The double-alloy powder mixed method is very proper for developing new small-mass products by changing the composi- tion of sintered Nd-Fe-B magnets, and there is little research on this aspect. The variation on magne...The double-alloy powder mixed method is very proper for developing new small-mass products by changing the composi- tion of sintered Nd-Fe-B magnets, and there is little research on this aspect. The variation on magnetic and mechanical properties of high intrinsic coercivity Nd-Fe-B magnets prepared by double-alloy powder mixed method was discussed, which is a method blend- ing two-type main phase alloy powders with different components. The results showed that the intrinsic coercivity and density of sin- tered Nd-Fe-B magnets increased gradually with the increase in Dy content, and the double-alloy powder mixed method could obtain high intrinsic coercivity Nd-Fe-B magnets with good crystallographic alignment and microstructure. The bending strength of sintered Nd-Fe-B magnets declined, and the Rockwell hardness of sintered Nd-Fe-B magnets first declined, and then increased with the in- crease in Dy content. The microstructure showed that there existed the phenomenon that the Dy element diffused into main phase dur- ing sintering process, and the distribution of Dy content in main phase had some variation in homogeneity as a result of incomplete reaction between the double-alloy powder types.展开更多
基金Project supported by the Natural Science Foundation of Hubei Province(2014CFB626,2015CFC785)the Research Project of Hubei Provincial Department of Education(D20151801)the Opening Foundation of Hubei Key Laboratory of Automotive Power Train and Electronic Control(ZDK1201404)
文摘The double-alloy powder mixed method is very proper for developing new small-mass products by changing the composi- tion of sintered Nd-Fe-B magnets, and there is little research on this aspect. The variation on magnetic and mechanical properties of high intrinsic coercivity Nd-Fe-B magnets prepared by double-alloy powder mixed method was discussed, which is a method blend- ing two-type main phase alloy powders with different components. The results showed that the intrinsic coercivity and density of sin- tered Nd-Fe-B magnets increased gradually with the increase in Dy content, and the double-alloy powder mixed method could obtain high intrinsic coercivity Nd-Fe-B magnets with good crystallographic alignment and microstructure. The bending strength of sintered Nd-Fe-B magnets declined, and the Rockwell hardness of sintered Nd-Fe-B magnets first declined, and then increased with the in- crease in Dy content. The microstructure showed that there existed the phenomenon that the Dy element diffused into main phase dur- ing sintering process, and the distribution of Dy content in main phase had some variation in homogeneity as a result of incomplete reaction between the double-alloy powder types.