The GH4169 superalloy with different content ofδ-Ni3Nb phase was welded by tungsten inert gas welding.A detailed study of microstructure and hardness of heat-affected zone(HAZ)was performed in both as-welded and aged...The GH4169 superalloy with different content ofδ-Ni3Nb phase was welded by tungsten inert gas welding.A detailed study of microstructure and hardness of heat-affected zone(HAZ)was performed in both as-welded and aged state.The results show that the precipitation ofδphase,especially the intergranularδphase,can lead to the enrichment of Nb and Mo elements,which promote the formation ofγ/Laves eutectic constituent at grain boundaries in HAZ.In as-welded state,the hardness decreases first and then increases(exhibiting a"V"shape)with distance away from fusion line in HAZ,which is governed by grain size.After aging treatment,however,theγ″phase plays a key role in hardness and leads to the"■"shape profiles of hardness in HAZ.展开更多
基金financially supported by the National Natural Science Foundation of China (No.51774213)the Regional Demonstration Project of Marine Economic Innovation and Development (No.BHSF2017-10)
文摘The GH4169 superalloy with different content ofδ-Ni3Nb phase was welded by tungsten inert gas welding.A detailed study of microstructure and hardness of heat-affected zone(HAZ)was performed in both as-welded and aged state.The results show that the precipitation ofδphase,especially the intergranularδphase,can lead to the enrichment of Nb and Mo elements,which promote the formation ofγ/Laves eutectic constituent at grain boundaries in HAZ.In as-welded state,the hardness decreases first and then increases(exhibiting a"V"shape)with distance away from fusion line in HAZ,which is governed by grain size.After aging treatment,however,theγ″phase plays a key role in hardness and leads to the"■"shape profiles of hardness in HAZ.