Ti, Al, graphite and diamond powders were used as raw materials to prepare Ti_2AlC matrixbonded diamond composite using self-propagating high-temperature synthesis(SHS) method. The effect of diamond size and content o...Ti, Al, graphite and diamond powders were used as raw materials to prepare Ti_2AlC matrixbonded diamond composite using self-propagating high-temperature synthesis(SHS) method. The effect of diamond size and content on the fabrication of Ti_2AlC-bonded diamond material was investigated. Results showed that Ti_2AlC matrix-bonded diamond composites could be obtained by SHS. The phase composition and microstructure of the Ti_2AlC-bonded diamond material were influenced by the diamond content and size. When the diamond(93 μm) additive amounts were 10% and 20%, the product phases included Ti_2AlC, TiC and Al_3Ti. However, excess Ti and Al persisted in the sample that contained 30% diamond. Diamond bonded well with the matrix in the sample that contained 10% diamond. Moreover, addition of coarse diamond particles with sizes of 93 and 125 μm produced a mainly Ti_2AlC matrix. However, diamond adequately reacted with Ti to form TiC when finer diamond particles(5 and 10 μm) were used.展开更多
The shrimp beam trawl fishery in the northern South China Sea is characterized by high by-catch and poor selectivity problems.Among by-catch species,banded scad(Caranx(Atule)kalla)is economically the most important on...The shrimp beam trawl fishery in the northern South China Sea is characterized by high by-catch and poor selectivity problems.Among by-catch species,banded scad(Caranx(Atule)kalla)is economically the most important one.The aim of this study is to improve the selective properties of codends for banded scad.Size selectivity of 2 traditional diamond mesh codends,with mesh size 25 and 30 mm(defined as D25 and D30,respectively),and 4 new combined square and diamond mesh codends,with25 mm square-mesh and 25 mm diamond-mesh(S25+D25),30 mm square-mesh and 25 mm diamondmesh(S30+D25),35 mm square-mesh and 25 mm diamond-mesh(S35+D25),and 35 mm square-mesh and18 mm diamond-mesh(S35+D18),were tested for banded scad in shrimp beam trawl fishery of the South China Sea.A total of 54 valid hauls were finished using the covered codend method,and 5750 banded scad were caught.Selective parameters were obtained using the logistic equation with the maximum likelihood method,by incorporating the between-haul variation.The results show that the present minimum mesh size for shrimp beam trawl in the South China Sea,25-mm diamond mesh size,is insufficient to release immature banded scad.The S35+D25 codend is proved to be the most eff ective codend to release immature banded scad,and its 50%retention length(L _(50))is larger than the minimum landing size(MLS=63.5 mm)of banded scad.However,the 95%confidence intervals of L _(50) overlap among the three combined mesh codends,the S25+D25,S30+D25 and S35+D25 codend.For a sustainable exploitation of banded scad,larger mesh sizes are suggested to be investigated for the combined mesh codends.展开更多
基金Funded by National Natural Science Foundation of China(Nos.51602356 and 11472316)the University Innovation Team Project in Henan Province(Nos.15IRTSTHN004,16A430049,17A430034,and 18A430035)Henan Innovative Excellent Scientific and Technological Team(No.CXTD2013048)
文摘Ti, Al, graphite and diamond powders were used as raw materials to prepare Ti_2AlC matrixbonded diamond composite using self-propagating high-temperature synthesis(SHS) method. The effect of diamond size and content on the fabrication of Ti_2AlC-bonded diamond material was investigated. Results showed that Ti_2AlC matrix-bonded diamond composites could be obtained by SHS. The phase composition and microstructure of the Ti_2AlC-bonded diamond material were influenced by the diamond content and size. When the diamond(93 μm) additive amounts were 10% and 20%, the product phases included Ti_2AlC, TiC and Al_3Ti. However, excess Ti and Al persisted in the sample that contained 30% diamond. Diamond bonded well with the matrix in the sample that contained 10% diamond. Moreover, addition of coarse diamond particles with sizes of 93 and 125 μm produced a mainly Ti_2AlC matrix. However, diamond adequately reacted with Ti to form TiC when finer diamond particles(5 and 10 μm) were used.
基金Supported by the Special Fund for Agro-scientific Research in the Public Interest(No.201203018)
文摘The shrimp beam trawl fishery in the northern South China Sea is characterized by high by-catch and poor selectivity problems.Among by-catch species,banded scad(Caranx(Atule)kalla)is economically the most important one.The aim of this study is to improve the selective properties of codends for banded scad.Size selectivity of 2 traditional diamond mesh codends,with mesh size 25 and 30 mm(defined as D25 and D30,respectively),and 4 new combined square and diamond mesh codends,with25 mm square-mesh and 25 mm diamond-mesh(S25+D25),30 mm square-mesh and 25 mm diamondmesh(S30+D25),35 mm square-mesh and 25 mm diamond-mesh(S35+D25),and 35 mm square-mesh and18 mm diamond-mesh(S35+D18),were tested for banded scad in shrimp beam trawl fishery of the South China Sea.A total of 54 valid hauls were finished using the covered codend method,and 5750 banded scad were caught.Selective parameters were obtained using the logistic equation with the maximum likelihood method,by incorporating the between-haul variation.The results show that the present minimum mesh size for shrimp beam trawl in the South China Sea,25-mm diamond mesh size,is insufficient to release immature banded scad.The S35+D25 codend is proved to be the most eff ective codend to release immature banded scad,and its 50%retention length(L _(50))is larger than the minimum landing size(MLS=63.5 mm)of banded scad.However,the 95%confidence intervals of L _(50) overlap among the three combined mesh codends,the S25+D25,S30+D25 and S35+D25 codend.For a sustainable exploitation of banded scad,larger mesh sizes are suggested to be investigated for the combined mesh codends.