mn/AC-1 mainly consisted of Mn3O4,with a few Mn2O3 crystals,whereas Mn/AC-2's materials were mainly Mn3O4 and some MnO crystals.Mn/AC-3 was exclusively composed of Mn3O4.HNO3 activation and Mn loading modification did not considerably affect the functional group species present on the catalyst.Modification conditions using the same loading quantities and higher calcination temperatures decreased the number of O—H and N—H bonds while conversely increasing the number of CC and C—O bonds.On the contrary,the use of a higher loading quantity while maintaining the same calcination temperature increased the number of O—H and N—H bonds.A higher loading quantity is beneficial for increasing Mn^4+species.A higher calcination temperature is beneficial for increasing Mn^3+sp展开更多
Modification conditions determine the surface topography and the active material phase composition of a catalyst.To study the influence of modification on a carbon-based sorbent,coconut husk activated carbon(AC)which ...Modification conditions determine the surface topography and the active material phase composition of a catalyst.To study the influence of modification on a carbon-based sorbent,coconut husk activated carbon(AC)which was activated using HNO3 and modified by FeSO4 and Fe(NO3)3 was examined.The pore textures and surface chemical characteristics of the carbon materials were examined by scanning electron microscopy(SEM),Brunner-Emmet-Teller(BET),X-ray diffraction(XRD)and Fourier transform infrared(FTIR)spectroscopy.The surface topography,the pore structure,active materials,and functional groups of AC,AC modificated by HNO3(HNO3/AC for short),and AC modificated by FeSO4 and Fe(NO3)3(Fe/AC for short)were systematically studied.Subsequently,the mechanism of modifying the conditions for the carbon materials was determined.Results showed that the surface micro topography of HNO3/AC became unsystematic and disordered.After modification with FeSO4,the ferriferous oxide was mainly present as a near-spherical crystal.Ferriferous oxides from Fe(NO3)3 modification mainly exhibited a plate shape.HNO3 modification could enlarge the pores but decrease the specific surface area of AC.FeSO4 modification resulted in a new net post structure in the pore canal of AC.Fe(NO3)3 modification caused the pore space structure to develop in the interior,and a higher calcination temperature was useful for ablation.The ash content of the AC was substantially reduced upon HNO3 modification.Upon FeSO4 modification,α-FeOOH,α-Fe2O3 andγ-Fe2O3 coexisted under the condition of a lower concentration of FeSO4 and a lower calcination temperature,and a higher FeSO4 concentration and calcination temperature generated moreα-Fe2O3.The same Fe(NO3)3 modification and a higher calcination temperature were beneficial to the minor chipping formation ofγ-Fe2O3.A higher Fe(NO3)3 loading produced a lower graphitization degree.HNO3 modification formed various new oxygen-containing functional groups and few nitrogen-containing groups.Based on the cover,FeSO4 and 展开更多
Fe-loaded activated carbon(AC)has high surface acidity and more active sites,while manganese-loaded AC has high oxygen content.Coconut husk AC modified by Fe-Mn was studied with the aim of revealing the modification m...Fe-loaded activated carbon(AC)has high surface acidity and more active sites,while manganese-loaded AC has high oxygen content.Coconut husk AC modified by Fe-Mn was studied with the aim of revealing the modification mechanism.First,HNO_(3)AC was prepared using the nitric acid immersion method.Second,Fe-Mn/AC was prepared using the Fe(N0_(3))_(3)and Mn(N0_(3))_(2)sequential immersion.The effects of HNO_(3),Fe(N0_(3))_(3),and Mn(N0_(3))_(2)on the pore texture and surface chemical characteristics of carbon materials were examined by scanning electron microscopy,Brunauer-Emmett-Teller(BET)analysis,X-ray diffraction and Fourier-transform infrared spectroscopy.The surface topography,pore structure,active material,and functional groups of AC,HNO_(3)/AC,and Fe-Mn/AC were systematically studied.The following results were obtained.The surface of HNO_(3)AC has more ditches and air voids;the micropores of HNO_(3)AC are deformed and flattened compared to those of AC.The surface of Fe-Mn/AC exhibits an accumulation phenomenon.MnFe_(2)O_(4)and FeMn_(2)O_(4)formed more pore structures.AC and HNO_(3)AC have numerous micropores.The higher loading quantity of Fe-Mn results in bigger specific surface.The active components of Fe-Mn/AC-1,Fe-Mn/AC-2,Fe-Mn/AC-3,and Fe-Mn/AC-4 are MnFe_(2)O_(4),MnO_(0.43)Fe_(2.57)O_(4),Mn_(3)O_(4),and ot-Fe_(2)O_(3)>respectively.The surface functional groups of AC and HNO_(3)AC are oxygen-containing functional groups.The effect of Fe-Mn modifying conditions on functional group species is rare;however,Fe/AC has more oxygen-containing functional groups.These research findings can aid in the desulfurization and denitrification of the Fe-Mn/AC catalyst.展开更多
采用双外推法对稻壳催化热解进行了动力学分析。结果表明,50%CuO+50%Fe_2O_3和50%CuO 50%Fe_2O_3加入促进了稻壳热解,三种条件下活化能分别为87.96,63.6和50.74 k J/mol,催化剂的加入使活化能分别降低了27.68%和42.31%。催化剂的加入没...采用双外推法对稻壳催化热解进行了动力学分析。结果表明,50%CuO+50%Fe_2O_3和50%CuO 50%Fe_2O_3加入促进了稻壳热解,三种条件下活化能分别为87.96,63.6和50.74 k J/mol,催化剂的加入使活化能分别降低了27.68%和42.31%。催化剂的加入没有改变反应机理函数,始终保持为二级化学反应模型[(1-α)^(-1)-1]。展开更多
基金The Science and Technology Plan of Yunnan Science and Technology Department(No.2019FB077,202001AT070029)the Open Fund of Key Laboratory of Ministry of Education for Metallurgical Emission Reduction and Comprehensive Utilization of Resources(No.JKF19-08)the Industrialization Cultivation Project of Scientific Research Fund of Yunnan Provincial Department of Education(No.2016CYH07).
文摘To study the mechanism by which activated carbon is modified by HNO3 and Mn(NO3)2,the pore texture and surface chemical characteristics of carbon materials in coconut husk activated carbon(AC)were examined via scanning electron microscopy(SEM),Brunauer-Emmett-Teller(BET),X-ray diffraction(XRD),Fourier-transform infrared spectroscopy(FTIR),and X-ray photoelectron spectroscopy(XPS).After being modified by HNO3,the millipore character of AC became deformed,and the character of the adjacent pores remained consolidated.The surface manganites of Mn/AC-1 presented as block and reticular fiber structures,Mn/AC-2's surface manganites presented as petty mammock crystals,and Mn/AC-3's surface manganites were observed as gauze nanosheets that interlace to fill in the pore canal.Nitric acid modification was shown to enlarge surface pores but decrease the specific surface area of AC.Mn loading can be used to construct a new pore structure that,in turn,increased the total specific surface area as well as the specific surface area and the volume of the millipores.Mn/AC-2's pore structure was optimized at a calcination temperature of 500℃and a loading quantity of 5%.The ash content of AC was considerably reduced after modified by HNO3.The active materials for Mn/AC-1 mainly consisted of Mn3O4,with a few Mn2O3 crystals,whereas Mn/AC-2's materials were mainly Mn3O4 and some MnO crystals.Mn/AC-3 was exclusively composed of Mn3O4.HNO3 activation and Mn loading modification did not considerably affect the functional group species present on the catalyst.Modification conditions using the same loading quantities and higher calcination temperatures decreased the number of O—H and N—H bonds while conversely increasing the number of CC and C—O bonds.On the contrary,the use of a higher loading quantity while maintaining the same calcination temperature increased the number of O—H and N—H bonds.A higher loading quantity is beneficial for increasing Mn^4+species.A higher calcination temperature is beneficial for increasing Mn^3+sp
基金General Project of Science and Technology Plan of Yunnan Science and Technology Department,China(No.2019FB077)Open Fund of Key Laboratory of Ministry of Education for Metallurgical Emission Reduction and Comprehensive Utilization of Resources,China(No.JKF19-08)。
文摘Modification conditions determine the surface topography and the active material phase composition of a catalyst.To study the influence of modification on a carbon-based sorbent,coconut husk activated carbon(AC)which was activated using HNO3 and modified by FeSO4 and Fe(NO3)3 was examined.The pore textures and surface chemical characteristics of the carbon materials were examined by scanning electron microscopy(SEM),Brunner-Emmet-Teller(BET),X-ray diffraction(XRD)and Fourier transform infrared(FTIR)spectroscopy.The surface topography,the pore structure,active materials,and functional groups of AC,AC modificated by HNO3(HNO3/AC for short),and AC modificated by FeSO4 and Fe(NO3)3(Fe/AC for short)were systematically studied.Subsequently,the mechanism of modifying the conditions for the carbon materials was determined.Results showed that the surface micro topography of HNO3/AC became unsystematic and disordered.After modification with FeSO4,the ferriferous oxide was mainly present as a near-spherical crystal.Ferriferous oxides from Fe(NO3)3 modification mainly exhibited a plate shape.HNO3 modification could enlarge the pores but decrease the specific surface area of AC.FeSO4 modification resulted in a new net post structure in the pore canal of AC.Fe(NO3)3 modification caused the pore space structure to develop in the interior,and a higher calcination temperature was useful for ablation.The ash content of the AC was substantially reduced upon HNO3 modification.Upon FeSO4 modification,α-FeOOH,α-Fe2O3 andγ-Fe2O3 coexisted under the condition of a lower concentration of FeSO4 and a lower calcination temperature,and a higher FeSO4 concentration and calcination temperature generated moreα-Fe2O3.The same Fe(NO3)3 modification and a higher calcination temperature were beneficial to the minor chipping formation ofγ-Fe2O3.A higher Fe(NO3)3 loading produced a lower graphitization degree.HNO3 modification formed various new oxygen-containing functional groups and few nitrogen-containing groups.Based on the cover,FeSO4 and
基金The authors are grateful for Open Fund of Key Laboratory of Ministry of Education for metallurgical emission reduction and comprehensive utilization of resources(JKF19-08),General Project of Science and Technology Plan of Yunnan Science and Technology Department(2019FB077 and 202001AT070029)the Open Fund of Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education(Grant No.FMRUlab-20-4).
文摘Fe-loaded activated carbon(AC)has high surface acidity and more active sites,while manganese-loaded AC has high oxygen content.Coconut husk AC modified by Fe-Mn was studied with the aim of revealing the modification mechanism.First,HNO_(3)AC was prepared using the nitric acid immersion method.Second,Fe-Mn/AC was prepared using the Fe(N0_(3))_(3)and Mn(N0_(3))_(2)sequential immersion.The effects of HNO_(3),Fe(N0_(3))_(3),and Mn(N0_(3))_(2)on the pore texture and surface chemical characteristics of carbon materials were examined by scanning electron microscopy,Brunauer-Emmett-Teller(BET)analysis,X-ray diffraction and Fourier-transform infrared spectroscopy.The surface topography,pore structure,active material,and functional groups of AC,HNO_(3)/AC,and Fe-Mn/AC were systematically studied.The following results were obtained.The surface of HNO_(3)AC has more ditches and air voids;the micropores of HNO_(3)AC are deformed and flattened compared to those of AC.The surface of Fe-Mn/AC exhibits an accumulation phenomenon.MnFe_(2)O_(4)and FeMn_(2)O_(4)formed more pore structures.AC and HNO_(3)AC have numerous micropores.The higher loading quantity of Fe-Mn results in bigger specific surface.The active components of Fe-Mn/AC-1,Fe-Mn/AC-2,Fe-Mn/AC-3,and Fe-Mn/AC-4 are MnFe_(2)O_(4),MnO_(0.43)Fe_(2.57)O_(4),Mn_(3)O_(4),and ot-Fe_(2)O_(3)>respectively.The surface functional groups of AC and HNO_(3)AC are oxygen-containing functional groups.The effect of Fe-Mn modifying conditions on functional group species is rare;however,Fe/AC has more oxygen-containing functional groups.These research findings can aid in the desulfurization and denitrification of the Fe-Mn/AC catalyst.
文摘采用双外推法对稻壳催化热解进行了动力学分析。结果表明,50%CuO+50%Fe_2O_3和50%CuO 50%Fe_2O_3加入促进了稻壳热解,三种条件下活化能分别为87.96,63.6和50.74 k J/mol,催化剂的加入使活化能分别降低了27.68%和42.31%。催化剂的加入没有改变反应机理函数,始终保持为二级化学反应模型[(1-α)^(-1)-1]。