Bisphenol A dicyanate ester resins modified by fluorine-containing liquid crystal compound(LCFE)are applied as polymer matrix(LCFE-BADCy),poly(p-phenylene-2,6-benzobisoxazole)(PBO)fibers as rein-forcements,and fluorin...Bisphenol A dicyanate ester resins modified by fluorine-containing liquid crystal compound(LCFE)are applied as polymer matrix(LCFE-BADCy),poly(p-phenylene-2,6-benzobisoxazole)(PBO)fibers as rein-forcements,and fluorine/adamantane PBO precursor(pre FABPBO)as interfacial compatibilizer to prepare the corresponding PBO fibers/FABPBO/LCFE-BADCy wave-transparent laminated composites.LCFE could improve the order degree of BADCy cured network,in favor of enhancing the wave-transparent perfor-mance,mechanical properties,and intrinsic thermal conductivity.The dielectric constant and dielectric loss of PBO fibers/FABPBO/LCFE-BADCy composites are highly temperature(25–200℃)and frequency(10^(4)–10^(7) Hz and 8.2–12.4 GHz)stable with the value of 2.49 and 0.003 under 10^(6) Hz at 25℃,and the corresponding wave transmission efficiency is 95.0%,higher than that of 92.5%for PBO fibers/BADCy com-posites.The interlamellar shear strength and flexural strength are respectively 50.7 MPa and 682.5 MPa,38.1%and 16.2%higher than those of PBO fibers/BADCy composites.Besides,the volume resistivity,breakdown voltage,heat resistance index,glass transition temperature,flame retardant grade,and ul-timate oxygen index of PBO fibers/FABPBO/LCFE-BADCy composites are respectively 5.3×10^(15)Ωcm,29.75 kV/mm,217.2℃,245.7℃,V-1 grade,and 33.6%,expected to be performed as a new generation of“lightweight/loading/wave-transparent”electromagnetic window materials in advanced military weapons and civil communication base station.展开更多
The novel dicyanate ester resin containing naphthalene unit (DNCY) was synthesized, and characterized by FT-IR, 1H-NMR, 13C-NMR and elemental analysis (EA). The thermal properties of DNCY resin was studied by thermal...The novel dicyanate ester resin containing naphthalene unit (DNCY) was synthesized, and characterized by FT-IR, 1H-NMR, 13C-NMR and elemental analysis (EA). The thermal properties of DNCY resin was studied by thermal degradation analysis at a heating rate of 10 C /min-1 in N2 and air. The DNCY resin exhibited better thermal and thermal-oxidative stability than bisphenol A dicyanate (BACY) resin.展开更多
A block copolymer of PDMS-b-PGMA is synthesized by polymerizing glycidyl methacrylate(GMA)via reversible addition-fragmentation chain transfer(RAFT)polymerization applying a polydimethylsiloxane(PDMS)based macro-RAFT ...A block copolymer of PDMS-b-PGMA is synthesized by polymerizing glycidyl methacrylate(GMA)via reversible addition-fragmentation chain transfer(RAFT)polymerization applying a polydimethylsiloxane(PDMS)based macro-RAFT agent,which is then performed to functionalize the quartz fibers(QFs@PDMS-b-PGMA)via a simple coating process.Finally,the QFs@PDMS-b-PGMA/bisphenol A dicyanate ester(BADCy)wave-transparent laminated composites are fabricated by high-temperature molding.Nuclear magnetic resonance(NMR)spectroscopy,Fourier transform infrared(FT-IR)spectroscopy and size ex-clusion chromatography(SEC)demonstrate the successful preparation of PDMS-b-PGMA with expected structure.When the molar mass and coating amount of PDMS-b-PGMA are respectively 8100 g/mol and 2.0 wt.%,QFs@PDMS-b-PGMA/BADCy wave-transparent laminated composites present optimal mechan-ical properties and wave-transparent performance.The interlaminar shear strength(ILSS)and flexural strength are 53.6 and 552.0 MPa,respectively.Meanwhile,the dielectric constant and dielectric loss val-ues are 2.61 and 0.0028 at 1 MHz(wave transmittance of 93.8%),showing good stability at different frequencies(102-106 Hz and 8.4-12.4 GHz)and temperatures(25-250℃).展开更多
Hybrid polymer membrane(TA-APTES),synthesized by tannic acid(TA)and aminopropyl trethoxysilane(APTES)based on the Schif’s base and Michael addition reaction,is deposited on the surface of poly(p-phenylene-2,6-benzobi...Hybrid polymer membrane(TA-APTES),synthesized by tannic acid(TA)and aminopropyl trethoxysilane(APTES)based on the Schif’s base and Michael addition reaction,is deposited on the surface of poly(p-phenylene-2,6-benzobisoxazole)(PBO)fbers,and then grafted with epoxy-terminated polysesquisiloxane(POSS)to obtain POSS-g-PBO@TA-APTES fbers.The POSS-g-PBO@TA-APTES fbers reinforced bisphenol A dicyanate ester(BADCy)resins(POSS-g-PBO@TAAPTES fbers/BADCy)wave-transparent laminated composites are prepared.The interlaminar shear strength and fexural strength of POSS-g-PBO@TA-APTES fbers/BADCy composites are respectively enhanced from 36.7 and 587.4 MPa to 42.8 and 645.8 MPa,increased by 16.6%and 9.9%compared with those of PBO fbers/BADCy composites.At 1 MHz,the corresponding dielectric constant and dielectric loss are reduced to 2.85 and 0.0047,respectively,lower than those of PBO fbers/BADCy(3.06 and 0.006)composites.Meanwhile,the simulated wave transmittance rate of POSS-g-PBO@TA-APTES fbers/BADCy composites with the thicknesses of 1.5–3.5 mm is higher than 86.2%at 0.3–40 GHz.The volume resistivity and breakdown strength of POSS-g-PBO@TA-APTES fbers/BADCy composites are 2.8×10^(15)Ω·cm and 19.80 kV/mm,higher than PBO fbers/BADCy composites(2.2×10^(15)Ω·cm and 17.69 kV/mm),respectively.And the corresponding heat resistant index is 221.5℃,lower than PBO fbers/BADCy composites(229.6℃).展开更多
基金The authors are grateful for the support and funding from National Scientific Research Project(Basis Strengthening Plan)State Key Laboratory of Solidification Processing in NWPU(No.SKLSP202103).
文摘Bisphenol A dicyanate ester resins modified by fluorine-containing liquid crystal compound(LCFE)are applied as polymer matrix(LCFE-BADCy),poly(p-phenylene-2,6-benzobisoxazole)(PBO)fibers as rein-forcements,and fluorine/adamantane PBO precursor(pre FABPBO)as interfacial compatibilizer to prepare the corresponding PBO fibers/FABPBO/LCFE-BADCy wave-transparent laminated composites.LCFE could improve the order degree of BADCy cured network,in favor of enhancing the wave-transparent perfor-mance,mechanical properties,and intrinsic thermal conductivity.The dielectric constant and dielectric loss of PBO fibers/FABPBO/LCFE-BADCy composites are highly temperature(25–200℃)and frequency(10^(4)–10^(7) Hz and 8.2–12.4 GHz)stable with the value of 2.49 and 0.003 under 10^(6) Hz at 25℃,and the corresponding wave transmission efficiency is 95.0%,higher than that of 92.5%for PBO fibers/BADCy com-posites.The interlamellar shear strength and flexural strength are respectively 50.7 MPa and 682.5 MPa,38.1%and 16.2%higher than those of PBO fibers/BADCy composites.Besides,the volume resistivity,breakdown voltage,heat resistance index,glass transition temperature,flame retardant grade,and ul-timate oxygen index of PBO fibers/FABPBO/LCFE-BADCy composites are respectively 5.3×10^(15)Ωcm,29.75 kV/mm,217.2℃,245.7℃,V-1 grade,and 33.6%,expected to be performed as a new generation of“lightweight/loading/wave-transparent”electromagnetic window materials in advanced military weapons and civil communication base station.
文摘The novel dicyanate ester resin containing naphthalene unit (DNCY) was synthesized, and characterized by FT-IR, 1H-NMR, 13C-NMR and elemental analysis (EA). The thermal properties of DNCY resin was studied by thermal degradation analysis at a heating rate of 10 C /min-1 in N2 and air. The DNCY resin exhibited better thermal and thermal-oxidative stability than bisphenol A dicyanate (BACY) resin.
文摘A block copolymer of PDMS-b-PGMA is synthesized by polymerizing glycidyl methacrylate(GMA)via reversible addition-fragmentation chain transfer(RAFT)polymerization applying a polydimethylsiloxane(PDMS)based macro-RAFT agent,which is then performed to functionalize the quartz fibers(QFs@PDMS-b-PGMA)via a simple coating process.Finally,the QFs@PDMS-b-PGMA/bisphenol A dicyanate ester(BADCy)wave-transparent laminated composites are fabricated by high-temperature molding.Nuclear magnetic resonance(NMR)spectroscopy,Fourier transform infrared(FT-IR)spectroscopy and size ex-clusion chromatography(SEC)demonstrate the successful preparation of PDMS-b-PGMA with expected structure.When the molar mass and coating amount of PDMS-b-PGMA are respectively 8100 g/mol and 2.0 wt.%,QFs@PDMS-b-PGMA/BADCy wave-transparent laminated composites present optimal mechan-ical properties and wave-transparent performance.The interlaminar shear strength(ILSS)and flexural strength are 53.6 and 552.0 MPa,respectively.Meanwhile,the dielectric constant and dielectric loss val-ues are 2.61 and 0.0028 at 1 MHz(wave transmittance of 93.8%),showing good stability at different frequencies(102-106 Hz and 8.4-12.4 GHz)and temperatures(25-250℃).
基金The authors are grateful for the support and funding from National Scientifc Research Project(Basis Strengthening Plan)China Postdoctoral Science Foundation(2019M653735)+3 种基金State Key Laboratory for Modifcation of Chemical Fibers and Polymer Materials from Donghua University(KF2001)State Key Laboratory of Solidifcation Processing in NWPU(SKLSP202103)L.Tang thanks for the Innovation Foundation for Doctor Dissertation of Northwestern Polytechnical University(CX2021036)This work is also fnancially supported by Polymer Electromagnetic Functional Materials Innovation Team of Shaanxi Sanqin Scholars.
文摘Hybrid polymer membrane(TA-APTES),synthesized by tannic acid(TA)and aminopropyl trethoxysilane(APTES)based on the Schif’s base and Michael addition reaction,is deposited on the surface of poly(p-phenylene-2,6-benzobisoxazole)(PBO)fbers,and then grafted with epoxy-terminated polysesquisiloxane(POSS)to obtain POSS-g-PBO@TA-APTES fbers.The POSS-g-PBO@TA-APTES fbers reinforced bisphenol A dicyanate ester(BADCy)resins(POSS-g-PBO@TAAPTES fbers/BADCy)wave-transparent laminated composites are prepared.The interlaminar shear strength and fexural strength of POSS-g-PBO@TA-APTES fbers/BADCy composites are respectively enhanced from 36.7 and 587.4 MPa to 42.8 and 645.8 MPa,increased by 16.6%and 9.9%compared with those of PBO fbers/BADCy composites.At 1 MHz,the corresponding dielectric constant and dielectric loss are reduced to 2.85 and 0.0047,respectively,lower than those of PBO fbers/BADCy(3.06 and 0.006)composites.Meanwhile,the simulated wave transmittance rate of POSS-g-PBO@TA-APTES fbers/BADCy composites with the thicknesses of 1.5–3.5 mm is higher than 86.2%at 0.3–40 GHz.The volume resistivity and breakdown strength of POSS-g-PBO@TA-APTES fbers/BADCy composites are 2.8×10^(15)Ω·cm and 19.80 kV/mm,higher than PBO fbers/BADCy composites(2.2×10^(15)Ω·cm and 17.69 kV/mm),respectively.And the corresponding heat resistant index is 221.5℃,lower than PBO fbers/BADCy composites(229.6℃).