The replacement metal gate（RMG） defectivity performance control is very challenging in high-k metal gate（HKMG） chemical mechanical polishing（CMP）. In this study, three major defect types, including fall-on parti...The replacement metal gate（RMG） defectivity performance control is very challenging in high-k metal gate（HKMG） chemical mechanical polishing（CMP）. In this study, three major defect types, including fall-on particles, micro-scratch and corrosion have been investigated. The research studied the effects of polishing pad,pressure, rotating speed, flow rate and post-CMP cleaning on the three kinds of defect, which finally eliminated the defects and achieved good surface morphology. This study will provide an important reference value for the future research of aluminum metal gate CMP.展开更多
Degradation induced by the negative bias temperature instability(NBTI)can be attributed to three mutually uncoupled physical mechanisms,i.e.,the generation of interface traps(ΔV_(IT)),hole trapping in pre-existing ga...Degradation induced by the negative bias temperature instability(NBTI)can be attributed to three mutually uncoupled physical mechanisms,i.e.,the generation of interface traps(ΔV_(IT)),hole trapping in pre-existing gate oxide defects(ΔV_(HT)),and the generation of gate oxide defects(ΔV_(OT)).In this work,the characteristic of NBTI for p-type MOSFET fabricated by using a 28-nm high-k metal gate(HKMG)process is thoroughly studied.The experimental results show that the degradation is enhanced at a larger stress bias and higher temperature.The effects of the three underlying subcomponents are evaluated by using the comprehensive models.It is found that the generation of interface traps dominates the NBTI degradation during long-time NBTI stress.Moreover,the NBTI parameters of the power-law time exponent and temperature activation energy as well as the gate oxide field acceleration are extracted.The dependence of operating lifetime on stress bias and temperature is also discussed.It is observed that NBTI lifetime significantly decreases as the stress increases.Furthermore,the decrease of charges related to interface traps and hole detrapping in pre-existing gate oxide defects are used to explain the recovery mechanism after stress.展开更多
基金Project supported by the Major National Science and Technology Special Projects(No.2009ZX02308)the Natural Science Foundation for the Youth of Hebei Province(Nos.F2012202094,F2015202267)the Outstanding Youth Science and Technology Innovation Fund of Hebei University of Technology(No.2013010)
文摘The replacement metal gate（RMG） defectivity performance control is very challenging in high-k metal gate（HKMG） chemical mechanical polishing（CMP）. In this study, three major defect types, including fall-on particles, micro-scratch and corrosion have been investigated. The research studied the effects of polishing pad,pressure, rotating speed, flow rate and post-CMP cleaning on the three kinds of defect, which finally eliminated the defects and achieved good surface morphology. This study will provide an important reference value for the future research of aluminum metal gate CMP.
文摘Degradation induced by the negative bias temperature instability(NBTI)can be attributed to three mutually uncoupled physical mechanisms,i.e.,the generation of interface traps(ΔV_(IT)),hole trapping in pre-existing gate oxide defects(ΔV_(HT)),and the generation of gate oxide defects(ΔV_(OT)).In this work,the characteristic of NBTI for p-type MOSFET fabricated by using a 28-nm high-k metal gate(HKMG)process is thoroughly studied.The experimental results show that the degradation is enhanced at a larger stress bias and higher temperature.The effects of the three underlying subcomponents are evaluated by using the comprehensive models.It is found that the generation of interface traps dominates the NBTI degradation during long-time NBTI stress.Moreover,the NBTI parameters of the power-law time exponent and temperature activation energy as well as the gate oxide field acceleration are extracted.The dependence of operating lifetime on stress bias and temperature is also discussed.It is observed that NBTI lifetime significantly decreases as the stress increases.Furthermore,the decrease of charges related to interface traps and hole detrapping in pre-existing gate oxide defects are used to explain the recovery mechanism after stress.