The softening and melting behavior of sinter, pellet and mixed burden was researched through high tem- perature reaction tests under load simulating traditional blast furnace （T-BF） and oxygen blast furnace （OBF） ...The softening and melting behavior of sinter, pellet and mixed burden was researched through high tem- perature reaction tests under load simulating traditional blast furnace （T-BF） and oxygen blast furnace （OBF） condi- tions. The results indicated that compared with T-BF, the softening zone of sinter and pellet became wide, but the melting zone became narrow in OBF. The permeabilities of both sinter and pellet were improved in OBF. Under the condition of OBF, the temperature of softening zone of mixed burden was increased by 63 K, but the temperature of melting zone was decreased by 76 K. Therefore, the permeability of material layer was significantly improved. This was mainly caused by the change of the melting behavior of pellet. In addition, the quality Of dripping iron in OBF was much better than that of T-BF.展开更多
为了解决高Al2O3含量综合炉料透气性较差和熔滴特征S值较高的问题,通过对提高烧结矿中的Mg O含量和在球团矿中配加Mg O含量的方法进行研究,结果显示合理配置Mg O含量后最高压差由1.70 k Pa分别降低到1.63 k Pa和1.33k Pa,特征S值由141 k...为了解决高Al2O3含量综合炉料透气性较差和熔滴特征S值较高的问题,通过对提高烧结矿中的Mg O含量和在球团矿中配加Mg O含量的方法进行研究,结果显示合理配置Mg O含量后最高压差由1.70 k Pa分别降低到1.63 k Pa和1.33k Pa,特征S值由141 k Pa·℃分别降低到100 k Pa·℃和99 k Pa·℃,改善了综合炉料的透气性、熔滴特征S值等熔滴特征参数;且在球团矿中配加Mg O含量对综合炉料熔滴特性的改善程度要优于提高烧结矿中的Mg O含量。此外,还对综合炉料的初渣进行研究,得出了综合炉料的熔滴特性的改善与初渣的矿物组成没有关系,主要是由于初渣化学成分的变化而产生的。展开更多
基金Item Sponsored by National Basic Research Program of China(2012CB720401)National Natural Science Foundation of China and Baosteel(51134008)
文摘The softening and melting behavior of sinter, pellet and mixed burden was researched through high tem- perature reaction tests under load simulating traditional blast furnace （T-BF） and oxygen blast furnace （OBF） condi- tions. The results indicated that compared with T-BF, the softening zone of sinter and pellet became wide, but the melting zone became narrow in OBF. The permeabilities of both sinter and pellet were improved in OBF. Under the condition of OBF, the temperature of softening zone of mixed burden was increased by 63 K, but the temperature of melting zone was decreased by 76 K. Therefore, the permeability of material layer was significantly improved. This was mainly caused by the change of the melting behavior of pellet. In addition, the quality Of dripping iron in OBF was much better than that of T-BF.
文摘为了解决高Al2O3含量综合炉料透气性较差和熔滴特征S值较高的问题,通过对提高烧结矿中的Mg O含量和在球团矿中配加Mg O含量的方法进行研究,结果显示合理配置Mg O含量后最高压差由1.70 k Pa分别降低到1.63 k Pa和1.33k Pa,特征S值由141 k Pa·℃分别降低到100 k Pa·℃和99 k Pa·℃,改善了综合炉料的透气性、熔滴特征S值等熔滴特征参数;且在球团矿中配加Mg O含量对综合炉料熔滴特性的改善程度要优于提高烧结矿中的Mg O含量。此外,还对综合炉料的初渣进行研究,得出了综合炉料的熔滴特性的改善与初渣的矿物组成没有关系,主要是由于初渣化学成分的变化而产生的。