Vacuum brazing of TiAl alloy to 40Cr steel sheets was conducted with newly developed CuTiNiZrV amorphous foils. It was found that a diffusion layer,filler metal and reaction layer existed in the brazed seam. The diffu...Vacuum brazing of TiAl alloy to 40Cr steel sheets was conducted with newly developed CuTiNiZrV amorphous foils. It was found that a diffusion layer,filler metal and reaction layer existed in the brazed seam. The diffusion layer in the joint brazed with Cu43.75Ti37.5Ni6.25Zr6.25V6.25(at.%) foil was flat and thin,containing Ti19Al6 and Ti2Cu intermetallic compounds; however,the diffusion layer brazed with Cu37.5Ti25Ni12.5Zr12.5V12.5 foil was uneven with bulges,consisting of essentially Ti-based solute solution. The foil with 12.5 at.% V showed inferior spreadability compared to that with 6.25 at.% V at brazing temperature. However,fracture happened along the diffusion layer with 6.25 at.% V foil due to the formation of brittle intermetallic phases,but the joints brazed with 12.5 at.% V foil failed through the TiAl substrate. These results show that designing amorphous alloy with less Ti and more V for brazing TiAl alloy to steel is appropriate.展开更多
基金financially supported by the State Key Laboratory of Advanced Welding and Joining,Harbin Institute of Technology,Harbin,Chinathe National Natural Science Foundation of China (Grant No.51374048)+1 种基金the National Basic Research Program of China ("973 Program",Grant No.2011CB013402)the Fundamental Research Funds for the Central Universities
文摘Vacuum brazing of TiAl alloy to 40Cr steel sheets was conducted with newly developed CuTiNiZrV amorphous foils. It was found that a diffusion layer,filler metal and reaction layer existed in the brazed seam. The diffusion layer in the joint brazed with Cu43.75Ti37.5Ni6.25Zr6.25V6.25(at.%) foil was flat and thin,containing Ti19Al6 and Ti2Cu intermetallic compounds; however,the diffusion layer brazed with Cu37.5Ti25Ni12.5Zr12.5V12.5 foil was uneven with bulges,consisting of essentially Ti-based solute solution. The foil with 12.5 at.% V showed inferior spreadability compared to that with 6.25 at.% V at brazing temperature. However,fracture happened along the diffusion layer with 6.25 at.% V foil due to the formation of brittle intermetallic phases,but the joints brazed with 12.5 at.% V foil failed through the TiAl substrate. These results show that designing amorphous alloy with less Ti and more V for brazing TiAl alloy to steel is appropriate.