The effects of rare earths(RE)-Mg-Ti compound modification on the structures and properties of high-carbon high speed steel(HSS) were researched.The impact toughness(α_k),the fracture toughness(K_(1c))and threshold o...The effects of rare earths(RE)-Mg-Ti compound modification on the structures and properties of high-carbon high speed steel(HSS) were researched.The impact toughness(α_k),the fracture toughness(K_(1c))and threshold of fatigue crack growth(ΔK_(th))are tested.The thermal fatigue test is done on a self-straining thermal fatigue tester,the wear test is done on a high temperature wear test machine.The results show that the matrix can be refined by the RE-Mg-Ti compound modification,the eutectic carbides are inclined to spheroidicize and are distributed evenly,the morphology and distribution of eutectic carbides are improved by appropriate RE-Mg-Ti complex modification.After RE-Mg-Ti compound modification,a little effects can be found on the strength,hardness and red hardness,but the fracture toughness(K_(1c)) and threshold of fatigue crack growth(△K_(th)) are improved in the meantime,the impact toughness (α_k) is increased by over one time,and the resistance to thermal fatigue and wear resistance at an elevated temperature are remarkably improved.展开更多
文摘The effects of rare earths(RE)-Mg-Ti compound modification on the structures and properties of high-carbon high speed steel(HSS) were researched.The impact toughness(α_k),the fracture toughness(K_(1c))and threshold of fatigue crack growth(ΔK_(th))are tested.The thermal fatigue test is done on a self-straining thermal fatigue tester,the wear test is done on a high temperature wear test machine.The results show that the matrix can be refined by the RE-Mg-Ti compound modification,the eutectic carbides are inclined to spheroidicize and are distributed evenly,the morphology and distribution of eutectic carbides are improved by appropriate RE-Mg-Ti complex modification.After RE-Mg-Ti compound modification,a little effects can be found on the strength,hardness and red hardness,but the fracture toughness(K_(1c)) and threshold of fatigue crack growth(△K_(th)) are improved in the meantime,the impact toughness (α_k) is increased by over one time,and the resistance to thermal fatigue and wear resistance at an elevated temperature are remarkably improved.