The alloying design of cast hot-forging die steels was analyzed. The relationship of the life of cast hot-forging dies with the failure patterns was studied. The thermal wear resistance was believed to be the key prop...The alloying design of cast hot-forging die steels was analyzed. The relationship of the life of cast hot-forging dies with the failure patterns was studied. The thermal wear resistance was believed to be the key property for the alloying design of cast hot-forging die steels. The alloying design parameters were selected and optimized for the cast hot-forging die steel with high wear resistance. The wear resistance of the optimized cast die steel was evaluated in comparison with commercial H13 steels and 3Cr2WSV steel. In the new cast hot-forging die steel, VC is predominant carbide with Cr and Mo as the main solution elements in α-Fe. It is found that the cast die steel has significantly lower wear rate than normal H13 steel and 3Cr2W8V steel, almost the same as that of high purity H13 steel. The high wear resistance of the new cast hot-forging die steel can be attributed to its reasonable alloying design and nonsensibility to the detrimental function of S and P.展开更多
The effect of main alloying elements on thermal wear of cast hot-forging die steels was studied. The wear mechanism was discussed. The results show that alloying elements have significant influences on the thermal wea...The effect of main alloying elements on thermal wear of cast hot-forging die steels was studied. The wear mechanism was discussed. The results show that alloying elements have significant influences on the thermal wear of cast hot-forging die steels. The wear rates decrease with an increase in chromium content from 3% to 4% and molybdenum content from 2% to 3%, respectively. With further increase of chromium and molybdenum contents, chromium slightly reduces the wear resistance and molybdenum severely deteriorates the wear resistance with high wear rate. Lower vanadium/carbon ratio （1.5-2.5） leads to a lower wear resistance with higher wear rate. With an increase in vanadium/carbon ratio, the wear resistance of the cast steel substantially increases. When vanadium/carbon ratio is 3, the wear rate reaches the lowest value. The predominant mechanism of thermal wear of cast hot-forging die steels are oxidation wear and fatigue delamination. The Fe2O3 and Fe3O4 or lumps of brittle wear debris are formed on the wear surface.展开更多
The cracking morphology of the hardfacing specimens taken from steel 5CrNiMo was observed. Meanwhile, the residual stress fields were measured and simulated. Based on experiment mentioned above, the improved structure...The cracking morphology of the hardfacing specimens taken from steel 5CrNiMo was observed. Meanwhile, the residual stress fields were measured and simulated. Based on experiment mentioned above, the improved structure and modified inclusion in hardfacing metal with rare earth （RE） oxide were analyzed. The results show that, the hardfacing crack is initiated from the coarse dendritic crystal grain boundary, inclusions and coarse austenite grain boundary in the HAZ and propagated by the residual stress existing in the center of the hardfacing metal and HAZ. The primary columnar grain structure can be refined by adding RE oxide in the coating of the electrode. The inclusion in the hardfacing metal can be modified as well. Meanwhile, if the martensite transformation temperature is decreased, the largest value of the residual tensile stress in the dangerous region can be reduced.展开更多
Thermal wear of cast hot-forging die steel modified by rare earths（RE） was studied and compared with commercially used die steels. The function of RE and the mechanism of thermal wear of cast steel modified by RE we...Thermal wear of cast hot-forging die steel modified by rare earths（RE） was studied and compared with commercially used die steels. The function of RE and the mechanism of thermal wear of cast steel modified by RE were discussed. The results showed that with increasing content of RE, the wear rate of cast steel reduced at first and then increased. By adding 0.05% （mass fraction） RE, the cast hot-forging die steel with optimum thermal wear resistance was obtained, which was better than that of H13 and 3Cr2WSV. The large amount of coarse inclusions, （RE）2O2S, resulted from excessive RE, which obviously deteriorated thermal wear resistance. The mechanism of thermal wear of the modified cast die steel is oxidation wear and oxide fatigue delamination. The wear debris are lumps of Fe2O3 and Fe3O4.展开更多
基金Item Sponsored by Hi-Tech Research and Development Program of China (2002AA331180)State Key Laboratory of Materials Modification by Laser,Ion and Electron Beams(0708)
文摘The alloying design of cast hot-forging die steels was analyzed. The relationship of the life of cast hot-forging dies with the failure patterns was studied. The thermal wear resistance was believed to be the key property for the alloying design of cast hot-forging die steels. The alloying design parameters were selected and optimized for the cast hot-forging die steel with high wear resistance. The wear resistance of the optimized cast die steel was evaluated in comparison with commercial H13 steels and 3Cr2WSV steel. In the new cast hot-forging die steel, VC is predominant carbide with Cr and Mo as the main solution elements in α-Fe. It is found that the cast die steel has significantly lower wear rate than normal H13 steel and 3Cr2W8V steel, almost the same as that of high purity H13 steel. The high wear resistance of the new cast hot-forging die steel can be attributed to its reasonable alloying design and nonsensibility to the detrimental function of S and P.
基金Item Sponsored by Early-Term Key Technology of Industrialization and Whole Set Equipment From Plan Committee of China(1999317) ,863 Project of China (2002AA331180) ,and Project of Key Lab of Universities in Jiangsu Province of China(Kjsmcx04004)
文摘The effect of main alloying elements on thermal wear of cast hot-forging die steels was studied. The wear mechanism was discussed. The results show that alloying elements have significant influences on the thermal wear of cast hot-forging die steels. The wear rates decrease with an increase in chromium content from 3% to 4% and molybdenum content from 2% to 3%, respectively. With further increase of chromium and molybdenum contents, chromium slightly reduces the wear resistance and molybdenum severely deteriorates the wear resistance with high wear rate. Lower vanadium/carbon ratio （1.5-2.5） leads to a lower wear resistance with higher wear rate. With an increase in vanadium/carbon ratio, the wear resistance of the cast steel substantially increases. When vanadium/carbon ratio is 3, the wear rate reaches the lowest value. The predominant mechanism of thermal wear of cast hot-forging die steels are oxidation wear and fatigue delamination. The Fe2O3 and Fe3O4 or lumps of brittle wear debris are formed on the wear surface.
基金Project supported by Key Project of Science and Technology of Hebei Province (04212201D) and Research Foundationfor theReturned Overseas Chinese Scholars of State Education Ministry
文摘The cracking morphology of the hardfacing specimens taken from steel 5CrNiMo was observed. Meanwhile, the residual stress fields were measured and simulated. Based on experiment mentioned above, the improved structure and modified inclusion in hardfacing metal with rare earth （RE） oxide were analyzed. The results show that, the hardfacing crack is initiated from the coarse dendritic crystal grain boundary, inclusions and coarse austenite grain boundary in the HAZ and propagated by the residual stress existing in the center of the hardfacing metal and HAZ. The primary columnar grain structure can be refined by adding RE oxide in the coating of the electrode. The inclusion in the hardfacing metal can be modified as well. Meanwhile, if the martensite transformation temperature is decreased, the largest value of the residual tensile stress in the dangerous region can be reduced.
基金Project supported by the Itemof Early-TermKey Technology of Industrialization ,Plan Committee of China (1999317) 863project of China (2002AA331180)
文摘Thermal wear of cast hot-forging die steel modified by rare earths（RE） was studied and compared with commercially used die steels. The function of RE and the mechanism of thermal wear of cast steel modified by RE were discussed. The results showed that with increasing content of RE, the wear rate of cast steel reduced at first and then increased. By adding 0.05% （mass fraction） RE, the cast hot-forging die steel with optimum thermal wear resistance was obtained, which was better than that of H13 and 3Cr2WSV. The large amount of coarse inclusions, （RE）2O2S, resulted from excessive RE, which obviously deteriorated thermal wear resistance. The mechanism of thermal wear of the modified cast die steel is oxidation wear and oxide fatigue delamination. The wear debris are lumps of Fe2O3 and Fe3O4.