The utilization of pure hydrogen as an energy source in fuel cells gave rise to renewed interest in developing active and stable water-gas shift catalysts. Gold catalysts have proven to be very efficient for water-gas...The utilization of pure hydrogen as an energy source in fuel cells gave rise to renewed interest in developing active and stable water-gas shift catalysts. Gold catalysts have proven to be very efficient for water-gas shift reaction at low temperature. The aim of the present study was to investigate the effect of:(i) different preparation methods(impregnation and coprecipitation) to obtain a modified ceria support,and(ii) the amount of Y_2 O_3(1.0 wt%, 2.5 wt%, 5.0 wt% and 7.5 wt%) as dopant on the water-gas shift activity of Au/CeO_2 catalysts. An extended characterization by means of S_(BET), XRD, HRTEM/HAADF, FTIR,H_2-TPR and CO-TPR measurements in combination with careful evaluation of the catalyst behavior allowed to shed light on the parameters governing the water-gas shift activity. The catalysts show very high activity(>90% CO conversion) in the temperature range 180-220 ℃,with a slightly better performance of the gold catalysts on supports prepared by impregnation. The decreased activity with increasing Y_2 O_3 concentration is related to the hindering of oxygen mobility due to ordering of surface oxygen vacancies in vicinity of segregated Y^(3+). The effect of catalyst pre-treatments and the stability of the best performing samples were examined as well.展开更多
Solid oxide fuel cell(SOFC) electrodes,after a high temperature sintering,may be impregnated to deposit nanoparticles within their pores to enhance the catalytic function.Samarium doped CeO2(SDC) nanoparticles were in...Solid oxide fuel cell(SOFC) electrodes,after a high temperature sintering,may be impregnated to deposit nanoparticles within their pores to enhance the catalytic function.Samarium doped CeO2(SDC) nanoparticles were infiltrated into(Pr0.7Ca0.3)0.9MnO3-δ(PCM) cathode of anode supported SOFC cells.The cell with 2.6 mg/cm2 SDC impregnated in cathode showed the maximum power density of 580 mW/cm2 compared with 310 mW/cm2 of the cell without impregnation at 850 °C.The cells were also characterized with the impeda...展开更多
Five types of rare earth/alkaline earth oxide-doped CeO2 superfine-powders were synthesized by a low-temperature combustion technique. The relevant solid electrolyte materials were also sintered by pressureless sinter...Five types of rare earth/alkaline earth oxide-doped CeO2 superfine-powders were synthesized by a low-temperature combustion technique. The relevant solid electrolyte materials were also sintered by pressureless sintering at different temperatures. The results of X-ray diffraction and transmission electron microscopy showed that the grain size of the powders was approximately 20-30 nm, and rare earth/alkaline earth oxides were completely dissolved into ceria-based solid solution with fluorite structure. The electrical conductivities of the SmzO3-CeO2 system were measured by the ac impedance technique in air at temperatures ranging from 513-900℃. The results indicated that the ionic conductivities of Srno.2oCe0.8Ol.875 solid electrolyte increase with increasing sintering temperature, and the relationship between the conductivities and measuring temperature obeys the An＇henius equation. Then the SmzO3-CeO2 material was further doped with other rare earth/alkaline earth oxide, and the conductivities improve with the effective index.展开更多
Ce0.8Sm0.2O1.9(SDC) nanopowders were synthesized by an acrylamide polymerization process.The XRD results showed that SDC powders prepared at 700 °C possessed a cubic fluorite structure.Transmission electron micro...Ce0.8Sm0.2O1.9(SDC) nanopowders were synthesized by an acrylamide polymerization process.The XRD results showed that SDC powders prepared at 700 °C possessed a cubic fluorite structure.Transmission electron microscopy(TEM) indicated that the particle sizes of powders were in the range of 10-15 nm.A 98.3% of theoretical density was obtained when the SDC pellets were sintered at 1350 °C for 5 h,indicating that the powders had good sinterability.The conductivity of the sintered SDC ceramics was 0.019 S/cm at 6...展开更多
Doped Ceria nano-powders were synthesized via a Pechini-type gel rout. The specific surface area of Ce_(0.8)Sm_(0.2)O_(1.9) powder measured by the multilayer BET method is 41 m2.g^(-1). The electrical conductivities o...Doped Ceria nano-powders were synthesized via a Pechini-type gel rout. The specific surface area of Ce_(0.8)Sm_(0.2)O_(1.9) powder measured by the multilayer BET method is 41 m2.g^(-1). The electrical conductivities of Sm_2O_(3)-CeO_2 systems were measured by the ac impedance technique in air at temperatures ranging from 513 to 900 ℃. Typical impedance spectra consist of two depressed semicircles at reduced measuring temperature and one depressed semicircle at elevated measuring temperature respectively, from which the grain interior and grain boundary conductivities were calculated. The relationship between the conductivities of Sm_2O_3 doped CeO_2 (SDC) electrolyte and measuring temperature obeys Arrhenius equation. The grain interior conductivity of SDC varies slightly with improving sintering temperature, while the total conductivity increases with enhancing sintering temperature. The effective index has a significant effect on the ionic conductivity of ceria doped based electrolyte. When the effective index improves, the ionic conductivity increases and the apparent conductance activation energy decreases.展开更多
基金supported by the Bulgarian National Science Fund(ContractдH09/5/2016)the CONACYT PDCPN 1216 and the University of Turin(Ricerca Locale 2016-2017)
文摘The utilization of pure hydrogen as an energy source in fuel cells gave rise to renewed interest in developing active and stable water-gas shift catalysts. Gold catalysts have proven to be very efficient for water-gas shift reaction at low temperature. The aim of the present study was to investigate the effect of:(i) different preparation methods(impregnation and coprecipitation) to obtain a modified ceria support,and(ii) the amount of Y_2 O_3(1.0 wt%, 2.5 wt%, 5.0 wt% and 7.5 wt%) as dopant on the water-gas shift activity of Au/CeO_2 catalysts. An extended characterization by means of S_(BET), XRD, HRTEM/HAADF, FTIR,H_2-TPR and CO-TPR measurements in combination with careful evaluation of the catalyst behavior allowed to shed light on the parameters governing the water-gas shift activity. The catalysts show very high activity(>90% CO conversion) in the temperature range 180-220 ℃,with a slightly better performance of the gold catalysts on supports prepared by impregnation. The decreased activity with increasing Y_2 O_3 concentration is related to the hindering of oxygen mobility due to ordering of surface oxygen vacancies in vicinity of segregated Y^(3+). The effect of catalyst pre-treatments and the stability of the best performing samples were examined as well.
文摘Solid oxide fuel cell(SOFC) electrodes,after a high temperature sintering,may be impregnated to deposit nanoparticles within their pores to enhance the catalytic function.Samarium doped CeO2(SDC) nanoparticles were infiltrated into(Pr0.7Ca0.3)0.9MnO3-δ(PCM) cathode of anode supported SOFC cells.The cell with 2.6 mg/cm2 SDC impregnated in cathode showed the maximum power density of 580 mW/cm2 compared with 310 mW/cm2 of the cell without impregnation at 850 °C.The cells were also characterized with the impeda...
文摘Five types of rare earth/alkaline earth oxide-doped CeO2 superfine-powders were synthesized by a low-temperature combustion technique. The relevant solid electrolyte materials were also sintered by pressureless sintering at different temperatures. The results of X-ray diffraction and transmission electron microscopy showed that the grain size of the powders was approximately 20-30 nm, and rare earth/alkaline earth oxides were completely dissolved into ceria-based solid solution with fluorite structure. The electrical conductivities of the SmzO3-CeO2 system were measured by the ac impedance technique in air at temperatures ranging from 513-900℃. The results indicated that the ionic conductivities of Srno.2oCe0.8Ol.875 solid electrolyte increase with increasing sintering temperature, and the relationship between the conductivities and measuring temperature obeys the An＇henius equation. Then the SmzO3-CeO2 material was further doped with other rare earth/alkaline earth oxide, and the conductivities improve with the effective index.
基金supported by the Scientific and Technological Development Plan of Jiangsu Province (BE2007014)the Natural Science Foundation of Jiangsu Province (BK2009293)National Basic Research Program of China (2007CB936300)
文摘Ce0.8Sm0.2O1.9(SDC) nanopowders were synthesized by an acrylamide polymerization process.The XRD results showed that SDC powders prepared at 700 °C possessed a cubic fluorite structure.Transmission electron microscopy(TEM) indicated that the particle sizes of powders were in the range of 10-15 nm.A 98.3% of theoretical density was obtained when the SDC pellets were sintered at 1350 °C for 5 h,indicating that the powders had good sinterability.The conductivity of the sintered SDC ceramics was 0.019 S/cm at 6...
文摘Doped Ceria nano-powders were synthesized via a Pechini-type gel rout. The specific surface area of Ce_(0.8)Sm_(0.2)O_(1.9) powder measured by the multilayer BET method is 41 m2.g^(-1). The electrical conductivities of Sm_2O_(3)-CeO_2 systems were measured by the ac impedance technique in air at temperatures ranging from 513 to 900 ℃. Typical impedance spectra consist of two depressed semicircles at reduced measuring temperature and one depressed semicircle at elevated measuring temperature respectively, from which the grain interior and grain boundary conductivities were calculated. The relationship between the conductivities of Sm_2O_3 doped CeO_2 (SDC) electrolyte and measuring temperature obeys Arrhenius equation. The grain interior conductivity of SDC varies slightly with improving sintering temperature, while the total conductivity increases with enhancing sintering temperature. The effective index has a significant effect on the ionic conductivity of ceria doped based electrolyte. When the effective index improves, the ionic conductivity increases and the apparent conductance activation energy decreases.