采用扫描电子显微镜(scanning electron microscopy,SEM)、维氏硬度仪和X射线衍射仪(X-ray diffraction,XRD)分别观测了不同磨削条件下淬硬轴承钢GCr15磨削表层的微观组织、显微硬度和残余应力,对淬硬轴承钢磨削变质层进行了系统的实验...采用扫描电子显微镜(scanning electron microscopy,SEM)、维氏硬度仪和X射线衍射仪(X-ray diffraction,XRD)分别观测了不同磨削条件下淬硬轴承钢GCr15磨削表层的微观组织、显微硬度和残余应力,对淬硬轴承钢磨削变质层进行了系统的实验研究.研究发现,磨削表层由表及里依次是白层、暗层和基体组织,暗层与白层的厚度之比在1.6～3.2之间变动.白层由致密的细晶马氏体、碳化物和残余奥氏体组成,而暗层由不同的回火组织构成,白层主要是磨削热和材料的强烈塑性变形共同作用的结果.白层硬度最大值达到983 HV,比基体组织高,而暗层硬度值仅为512 HV,较基体组织低.白层表面存在大小为612.24 MPa的残余拉应力,且随着白层的增厚而增大,而暗层则呈现出残余压应力.当白层较厚时,白层内会出现微裂纹,其中以贯穿白层的中位裂纹以及白层外侧和白层/暗层过渡区的横向裂纹居多.展开更多
A study was undertaken to investigate the performan ce of PCBN tool in the finish turning GCr15 bearing steel with different hardness between 30～64 HRC. The natural thermocouple was used to measure the cutting tem p ...A study was undertaken to investigate the performan ce of PCBN tool in the finish turning GCr15 bearing steel with different hardness between 30～64 HRC. The natural thermocouple was used to measure the cutting tem p erature, tool life and cutting temperature were investigated and compared. The m aterial can be heated by this instrument which using low voltage and high elec trical current, while PCBN can’t be heated by electrifying directly, so the ke ntanium layer coating over the PCBN is heated, so the PCBN is heated and its th ermoelectric property is got by this method. [TPP129,+60mm88mm,Y,PZ#] Fig.1 Effect of cutting depth and workpiec hardness on. the cutting temperatureThe objective was to determine the influence of the workpiece hardness on change s in cutting temperature and tool wear characterize. It can be found from Fig.1 that the cutting temperature show an increasing tendency with the improvement of workpiece hardness within the cutting speed scope when the workpiece hardness i s under HRC50. And on the other hand, it is found that the cutting temperature s how the downtrend with the improvement of workpiece hardness when the workpiece hardness is over HRC50. According to experimental results, the critical hard ness when turning hardened GCr15 bearing steel with PCBN tool is about HRC50. Th e wear causes of PCBN tool have been found out through taking photos on the micr o-shape of PCBN poly-laminate initial surface as well as face and flank of wea r tool and analysis on chemical elements. It is discovered that the PCBN tools a re not suitable for cutting the workpiece at nearly critical hardness, because n ear the critical hardness, PCBN wear at the highest speed. For researching the w ear rule of PCBN tool, the tool wear experiments have been carried on by using b earing steel GCr15 at hardness HRC40 and HRC60 with changing cutting speed. The indexes of tool life equations is gained under two kinds of conditions w hich are bigger than 0.6, so the effects of cutting speed on the PCBN tool are m u展开更多
White layers in hard turned surfaces were identified and measured as a function ot turning parameters based on the Taguchi method. It reveals that white layers generate on the machine surface in the absence of tool fl...White layers in hard turned surfaces were identified and measured as a function ot turning parameters based on the Taguchi method. It reveals that white layers generate on the machine surface in the absence of tool flank wear, and white layer depth varies with the different combinations of hard turning parameters. Turning speed has the most important impact on white layer depth, feed rate follows, and cutting depth at last. The white layer generation consequently suggests a strong couple relation to the heat generation and thermal process of hard turning operation. White layer disappears under an optimal combination of turning parameters by Taguchi method. It suggests that a superior surface integrity without white layer is feasible under some selected combinations of turning parameters by a sharp CBN cutting tool.展开更多
文摘A study was undertaken to investigate the performan ce of PCBN tool in the finish turning GCr15 bearing steel with different hardness between 30～64 HRC. The natural thermocouple was used to measure the cutting tem p erature, tool life and cutting temperature were investigated and compared. The m aterial can be heated by this instrument which using low voltage and high elec trical current, while PCBN can’t be heated by electrifying directly, so the ke ntanium layer coating over the PCBN is heated, so the PCBN is heated and its th ermoelectric property is got by this method. [TPP129,+60mm88mm,Y,PZ#] Fig.1 Effect of cutting depth and workpiec hardness on. the cutting temperatureThe objective was to determine the influence of the workpiece hardness on change s in cutting temperature and tool wear characterize. It can be found from Fig.1 that the cutting temperature show an increasing tendency with the improvement of workpiece hardness within the cutting speed scope when the workpiece hardness i s under HRC50. And on the other hand, it is found that the cutting temperature s how the downtrend with the improvement of workpiece hardness when the workpiece hardness is over HRC50. According to experimental results, the critical hard ness when turning hardened GCr15 bearing steel with PCBN tool is about HRC50. Th e wear causes of PCBN tool have been found out through taking photos on the micr o-shape of PCBN poly-laminate initial surface as well as face and flank of wea r tool and analysis on chemical elements. It is discovered that the PCBN tools a re not suitable for cutting the workpiece at nearly critical hardness, because n ear the critical hardness, PCBN wear at the highest speed. For researching the w ear rule of PCBN tool, the tool wear experiments have been carried on by using b earing steel GCr15 at hardness HRC40 and HRC60 with changing cutting speed. The indexes of tool life equations is gained under two kinds of conditions w hich are bigger than 0.6, so the effects of cutting speed on the PCBN tool are m u
基金The Ministry of Education of China"985"of International cooperation project"Clean Manufactur-ing Technology"
文摘White layers in hard turned surfaces were identified and measured as a function ot turning parameters based on the Taguchi method. It reveals that white layers generate on the machine surface in the absence of tool flank wear, and white layer depth varies with the different combinations of hard turning parameters. Turning speed has the most important impact on white layer depth, feed rate follows, and cutting depth at last. The white layer generation consequently suggests a strong couple relation to the heat generation and thermal process of hard turning operation. White layer disappears under an optimal combination of turning parameters by Taguchi method. It suggests that a superior surface integrity without white layer is feasible under some selected combinations of turning parameters by a sharp CBN cutting tool.