A macromer, methoxypolyethylene glycol acrylate （MPEGAA）, was synthesized by direct esterification using methoxypolyethylene glycol （MPEG-1200） and acrylic acid （AA） as the main materials. MPEGAA was then used t...A macromer, methoxypolyethylene glycol acrylate （MPEGAA）, was synthesized by direct esterification using methoxypolyethylene glycol （MPEG-1200） and acrylic acid （AA） as the main materials. MPEGAA was then used to prepare a polyacrylic acid superplasticizer modified with 2-acrylamido-2- methylpropane sulfonic acid （AMPS）. A single-factor test was performed to investigate the effects of the molar ratio of acid to alcohol （n（AA）/n（MPEG））, inhibitor amount, catalyst amount, temperature, and time of esterification on the synthesis of MPEGAA. The experimental results showed that the optimal esterification conditions were as follows： n（AA）/n（MPEG）, 3.5：1; amount of hydroquinone （as an inhibitor）, 1.2%; amount of para-toluenesulfonic acid （as a catalyst）, 5.5%; reaction temperature, 95 ~C; and reaction time, 6 h. The AMPS- modified polyacrylic acid superplasticizer prepared under the optimal esterification conditions enabled the achievement and maintenance of high cement dispersibility. At an admixture amount of 0.15%, the cement paste fluidity was initially as high as 300 mm, and then decreased to 315 mm after 1 h and to 290 mm after 2 h.展开更多
基金Funded by the Fujian Education Department(Nos.JA11329,JA12412)the Quanzhou(Fujian)Technology Research and Development Program(No.2010G7)
文摘A macromer, methoxypolyethylene glycol acrylate （MPEGAA）, was synthesized by direct esterification using methoxypolyethylene glycol （MPEG-1200） and acrylic acid （AA） as the main materials. MPEGAA was then used to prepare a polyacrylic acid superplasticizer modified with 2-acrylamido-2- methylpropane sulfonic acid （AMPS）. A single-factor test was performed to investigate the effects of the molar ratio of acid to alcohol （n（AA）/n（MPEG））, inhibitor amount, catalyst amount, temperature, and time of esterification on the synthesis of MPEGAA. The experimental results showed that the optimal esterification conditions were as follows： n（AA）/n（MPEG）, 3.5：1; amount of hydroquinone （as an inhibitor）, 1.2%; amount of para-toluenesulfonic acid （as a catalyst）, 5.5%; reaction temperature, 95 ~C; and reaction time, 6 h. The AMPS- modified polyacrylic acid superplasticizer prepared under the optimal esterification conditions enabled the achievement and maintenance of high cement dispersibility. At an admixture amount of 0.15%, the cement paste fluidity was initially as high as 300 mm, and then decreased to 315 mm after 1 h and to 290 mm after 2 h.