Magnesium(Mg)alloys are considered to be a new generation of revolutionary medical metals.Laser-beam powder bed fusion(PBF-LB)is suitable for fabricating metal implants withpersonalized and complicated structures.Howe...Magnesium(Mg)alloys are considered to be a new generation of revolutionary medical metals.Laser-beam powder bed fusion(PBF-LB)is suitable for fabricating metal implants withpersonalized and complicated structures.However,the as-built part usually exhibits undesirable microstructure and unsatisfactory performance.In this work,WE43 parts were firstly fabricated by PBF-LB and then subjected to heat treatment.Although a high densification rate of 99.91%was achieved using suitable processes,the as-built parts exhibited anisotropic and layeredmicrostructure with heterogeneously precipitated Nd-rich intermetallic.After heat treatment,fine and nano-scaled Mg24Y5particles were precipitated.Meanwhile,theα-Mg grainsunderwent recrystallization and turned coarsened slightly,which effectively weakened thetexture intensity and reduced the anisotropy.As a consequence,the yield strength and ultimate tensile strength were significantly improved to(250.2±3.5)MPa and(312±3.7)MPa,respectively,while the elongation was still maintained at a high level of 15.2%.Furthermore,the homogenized microstructure reduced the tendency of localized corrosion and favoredthe development of uniform passivation film.Thus,the degradation rate of WE43 parts was decreased by an order of magnitude.Besides,in-vitro cell experiments proved their favorable biocompatibility.展开更多
NiTi alloys have drawn significant attentions in biomedical and aerospace fields due to their unique shape memory effect(SME),superelasticity(SE),damping characteristics,high corrosion resistance,and good biocompatibi...NiTi alloys have drawn significant attentions in biomedical and aerospace fields due to their unique shape memory effect(SME),superelasticity(SE),damping characteristics,high corrosion resistance,and good biocompatibility.Because of the unsatisfying processabilities and manufacturing requirements of complex NiTi components,additive manufacturing technology,especially laser powder bed fusion(LPBF),is appropriate for fabricating NiTi products.This paper comprehensively summarizes recent research on the NiTi alloys fabricated by LPBF,including printability,microstructural characteristics,phase transformation behaviors,lattice structures,and applications.Process parameters and microstructural features mainly influence the printability of LPBF-processed NiTi alloys.The phase transformation behaviors between austenite and martensite phases,phase transformation temperatures,and an overview of the influencing factors are summarized in this paper.This paper provides a comprehensive review of the mechanical properties with unique strain-stress responses,which comprise tensile mechanical properties,thermomechanical properties(e.g.critical stress to induce martensitic transformation,thermo-recoverable strain,and SE strain),damping properties and hardness.Moreover,several common structures(e.g.a negative Poisson’s ratio structure and a diamond-like structure)are considered,and the corresponding studies are summarized.It illustrates the various fields of application,including biological scaffolds,shock absorbers,and driving devices.In the end,the paper concludes with the main achievements from the recent studies and puts forward the limitations and development tendencies in the future.展开更多
The new generation of Sc and Zr modified Al alloys has been attracted wide concerns in aerospace industry,owing to the excellent mechanical performances and superior thermal stability than other normal Al alloys.By mi...The new generation of Sc and Zr modified Al alloys has been attracted wide concerns in aerospace industry,owing to the excellent mechanical performances and superior thermal stability than other normal Al alloys.By microalloying with Sc and Zr,the Al3(Sc,Zr)particle forms as the grain refiner during the solidification,which is extremely beneficial for the laser powder bed fusion(LPBF)processed Al alloys.In this study,a new type Al-14.1 Mg-0.47 Si-0.31 Sc-0.17 Zr alloy was additively manufactured by LPBF,and the microstructure,tensile properties and thermal stability were studied in detail.By using a single melt-67°scanning strategy,the LPBF-processed specimen with a relative density of 99.4%and tensile strength of 487.7 MPa was obtained at 160 W-200 mm/s.And this AlMgSiScZr alloy can still exhibit an excellent tensile strength of 393.9 MPa at a moderate temperature of 473 K.After the aging treatment,the tensile properties further increased due to the precipitate hardening of Mg2Si and Al3(Sc,Zr),and the maximum value(580 MPa)was reached at an aging time of 10 h.The average crystal size was almost unchanged after aging treated at 325℃and 24 h,indicating this AlMgSiScZr alloy has an improved thermal stability.The AlMgSiScZr alloy is recommended to substitute some particular titanium alloys in aerospace field afterwards.展开更多
The inflexible concept of membrane curvature as an independent property of lipid structures is today obsolete.Lipid bilayers behave as many-body entities with emergent properties that depend on their interactions with...The inflexible concept of membrane curvature as an independent property of lipid structures is today obsolete.Lipid bilayers behave as many-body entities with emergent properties that depend on their interactions with the environment.In particular,proteins exert crucial actions on lipid molecules that ultimately condition the collective properties of the membranes.In this review,the potential of enhanced molecular dynamics to address cell-biology problems is discussed.The cases of membrane deformation,membrane fusion,and the fusion pore are analyzed from the perspective of the dimensionality reduction by collective variables.Coupled lipid-protein interactions as fundamental determinants of large membrane remodeling events are also commented.Finally,novel strategies merging cell biology and physics are considered as future lines of research.展开更多
Three kinds of welds were made using low frequency pulse current variable polarity tungsten inter gas （LPVPTIG） with argon shielding, direct current TIG （DCTIG） with helium shielding and high frequency pulse curr...Three kinds of welds were made using low frequency pulse current variable polarity tungsten inter gas （LPVPTIG） with argon shielding, direct current TIG （DCTIG） with helium shielding and high frequency pulse current variable polarity TIG （HPVPTIG） with argon shielding, respectively. It was found that macrosegregation bands with large amount of thick continuous eutectics and microporosities formed in the LPVPTIG weld due to the fluctuation of the pulse varied heat input. Only microsegregation existed in the DCTIG weld and HPVPTIG weld. However,the HPVPTIG weld had lower extent of Cu microsegregation since its welding speed was slower. The tensile results indicated that the mechanical properties of the weld decreased with the increase of the segregation extent of Cu and porosities, and LPVPTIG weld had lower tensile properties in the longitudinal direction than those in the transverse direction due to the macrosegregation bands.展开更多
Laser powder bed fusion(L-PBF)of Sc/Zr-modified Al-based alloys has recently become a promising method for developing a new generation of high-performance Al alloys.To clarify the modification roles of Sc/Zr elements,...Laser powder bed fusion(L-PBF)of Sc/Zr-modified Al-based alloys has recently become a promising method for developing a new generation of high-performance Al alloys.To clarify the modification roles of Sc/Zr elements,an Al–4.66Mg–0.48Mn–0.72Sc–0.33Zr(wt.%)alloy was processed using L-PBF.The effect of the local solidification condition of the molten pool on the precipitation behavior of primary Al_(3)(Sc,Zr)was analyzed based on time-dependent nucleation theory.It was found that primary Al_(3)(Sc,Zr)inevitably precipitated at the fusion boundary,while its precipitation could be effectively suppressed in the inner region of the molten pool.This subsequently induced the formation of a heterogeneousα-Al matrix.After direct aging,the heredity of solidification microstructure introduced heterogeneous secondary Al_(3)(Sc,Zr)precipitates withinα-Al matrix.Owing to the inverse relationship between grain boundary strengthening and precipitation strengthening,the direct-aged sample with dual heterogeneous structures exhibited reduced mechanical heterogeneity,resulting in lowered hetero-deformation-induced hardening.The low strain-hardening capability in the direct-aged sample promoted necking instability while inducing a large Lüders elongation,which effectively improved the tensile ductility.展开更多
基金supported by the following funds:National Natural Science Foundation of China(51935014,52165043)Jiangxi Provincial Cultivation Program for Academic and Technical Leaders of Major Subjects(20225BCJ23008)+1 种基金Jiangxi Provincial Natural Science Foundation(20224ACB204013,20224ACB214008)Scientific Research Project of Anhui Universities(KJ2021A1106)。
文摘Magnesium(Mg)alloys are considered to be a new generation of revolutionary medical metals.Laser-beam powder bed fusion(PBF-LB)is suitable for fabricating metal implants withpersonalized and complicated structures.However,the as-built part usually exhibits undesirable microstructure and unsatisfactory performance.In this work,WE43 parts were firstly fabricated by PBF-LB and then subjected to heat treatment.Although a high densification rate of 99.91%was achieved using suitable processes,the as-built parts exhibited anisotropic and layeredmicrostructure with heterogeneously precipitated Nd-rich intermetallic.After heat treatment,fine and nano-scaled Mg24Y5particles were precipitated.Meanwhile,theα-Mg grainsunderwent recrystallization and turned coarsened slightly,which effectively weakened thetexture intensity and reduced the anisotropy.As a consequence,the yield strength and ultimate tensile strength were significantly improved to(250.2±3.5)MPa and(312±3.7)MPa,respectively,while the elongation was still maintained at a high level of 15.2%.Furthermore,the homogenized microstructure reduced the tendency of localized corrosion and favoredthe development of uniform passivation film.Thus,the degradation rate of WE43 parts was decreased by an order of magnitude.Besides,in-vitro cell experiments proved their favorable biocompatibility.
基金sponsored by the Natural and Science Foundation of China(Grant No.52275331)the Key-Area Research and Development Program of Guangdong Province(No.2020B090923001)+3 种基金the Key Research and Development Program of Hubei Province(No.2022BAA011)the Academic Frontier Youth Team(2018QYTD04)at Huazhong University of Science and Technology(HUST)the Hong Kong Scholars Program(No.XJ2022014)the Laboratory Project of Science and Technology on Power Beam Processes Laboratory。
文摘NiTi alloys have drawn significant attentions in biomedical and aerospace fields due to their unique shape memory effect(SME),superelasticity(SE),damping characteristics,high corrosion resistance,and good biocompatibility.Because of the unsatisfying processabilities and manufacturing requirements of complex NiTi components,additive manufacturing technology,especially laser powder bed fusion(LPBF),is appropriate for fabricating NiTi products.This paper comprehensively summarizes recent research on the NiTi alloys fabricated by LPBF,including printability,microstructural characteristics,phase transformation behaviors,lattice structures,and applications.Process parameters and microstructural features mainly influence the printability of LPBF-processed NiTi alloys.The phase transformation behaviors between austenite and martensite phases,phase transformation temperatures,and an overview of the influencing factors are summarized in this paper.This paper provides a comprehensive review of the mechanical properties with unique strain-stress responses,which comprise tensile mechanical properties,thermomechanical properties(e.g.critical stress to induce martensitic transformation,thermo-recoverable strain,and SE strain),damping properties and hardness.Moreover,several common structures(e.g.a negative Poisson’s ratio structure and a diamond-like structure)are considered,and the corresponding studies are summarized.It illustrates the various fields of application,including biological scaffolds,shock absorbers,and driving devices.In the end,the paper concludes with the main achievements from the recent studies and puts forward the limitations and development tendencies in the future.
文摘The new generation of Sc and Zr modified Al alloys has been attracted wide concerns in aerospace industry,owing to the excellent mechanical performances and superior thermal stability than other normal Al alloys.By microalloying with Sc and Zr,the Al3(Sc,Zr)particle forms as the grain refiner during the solidification,which is extremely beneficial for the laser powder bed fusion(LPBF)processed Al alloys.In this study,a new type Al-14.1 Mg-0.47 Si-0.31 Sc-0.17 Zr alloy was additively manufactured by LPBF,and the microstructure,tensile properties and thermal stability were studied in detail.By using a single melt-67°scanning strategy,the LPBF-processed specimen with a relative density of 99.4%and tensile strength of 487.7 MPa was obtained at 160 W-200 mm/s.And this AlMgSiScZr alloy can still exhibit an excellent tensile strength of 393.9 MPa at a moderate temperature of 473 K.After the aging treatment,the tensile properties further increased due to the precipitate hardening of Mg2Si and Al3(Sc,Zr),and the maximum value(580 MPa)was reached at an aging time of 10 h.The average crystal size was almost unchanged after aging treated at 325℃and 24 h,indicating this AlMgSiScZr alloy has an improved thermal stability.The AlMgSiScZr alloy is recommended to substitute some particular titanium alloys in aerospace field afterwards.
基金Grants from CONICET(PIP-0409CO)ANPCyT(PICT2020-1897)are gratefully acknowledged。
文摘The inflexible concept of membrane curvature as an independent property of lipid structures is today obsolete.Lipid bilayers behave as many-body entities with emergent properties that depend on their interactions with the environment.In particular,proteins exert crucial actions on lipid molecules that ultimately condition the collective properties of the membranes.In this review,the potential of enhanced molecular dynamics to address cell-biology problems is discussed.The cases of membrane deformation,membrane fusion,and the fusion pore are analyzed from the perspective of the dimensionality reduction by collective variables.Coupled lipid-protein interactions as fundamental determinants of large membrane remodeling events are also commented.Finally,novel strategies merging cell biology and physics are considered as future lines of research.
文摘Three kinds of welds were made using low frequency pulse current variable polarity tungsten inter gas （LPVPTIG） with argon shielding, direct current TIG （DCTIG） with helium shielding and high frequency pulse current variable polarity TIG （HPVPTIG） with argon shielding, respectively. It was found that macrosegregation bands with large amount of thick continuous eutectics and microporosities formed in the LPVPTIG weld due to the fluctuation of the pulse varied heat input. Only microsegregation existed in the DCTIG weld and HPVPTIG weld. However,the HPVPTIG weld had lower extent of Cu microsegregation since its welding speed was slower. The tensile results indicated that the mechanical properties of the weld decreased with the increase of the segregation extent of Cu and porosities, and LPVPTIG weld had lower tensile properties in the longitudinal direction than those in the transverse direction due to the macrosegregation bands.
基金financially supported by the National Key Research and Development Program of China(Nos.2018YFB1106302 and 2016YFB1100104)the National Natural Science Foundation of China(No.52005411)。
文摘Laser powder bed fusion(L-PBF)of Sc/Zr-modified Al-based alloys has recently become a promising method for developing a new generation of high-performance Al alloys.To clarify the modification roles of Sc/Zr elements,an Al–4.66Mg–0.48Mn–0.72Sc–0.33Zr(wt.%)alloy was processed using L-PBF.The effect of the local solidification condition of the molten pool on the precipitation behavior of primary Al_(3)(Sc,Zr)was analyzed based on time-dependent nucleation theory.It was found that primary Al_(3)(Sc,Zr)inevitably precipitated at the fusion boundary,while its precipitation could be effectively suppressed in the inner region of the molten pool.This subsequently induced the formation of a heterogeneousα-Al matrix.After direct aging,the heredity of solidification microstructure introduced heterogeneous secondary Al_(3)(Sc,Zr)precipitates withinα-Al matrix.Owing to the inverse relationship between grain boundary strengthening and precipitation strengthening,the direct-aged sample with dual heterogeneous structures exhibited reduced mechanical heterogeneity,resulting in lowered hetero-deformation-induced hardening.The low strain-hardening capability in the direct-aged sample promoted necking instability while inducing a large Lüders elongation,which effectively improved the tensile ductility.