The initiation, propagation and the accompanied dislocation structures of the cracks in AZ80 magnesium alloy during multiple forging processes were investigated. The results show that the cracks firstly initiate at th...The initiation, propagation and the accompanied dislocation structures of the cracks in AZ80 magnesium alloy during multiple forging processes were investigated. The results show that the cracks firstly initiate at the Mg/Mg17Al12 interface under the hoop tensile stress on equatorial free surface. On further deformation, the cracks in the Mg17Al12 particles tend to propagate along the grain boundaries(GBs) in a zigzag pattern and link with adjacent cracks in other Mg17Al12 particles to form one whole crack, leading to the fracture surface. Low deformation temperature and too many forging passes during the deformation will promote the nucleation of interfacial microcrack inside the specimens due to the strong plastic strain incompatibility and the high internal stresses near the GBs. The loading axis rotating during the process can change the stress field at the tip of cracks, leading to the change of the crack propagating path and assisting in inhabiting microcracking development.展开更多
Fracture behavior of CrN coatings deposited on the surface of silicon and AISI52100 steel by different energy ion beam assisted magnetron sputtering technique （IBAMS） was studied using indentation and dynamic cycle ...Fracture behavior of CrN coatings deposited on the surface of silicon and AISI52100 steel by different energy ion beam assisted magnetron sputtering technique （IBAMS） was studied using indentation and dynamic cycle impact. It is found that, for the coatings on silicon substrate, the cracks form in the indentation corners and then propagate outward under Vickers indentation. The coating prepared using ion assisted energy of 800 eV shows the highest fracture resistance due to its compact structure. Under Rockwell indentation, only finer radial cracks are found in the CrN coating on AISI 52100 steel without ion assisting while in the condition of ion assisting energy of 800 eV, radial, lateral cracks and spalling appear in the vicinity of indentation. The fracture of CrN coatings under dynamic cycle impact is similar to fatigue. The impact fracture resistance of CrN coatings increases with the increase of ion assisting energy.展开更多
基金Project(04GK1008-1) supported by the Major Program of Science and Technology of Hunan Province Project(03JKY1016) supported by the Key Program of Science and Technology of Hunan Province
文摘The initiation, propagation and the accompanied dislocation structures of the cracks in AZ80 magnesium alloy during multiple forging processes were investigated. The results show that the cracks firstly initiate at the Mg/Mg17Al12 interface under the hoop tensile stress on equatorial free surface. On further deformation, the cracks in the Mg17Al12 particles tend to propagate along the grain boundaries(GBs) in a zigzag pattern and link with adjacent cracks in other Mg17Al12 particles to form one whole crack, leading to the fracture surface. Low deformation temperature and too many forging passes during the deformation will promote the nucleation of interfacial microcrack inside the specimens due to the strong plastic strain incompatibility and the high internal stresses near the GBs. The loading axis rotating during the process can change the stress field at the tip of cracks, leading to the change of the crack propagating path and assisting in inhabiting microcracking development.
基金Funded by the National Natural Science Foundation of China(No. 50771070)Shanxi Province Science and Technology Key Projects (No. 20100321078-02)
文摘Fracture behavior of CrN coatings deposited on the surface of silicon and AISI52100 steel by different energy ion beam assisted magnetron sputtering technique （IBAMS） was studied using indentation and dynamic cycle impact. It is found that, for the coatings on silicon substrate, the cracks form in the indentation corners and then propagate outward under Vickers indentation. The coating prepared using ion assisted energy of 800 eV shows the highest fracture resistance due to its compact structure. Under Rockwell indentation, only finer radial cracks are found in the CrN coating on AISI 52100 steel without ion assisting while in the condition of ion assisting energy of 800 eV, radial, lateral cracks and spalling appear in the vicinity of indentation. The fracture of CrN coatings under dynamic cycle impact is similar to fatigue. The impact fracture resistance of CrN coatings increases with the increase of ion assisting energy.